National Institute Of Materials Physics - Romania

Ti-aluminosilicate gels were used as supports for the immobilization of Fe, Co, and Ni oxides (5%) by impregnation and synthesis of efficient photocatalysts for the degradation of beta-lactam antibiotics from water. Titanium oxide (1 and 2%) was incorporated into the zeolite network by modifying the gel during the zeolitization process. The formation of the zeolite Y structure and its microporous structure were evidenced by X-ray diffraction and N-2 physisorption. The structure, composition, reduction, and optical properties were studied by X-ray diffraction, H-2-TPR, XPS, Raman, photoluminescence, and UV-Vis spectroscopy. The obtained results indicated a zeolite Y structure for all photocatalysts with tetracoordinated Ti4+ sites. The second transitional metals supported by the post-synthesis method were obtained in various forms, such as oxides and/or in the metallic state. A red shift of the absorption edge was observed in the UV-Vis spectra of photocatalysts upon the addition of Fe, Co, or Ni species. The photocatalytic performances were evaluated for the degradation of cefuroxime in water under visible light irradiation. The best results were obtained for iron-immobilized photocatalysts. Scavenger experiments explained the photocatalytic results and their mechanisms. A different contribution of the active species to the photocatalytic reactions was evidenced.

The primary objective of this research was to develop efficient solid catalysts that can directly convert the lactic acid (LA) obtained from lignocellulosic biomass into alanine (AL) through a reductive amination process. To achieve this, various catalysts based on ruthenium were synthesized using different carriers such as multi-walled carbon nanotubes (MWCNTs), beta-zeolite, and magnetic nanoparticles (MNPs). Among these catalysts, Ru/MNP demonstrated a remarkable yield of 74.0% for alanine at a temperature of 200 degrees C. This yield was found to be superior not only to the Ru/CNT (55.7%) and Ru/BEA (6.6%) catalysts but also to most of the previously reported catalysts. The characterization of the catalysts and their catalytic results revealed that metallic ruthenium nanoparticles, which were highly dispersed on the external surface of the magnetic carrier, significantly enhanced the catalyst's ability for dehydrogenation. Additionally, the -NH2 basic sites on the catalyst further facilitated the formation of alanine by promoting the adsorption of acidic reactants. Furthermore, the catalyst could be easily separated using an external magnetic field and exhibited the potential for multiple reuses without any significant loss in its catalytic performance. These practical advantages further enhance its appeal for applications in the reductive amination of lactic acid to alanine.

This paper tackles the influence of the functionalization of polystyrene and graphene oxide (GO) composites on the flammability characteristics. A microscale combustion calorimeter (MCC) was used to experimentally determine the heat release capacity (HRC), the specific heat release rate (HRR) and the total heat released (THR). Neural models were designed that correlate the THR with a number of parameters related to the composition and type of flame retardant used, the heating rate, the amount of residue, the HRC, the peak heat release rate (PHRR), the temperature at the peak pyrolysis rate (TPHRR) and the time elapsed until the occurrence of the peak heat release rate (Time). The best results in the training, validation and testing stages were achieved with the neural model with 9 neurons in the input layer, 40 neurons in the hidden layer and one neuron in the output layer. This model was incorporated into an optimization procedure, based on a genetic algorithm, to establish the values of the input parameters used in the training of the neural networks, in order to generate a minimum THR value, which is the output parameter. Since the synthesis of polystyrene particles with different GO concentrations is costly, this research helps to reduce the number of experimental tests and allows to determine the best GO concentration by means of neural models and genetic algorithms.

For the development of memory devices for the continuous advancement of IT engineering, a good understanding of the charging-discharging mechanisms in nanocrystalline floating gate memories is crucial to overcoming the current limitations. The charging-discharging mechanism in Al2O3/Ge/Al2O3 trilayer memory structures obtained by magnetron sputtering deposition is investigated as a function of the postdeposition annealing temperature, up to 900 degrees C. The change by annealing of C-V hysteresis curves from a clockwise type at low temperatures to counterclockwise one in a sample annealed within the intermediary temperature range of 550 to 650 degrees C, and then, a return to a clockwise type for annealing within the higher temperature range of 800-900 degrees C was observed. Up to 700 degrees C, memory performances are constantly improved reaching for 600 degrees C annealed samples, a memory window of 5.6 V for voltage sweep in the range -1 to +15 V, and good retention characteristics for 650 degrees C annealed structures, in which the charge loss is only similar to 2% after 10(8) s. When the annealing temperature was increased above 700 degrees C, a rapid decrease in the memory performance takes place. The annealing-induced changes are explained based on the Ge fast diffusion and nanocrystallization process, in correlation with morphological and structural high-resolution transmission electron microscopy results.

This study reports the development of a novel biocomposite for potential applications in the environmental remediation. The hydroxyapatite/sodium bicarbonate (HAp-SB) biocomposite obtained by a cheap method could offer promising characteristics to be used in environmental applications. The obtaining of HAp-SB ceramic composites was studied with the aim of increasing the adsorption efficiency of lead ions from contaminated waters. A composite material (HAp-SB) with good crystallinity that preserves the hexagonal structure of pure hydroxyapatite was obtained. For the powder recovered after decontamination of the lead solution (PbHAp-SB), the XRD model highlighted additional maxima belonging to Ca10(PO4)5(OH)2, Ca0.805Pb4.195(PO4)(OH) and PbH2P2O7. The FTIR spectra of PbHAp-SB are similar to those of HAp-SB composites showing a broadening of the vibration peaks and a slight shift. The XPS and EDS studies illustrated the purity of the HAp-SB sample. Moreover, the presence of lead in the powder recovered after decontamination was also highlighted by XPS and EDS studies. The efficiency of HAp-SB in the adsorption of Pb2+ ions from the contaminated solution was also highlighted by ultrasound studies using double-distilled water as the reference liquid. The adsorption kinetics were investigated with the aid of Langmuir and Freundlich theoretical models. The results demonstrated that the HAp-SB ceramic composite has a strong affinity for the adsorption of Pb2+ ions from contaminated solutions. The removal efficiency of Pb2+ ions was about 92% for the initial Pb2+ concentration above 50 mg/L. The results of the cell viability and cytotoxicity studies demonstrated that HAp-SB nanoparticles did not influence negatively the HeLa cell's viability and did not induce any significant changes of the morphological features of HeLa cells after 24 h of incubation. The batch adsorption results as well as the cytotoxicity assay results suggested that the HAp-SB powder could be successfully used for the removal of Pb2+ from contaminated water.

Electrospun nanofibres based on poly(styrene sulfonate) doped poly(3,4-ethylenedioxythiophene) (PEDOT:PSS) were fabricated using a straightforward procedure which combines electrospinning, sputtering deposition and electrochemical synthesis. In general, electrospun fibre meshes based on conducting polymers are prepared by mixing the conducting polymer with a carrier polymer or chemically coverage of the fibres. In contrast, freestanding nylon 6/6 nanofibre webs were prepared through electrospinning and were coated by sputtering with gold in order to make them conductive. Further, a PEDOT:PSS layer was electrochemically deposited onto the metalized nanofibre meshes and the synthesis parameters were chosen in such a way to preserve the high active area of the fibres. The prepared material was morphologically characterized and the formation of PEDOT:PSS was also demonstrated. The PEDOT:PSS coated nanofibres revealed remarkable electrical properties (sheet resistance of about 3.5 Omega cm(-2)), similar to those of metalized nanofibres (sheet resistance around 3 Omega cm2). The in vitro studies using L929 fibroblast mouse cells showed that the bioactive material has no cytotoxic effect and allows proliferation. Moreover, after 72 h of incubation, the fibroblasts shrunk their nuclei and spread suggesting that a differentiation in myofibroblast occurs without application of any kind of external stimuli. These results will be helpful for developing efficient materials for wound healing applications that work without energy consumption.

The paper describes the chemical modification of the graphene oxide (GO) surface with glucosamine, which was conjugated to GO via a carbodiimide-mediated amidation-type reaction. The efficiency of the reaction was confirmed by FT-IR and Raman spectroscopy and elemental analysis. The elaborated functionalization significantly reduces the agglomeration of graphene oxide platelets. The interactions at the interface of GO and two types of ceramic nanoparticles (ZrO2 and Al2O3 with particle sizes of 58 nm and 158 nm, respectively) were examined by zeta potential measurements at different pH values. The viscosity of ZrO2 suspensions (35 vol% of solid loading) at 1.5 s- 1 increases from 24.8 Pas to 170.7 Pas and 142.7 Pas with the addition of GO and f-GO, respectively. The interfaces at ceramic-graphene heterostructures obtained by slip casting method have been analyzed by SEM. The investigations revealed the presence of multilayer graphene oxide and flexible single-layer f-GO within the ceramic matrix.

For the development of memory devices for the continuous advancement of IT engineering, a good understanding of the charging-discharging mechanisms in nanocrystalline floating gate memories is crucial to overcoming the current limitations. The charging-discharging mechanism in Al2O3/Ge/Al2O3 trilayer memory structures obtained by magnetron sputtering deposition is investigated as a function of the postdeposition annealing temperature, up to 900 degrees C. The change by annealing of C-V hysteresis curves from a clockwise type at low temperatures to counterclockwise one in a sample annealed within the intermediary temperature range of 550 to 650 degrees C, and then, a return to a clockwise type for annealing within the higher temperature range of 800-900 degrees C was observed. Up to 700 degrees C, memory performances are constantly improved reaching for 600 degrees C annealed samples, a memory window of 5.6 V for voltage sweep in the range -1 to +15 V, and good retention characteristics for 650 degrees C annealed structures, in which the charge loss is only similar to 2% after 10(8) s. When the annealing temperature was increased above 700 degrees C, a rapid decrease in the memory performance takes place. The annealing-induced changes are explained based on the Ge fast diffusion and nanocrystallization process, in correlation with morphological and structural high-resolution transmission electron microscopy results.

In order to develop the building blocks for future biosensing and spintronic applications, an engraving technique using electron beam lithography is employed in order to develop nanomagnetic pre-patterned structures with logic potential. The paper describes the realization and morphological and magnetic characterization of potentially logic-conditioned substrates, a building block to be further used as an integration platform upon which nanodevices, such as magnetic wires, or various geometrical shapes, circles, triangles, can be considered as pre-requisite for full integration into logic devices. As a proof of concept, regular arrays of FePt circles or magnetic dots were devised and structural characterization by X-ray diffraction and transmission electron microscopy proved the occurrence of the tetragonal L1(0) phase. Moreover, the magnetic characterization provided more insight into the potential of such arrays of magnetic devices as the hysteresis provided good values of magnetic coercivity, remanent and saturation magnetization. These findings show good potential for developing regular arrays of uniformly shaped magnetic entities with encouraging magnetic performances in view of potential applications in various applications.

In this work, electrochemical deposition techniques (galvanostatic and potentiostatic) were used to obtain coatings of a new composite polymer, 3-methylpyrrole-sodium dodecyl sulfate/poly 2-methythiophene (P3MPY-SDS/P2MT), on cobalt-based alloy samples for anti-corrosion safety. The use of sodium dodecyl sulfate as a dopant ion in electrosynthesis can have a relevant effect on the anticorrosive property of the composite polymer layer by blocking the entry of corrosive ions. The cobalt alloy specimen had an important impact on the electrochemical performance of the composite coating and this together with the presence of the polymeric layer was achieved by simultaneously constitution of a complex oxides film and polymeric layers. The polymeric coatings were analyzed using scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) spectroscopy, and cyclic voltammetry (CV) methods. The corrosion protection of the P3MPY-SDS/P2MT-covered cobalt-based alloy was explored using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization procedures in a 1 M HCl solution. The corrosion speed of the P3MPY-SDS/P2MT-covered cobalt-based alloy was observed to be similar to 10 times less than an uncovered specimen, and the effectiveness of the composite layers of this coating is greater than 91%. This superior efficaciousness was obtained by the electropolymerization of P3MPY-SDS/P2MT at current densities of 1 mA/cm(2) and 0.5 mA/cm(2), applied potentials of 0.9 V and 1.0 V, and a molar ratio of 5:1. Corrosion test results indicate that the P3MPY-SDS/P2MT coatings provide a good result: protection against the corrosion of a cobalt-based alloy in aggressive solutions.