National Institute Of Materials Physics - Romania

Herein, a new direct synthesis route leading to a mesoporous NiWO4 with crystalline framework and NiWO4 -graphene nanoplatelets (GNP) composite is reported. Ni and W assembled into a mesoporous tungstate type of symmetry by co-precipitation synthesis route and its composite with GNP were used as supports for electrocatalysts, with reduced Pt content (8 wt.%), in oxygen reduction reaction (ORR) and hydrogen oxidation reaction (HOR) in acidic medium. A comprehensive assessment of the modifications related to the crystalline and porous structures, morphological aspects as well as the surface chemistry aiming to explain the electrochemical properties was performed. It was found that the presence of GNP during the synthesis process leads, mainly, to the enhanced growth of NiWO4 nanocrystallites, as well as induces changes in the surface chemistry. The elec-trochemical results show that the introduction of GNPs into the NiWO4 composite support leads to a significant improvement in the activity of the Pt electrocatalyst in ORR and HOR compared to both initial NiWO4 and Pt/NiWO4 samples, as well as mechanical mixtures of these catalysts with carbon. Mass activity for hydrogen oxidation, determined in a mixed kinetic-diffusion controlled region, obtained on the 8 wt.% Pt/NiWO4-GNP catalyst was significantly higher compared to the commercial 20 wt.% Pt/C Quintech catalyst. Our comprehensive structural and surface chemistry assessments indicate this composite material as a viable electrocatalyst for PEMFCs using a broader type of fuels.& COPY; 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Light-emissive compounds able to transfer protons, either intra-or intermolecularly in the excited state, have increasingly attracted attention, especially by structural diversification of recognized fluorophores. We report herein synthesis and structural characterization of novel 1,3,4-oxadiazole-based compounds functionalised by salicylaldehyde or o-vanillin moieties. Solution absorption and emission spectroscopy performed on the resulted compounds indicated the essential influence of the established (intra and/or intermolecular) hydrogen bonds onto the optical properties. Theoretical calculations positively contributed to the effort of understanding the emissive behaviour of the compounds and the calculated data correlated very well to experiments. Occurrence of hydrogen bond interactions has been also observed in solid state and we discuss their molecular structures and the effects on the luminescent behaviour. The phenol groups in close proximity of the oxadiazole core were further exploited in cocrystallization experiments with pyridine-based co-partners. Hydrogen bonding were also found responsible for the supramolecular recognition between the two components. One type of the resulted co -crystals preserved the luminescence of the starting compound.

Electronic and stability properties of quasi-2D alkylammonium perovskites are investigated using density functional theory (DFT) calculations and validated experimentally on selected classes of compounds. Our analysis is focused on perovskite structures of formula (A)(2)(A ')(n-1)PbnX3n+1, with large cations A = butyl-, pentyl-, hexylammonium (BA, PA, HXA), small cations A ' = methylammonium, formamidinium, ethylammonium, guanidinium (MA, FA, EA, GA) and halogens X = I, Br, Cl. The role of the halogen ions is outlined for the band structure, stability and defect formation energies. Two opposing trends are found for the absorption efficiency versus stability, the latter being assessed with respect to possible degradation mechanisms. Experimental validation is performed on quasi-2D perovskites based on pentylammonium cations, namely: (PA)(2)PbX4 and (PA)(2)(MA)Pb2X7, synthesized by antisolvent-assisted vapor crystallization. Structural and optical analysis are inline with the DFT based calculations. In addition, the thermogravimetric analysis shows an enhanced stability of bromide and chloride based compounds, in agreement with the theoretical predictions.

The paper presents a study concerning the role of ferroelectric filler size and clustering in the dielectric properties of 20%BaTiO3-80%PVDF and of 20% (2%Ag-98%BaTiO3)-PVDF hybrid nanocomposites. By finite element calculations, it was shown that using fillers with epsilon > 103 does not provide a permittivity rise in the composites and the effective dielectric constant tends to saturate to specific values determined by the filler size and agglomeration degree. Irrespective of the ferroelectric filler sizes, the addition of metallic ultrafine nanoparticles (Ag) results in permittivity intensification and the effect is even stronger if the metallic nanoparticles are connected to a higher degree with the ferroelectric particles' surfaces. When using coarse ferroelectric fillers, the probability of clustering is higher, thus favoring the permittivity increase by field concentration in small regions close to the interfaces separating dissimilar materials. The modeling results were validated by an experimental dielectric analysis performed in a series of PVDF-based thick films with the same amount of BaTiO3 fillers or with Ag-BaTiO3 hybrid fillers. Similar trends as predicted by simulations were found experimentally but with slightly higher permittivity values which were assigned to the modifications of the polymer phase composition due to the presence of nanofillers and the local sample inhomogeneity (the presence of clustering, in particular for coarse BaTiO3 grains), which create regions with enhanced local fields.

The catalytic hydrotreatment of humins, the solid byproduct produced from the conversion of C6 sugars (glucose, fructose) to 5-hydroxymethylfurfural (HMF), using supported Pd@zeolite (Beta, Y, and USY) catalysts with different amounts of Pd (i.e., 0.5, 1.0 and 1.5 wt%) was investigated under molecular hydrogen pressure. The highest conversion of humins (52.0%) was obtained on 1.5Pd@USY catalyst while the highest amount of humins oil (27.3%) was obtained in the presence of the 1Pd@Beta zeolite sample, at P-H2 = 30 bars and T = 250 degrees C. The major compounds in the humins oil evidenced by GC-MS are alcohols, organic acids, ethers, and alkyl-phenolics. However, although all these classes of compounds are obtained regardless of the nature of the catalyst used, the composition of the mixture differs from one catalyst to another. Furanic compounds were not identified in the reaction products. A possible explanation may be related to their high reactivity under the reaction conditions, in the presence of the Pd-based catalysts these compounds lead to alkyl phenolics, important intermediates in the petrochemical industry.

Due to the currently worldwide petrochemical feedstock shortage, the ethylene synthesis from renewable non-oil sources becomes of high interest. The catalysts were prepared in two steps: (i) formation of spheres containing the carbon-coated Mn core by hydrothermal method, (ii) formation of the Si-Zr oxide shell by sol-gel method. The prepared catalysts were characterized by N2 physisorption, SEM-EDX, XRD, XPS, and NH3-TPD. The catalytic results have shown that Fe, Zn or Ni modified Mn core exhibited superior activity compared to the catalysts containing only Mn in the core. With 75% yield and 98% ethanol conversion at 350 degrees C and WHSV of 1.4 h-1, MnNi@SiZr was the best catalyst. These results are due to an increased number of acid sites compared to the other materials and an optimal ratio of weak/medium acid sites. Our findings suggest new lines for developing active and stable catalysts for ethylene synthesis from ethanol.

The incorporation of therapeutic-capable ions into bioactive glasses (BGs), either based on silica (SBGs) or phosphate (PBGs), is currently envisaged as a proficient path for facilitating bone regeneration. In conjunction with this view, the single and complementary structural and bio-functional roles of CuO and Ga2O3 (in the 2-5 mol% range) were assessed, by deriving a series of SBG and PBG formulations starting from the parent glass systems, FastOs (R) BG -38.5SiO2-36.1CaO-5.6P2O5-19.2MgO-0.6CaF2, and 50.0P2O5-35.0CaO-10.0Na2O-5.0 Fe2O3 (mol%), respectively, using the process of melt-quenching. The inter-linked physico-chemistry -biological response of BGs was assessed in search of bio-functional triggers. Further light was shed on the structural role -as network former or modifier -of Cu and Ga, immersed in SBG and PBG matrices. The preliminary biological performance was surveyed in vitro by quantification of Cu and Ga ion release under homeostatic conditions, cytocompatibility assays (in fibroblast cell cultures) and antibacterial tests (against Staphylococcus aureus). The similar (Cu) and dissimilar (Ga) structural roles in the SBG and PBG vitreous networks governed their release. Namely, Cu ions were leached in similar concentrations (ranging from 10-35 ppm and 50-110 ppm at BG doses of 5 and 50 mg/mL, respectively) for both type of BGs, while the release of Ga ions was 1-2 orders of magnitude lower in the case of SBGs (i.e., 0.2-6 ppm) compared to PBGs (i.e., 9-135 ppm). This was attributed to the network modifier role of Cu in both types of BGs, and conversely, to the network former (SBGs) and network modifier (PBGs) roles of Ga. All glasses were cytocompatible at a dose of 5 mg/mL, while at the same concentration the antimicrobial efficiency was found to be accentuated by the coupled release of Cu and Ga ions from SBG. By collective assessment, the most prominent candidate material for the further development of implant coatings and bone graft substitutes was delineated as the 38.5SiO2-34.1CaO-5.6P2O5-16.2MgO-0.6CaF2-2.0CuO-3.0Ga2O3 (mol%) SBG system, which yiel-ded moderate Cu and Ga ion release, excellent cytocompatibility and marked antibacterial efficacy. (c) 2021 The Chinese Ceramic Society. Production and hosting by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

TiO2-based mixed oxide-carbon composite supports have been suggested to provide enhanced stability for platinum (Pt) electrocatalysts in polymer electrolyte membrane (PEM) fuel cells. The addition of molybdenum (Mo) to the mixed oxide is known to increase the CO tolerance of the electrocatalyst. In this work Pt catalysts, supported on Ti1-xMoxO2-C composites with a 25/75 oxide/carbon mass ratio and prepared from different carbon materials (C: Vulcan XC-72, unmodified and functionalized Black Pearls 2000), were compared in the hydrogen oxidation reaction (HOR) and in the oxygen reduction reaction (ORR) with a commercial Pt/C reference catalyst in order to assess the influence of the support on the electrocatalytic behavior. Our aim was to perform electrochemical studies in preparation for fuel cell tests. The ORR kinetic parameters from the Koutecky-Levich plot suggested a four-electron transfer per oxygen molecule, resulting in H2O. The similarity between the Tafel slopes suggested the same reaction mechanism for electrocatalysts supported by these composites. The HOR activity of the composite-supported electrocatalysts was independent of the type of carbonaceous material. A noticeable difference in the stability of the catalysts appeared only after 5000 polarization cycles; the Black Pearl-containing sample showed the highest stability.

To enhance the spectral response of solar cells, an experimental study on LaPO4:0.01Ce(3+)/xNd(3+) (x = 0, 2, 4 mol%) was carried out, where structural and morphological properties of the prepared samples were well characterized by the means of X-ray diffraction, Fourier transform infrared spectroscopy, and scanning electronic microscope. Additionally, the photoluminescence behavior of phosphors in ultraviolet-visible (UV-VIS) and Near-infrared (NIR) regions were investigated to confirm the energy transfer (ET) from Ce3+ to Nd3+. Moreover, the quantum efficiency of Ce3+/Nd3+-co-doped samples was estimated as high as similar to 172% and the possible ET process was described. Accordingly, the LaPO4:Ce3+/Nd3+ phosphors can convert the UV light (275 nm) into NIR photons (approx. 1059 nm) through the possible two-pathway energy transfer processes from Ce3+ sensitizer ions to Nd3+ activators. Obtained NIR down-conversion emissions are suitable for improving the conversion efficiency of c-Si solar cells.

The role of Ag addition on the structural, dielectric, and mechanical harvesting response of 20%(xAg - (1 - x)BaTiO3) - 80%PVDF (x = 0, 2, 5, 7 and 27 vol.%) flexible composites is investigated. The inorganic fillers were realized by precipitating fine (similar to 3 nm) silver nanoparticles onto BaTiO3 nanoparticles (similar to 60 nm average size). The hybrid admixtures with a total filling factor of 20 vol.% were embedded into the PVDF matrix. The presence of filler enhances the amount of beta-PVDF polar phase and the BaTiO3 filler induces an increase of the permittivity from 11 to 18 (1 kHz) in the flexible composites. The addition of increasing amounts of Ag is further beneficial for permittivity increase; with the maximum amount (x = 27 vol.%), permittivity is three times larger than in pure PVDF (epsilon(r) similar to 33 at 1 kHz) with a similar level of tangent losses. This result is due to the local field enhancement in the regions close to the filler-PVDF interfaces which are additionally intensified by the presence of silver nanoparticles. The metallic addition is also beneficial for the mechanical harvesting ability of such composites: the amplitude of the maximum piezoelectric-triboelectric combined output collected in open circuit conditions increases from 0.2 V/cm(2) (PVDF) to 30 V/cm(2) for x = 27 vol.% Ag in a capacitive configuration. The role of ferroelectric and metallic nanoparticles on the increasing mechanical-electric conversion response is also been explained.