National Institute Of Materials Physics - Romania

This study presents the design and manufacture of metasurface lenses optimized for focusing light with 1.55 mu m wavelength. The lenses are fabricated on silicon substrates using electron beam lithography, ultraviolet-nanoimprint lithography and cryogenic deep reactive-ion etching techniques. The designed metasurface makes use of the geometrical phase principle and consists of rectangular pillars with target dimensions of height h = 1200 nm, width w = 230 nm, length l = 354 nm and periodicity p = 835 nm. The simulated efficiency of the lens is 60%, while the master lenses obtained by using electron beam lithography are found to have an efficiency of 45%. The lenses subsequently fabricated via nanoimprint are characterized by an efficiency of 6%; the low efficiency is mainly attributed to the rounding of the rectangular nanostructures during the pattern transfer processes from the resist to silicon due to the presence of a thicker residual layer.

In this paper, three deposition techniques are combined to create a window material with high average transmission at oblique angles of incidence. Spectrophotometry and ellipsometry measurements, respectively, yield the optical constants n and k. In contrast with other analyses on the subject, a high average transmission, higher than 91% in the 450-900 nm spectral range, is obtained at incident angles of 20-25 degrees. The refractive index and extinction coefficient are determined by the Swanepoel method. The iterative optimization performed using the OpenFilters software leads to an antireflection (AR) multilayer with low reflection and high transmission. The surface quality of the films was characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM), which revealed compact, continuous, and smooth films.

In this work, synthesis and optical properties of a new composite based on poly(o-phenylenediamine) (POPD) fiber like structures, poly(vinylidene fluoride) (PVDF) spheres and double-walled carbon nanotubes (DWNTs) are reported. As increasing the PVDF weight in the mixture of the chemical polymerization reaction of o-phenylenediamine, the presence of the PVDF spheres onto the POPD fibers surface is highlighted by scanning electron microscopy (SEM). The down-shift of the Raman line from 1421 cm(-1) to 1415 cm(-1) proves the covalent functionalization of DWNTs with the POPD-PVDF blends. The changes in the absorbance of the IR bands peaked around 840, 881, 1240 and 1402 cm(-1) indicate hindrance steric effects induced of DWNTs to the POPD fiber like structures and the PVDF spheres, as a consequence of the functionalization process of carbon nanotubes with macromolecular compounds. The presence of the PVDF spheres onto the POPD fiber like structures surface induces a POPD photoluminescence (PL) quenching process. An additional PL quenching process of the POPD-PVDF blends is reported to be induced in the presence of DWNTs. The studies of anisotropic PL highlight a change of the angle of the binding of the PVDF spheres onto the POPD fiber like structures surface from 50.2 degrees to 38 degrees when the carbon nanotubes concentration increases in the POPD-PVDF/DWNTs composites mass up to 2 wt.%.

The Laser-induced Thermionic Vacuum Arc method was applied to optimize magnesium-silver (Mg:Ag) alloys, which can be potentially used as stable metallic cathodes for optoelectronic devices. Besides lowering the cathode work function given by the magnesium that improves the electron injection, Mg:Ag alloys induce a higher electrical conductivity, estimated here to be 3.42 x 10(7) S m(-1) for AgMg3, compared with 2.64 x 10(7) S m(-1), estimated here for Mg thin films. Mg:Ag alloys avoid the critical issue of Mg oxidation for better charge injection in optoelectronic active layers. By improving the Thermionic Vacuum Arc technique with the laser beam, this method enables the control of the silver concentration in these alloys due to photonic processes. The uniformity of metallic thin films, compactness, and high purity are the primary advantages of the Laser-induced Thermionic Vacuum Arc method. (C) 2021 Elsevier B.V. All rights reserved.

The electrochemical behavior and the interaction of the immunosuppressive drug azathioprine (AZA) with deoxyribonucleic acid (DNA) were investigated using voltammetric techniques, mass spectrometry (MS), and scanning electron microscopy (SEM). The redox mechanism of AZA on glassy carbon (GC) was investigated using cyclic and differential pulse (DP) voltammetry. It was proven that the electroactive center of AZA is the nitro group and its reduction mechanism is a diffusion-controlled process, which occurs in consecutive steps with formation of electroactive products and involves the transfer of electrons and protons. A redox mechanism was proposed and the interaction of AZA with DNA was also investigated. Morphological characterization of the DNA film on the electrode surface before and after interaction with AZA was performed using scanning electron microscopy. An electrochemical DNA biosensor was employed to study the interactions between AZA and DNA with different concentrations, incubation times, and applied potential values. It was shown that the reduction of AZA molecules bound to the DNA layer induces structural changes of the DNA double strands and oxidative damage, which were recognized through the occurrence of the 8-oxo-deoxyguanosine oxidation peak. Mass spectrometry investigation of the DNA film before and after interaction with AZA also demonstrated the formation of AZA adducts with purine bases.

In the present study, we report the synthesis of a dextran coated iron oxide nanoparticles (DIO-NPs) thin layer on glass substrate by an adapted method. The surface morphology of the obtained samples was analyzed by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), optical, and metallographic microscopies. In addition, the distribution of the chemical elements into the DIO-NPs thin layer was analyzed by Glow Discharge Optical Emission Spectrometry (GDOES). Furthermore, the chemical bonds formed between the dextran and iron oxide nanoparticles was investigated by Fourier Transform Infrared Spectroscopy (FTIR). Additionally, the HepG2 viability incubated with the DIO-NPs layers was evaluated at different time intervals using MTT (3-(4, 5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay. The goal of this study was to obtain a DIO-NPs thin layer which could be used as a coating for medical devices such as microfluidic channel, microchips, and catheter. The results of the surface morphology investigations conducted on DIO-NPs thin layer suggests the presence of a continuous and homogeneous layer. In addition, the GDOES results indicate the presence of C, H, Fe, and O signal intensities characteristic to the DIO-NPs layers. The presence in the IR spectra of the Fe-CO metal carbonyl vibration bonds prove that the linkage between iron oxide nanoparticles and dextran take place through carbon-oxygen bonds. The cytotoxicity assays highlighted that HepG2 cells morphology did not show any noticeable modifications after being incubated with DIO-NPs layers. In addition, the MTT assay suggested that the DIO-NPs layers did not present any toxic effects towards HEpG2 cells.

Cation-substituted hydroxyapatite (HA), standalone or as a composite (blended with polymers or metals), is currently regarded as a noteworthy candidate material for bone repair/regeneration either in the form of powders, porous scaffolds or coatings for endo-osseous dental and orthopaedic implants. As a response to the numerous contradictions reported in literature, this work presents, in one study, the physico-chemical properties and the cytocompatibility response of single cation-doped (Ce, Mg, Sr or Zn) HA nanopowders in a wide concentration range (0.5-5 at.%). The modification of composition, morphology, and structure was multiparametrically monitored via energy dispersive X-ray, X-ray photoelectron, Fourier-transform infrared and micro-Raman spectroscopy methods, as well as by transmission electron microscopy and X-ray diffraction. From a compositional point of view, Ce and Sr were well-incorporated in HA, while slight and pronounced deviations were observed for Mg and Zn, respectively. The change of the lattice parameters, crystallite size, and substituting cation occupation factors either in the Ca(I) or Ca(II) sites were further determined. Sr produced the most important HA structural changes. The in vitro biological performance was evaluated by the (i) determination of leached therapeutic cations (by inductively coupled plasma mass spectrometry) and (ii) assessment of cell behaviour by both conventional assays (e.g., proliferation-3-(4,5-dimethyl thiazol-2-yl) 5-(3-carboxymethoxyphenyl)-2-(4-sulfophenyl)-2H-tetrazolium assay; cytotoxicity-lactate dehydrogenase release assay) and, for the first time, real-time cell analysis (RTCA). Three cell lines were employed: fibroblast, osteoblast, and endothelial. When monophasic, the substituted HA supported the cells' viability and proliferation without signs of toxicity. The RTCA results indicate the excellent adherence of cells. The study strived to offer a perspective on the behaviour of Ce-, Mg-, Sr-, or Zn-substituted HAs and to deliver a well-encompassing viewpoint on their effects. This can be highly important for the future development of such bioceramics, paving the road toward the identification of candidates with highly promising therapeutic effects.

Composites of magnetite (Fe3O4) nanoparticles dispersed in a polydimethylsiloxane (PDMS) matrix were prepared by a molding process. Two types of samples were obtained by free polymerization with randomly dispersed particles and by polymerization in an applied magnetic field. The magnetite nanoparticles were obtained from magnetic micrograins of acicular goethite (alpha-FeOOH) and spherical hematite (alpha-Fe2O3), as demonstrated by XRD measurements. The evaluation of morphological and compositional properties of the PDMS:Fe3O4 composites, performed by SEM and EDX, showed that the magnetic particles were uniformly distributed in the polymer matrix. Addition of magnetic dispersions promotes an increase of thermal conductivity compared with pristine PDMS, while further orienting the powders in a magnetic field during the polymerization process induces a decrease of the thermal conductivity compared with the un-oriented samples. The shape of the magnetic dispersions is an important factor, acicular dispersions providing a higher value for thermal conductivity compared with classic commercial powders with almost spherical shapes.

The structure of the IrQ(ppy)(2) organometallic dual phosphorescent compound was experimentally and theoretically investigated. The Metal-to-Ligand Charge Transfer toward the phenylpiridine and quinoline ligands explains its dual phosphorescence property. The IrQ(ppy)(2) organometallic's electronic properties extend the absorption spectra toward the lower energies than Ir(ppy)(3) due to the bandgap reduction induced by the quinoline ligand. The magneto-optical measurements reveal A-terms, which are produced by splitting the triplet states and B-terms, which arise when the electronic levels are mixed in the magnetic field. The IrQ(ppy)(2) molecule's transport properties confirm an ambipolar character, consisting of a higher hole transport character induced by the phenyilpiridine ligands and a lower electron transport character induced by the quinoline ligand. (C) 2021 Elsevier B.V. All rights reserved.

The effect of temperature on the features of the crystal and magnetic structures, as well as the magnetic properties of the solid solution of SrFe10.8In1.2O19 hexaferrite was investigated. The appearance of ferroelectric properties was detected at room temperature, which contradicts the generally accepted opinion on the description of the crystal structure of hexaferrites within the framework of the centrosymmetric P6(3)/mmc (No. 194) space group. The reasons of spontaneous polarization in solid solutions of hexaferrites remain controversial. No deviation from the collinear magnetic structure was found in the investigated temperature range from 1.5 to 350 K, while the thermal expansion of the unit cell was practically absent in the range from 1.5 to 50 K. The crystal structure of hexaferrites was considered in the framework of both centrosymmetric P6(3)/mmc and non-centrosymmetric P6(3)mc space groups, which allowed us to associate the emerging spontaneous polarization with unequal distortions of neighboring oxygen polyhedra.