National Institute Of Materials Physics - Romania

Novel metal nanoporous transition metal oxides M (x) O (y) (Co3O4, CuO) have been synthesized by thermal decomposition of inorganic salts precursors (acetates, nitrates) impregnated into hexagonal mesoporous silica (OMS, ordered mesoporous silica) of SBA-15 type (prepared in-house) at different precursor loadings, the mesocomposites thus obtained being monitored after each impregnation-calcination step by small and wide angle powder XRD. The pore size for the ordered silica host range from 5.08 to 7.06 nm. Retention of the hexagonal silica framework has been observed in spite of the temperatures up to 500 A degrees C. Mesoporous Co3O4 has been obtained by leaching the silica through overnight HF dissolution, which partially preserved the small-range ordering found in the parent Co3O4@OMS composite prior to leaching. Both Co3O4 (meso) and Co3O4@SBA-15 have been tested in methane oxidation and were found to be superior to the bulk Co3O4 performance, with mesoporous Co3O4 being able to fully oxidize methane to CO2 and H2O at 350 A degrees C, while Co3O4@OMS exhibits a lower activity with 20 % conversion at 350 A degrees C. CuO@OMS shows the lowest activity, with only similar to 13 % conversion at 500 A degrees C.

Magnetoresistive Fe-Co based thin film structures were produced using thermionic vacuum arc method. The purpose of this work was to obtain significant magnetic response on different granular combinatorial structures. The Giant Magnetoresistive (GMR) and combination between GMR and Tunneling Magnetoresistive (TMR) properties of the thin film structures were the aim of the work. The proposed method in order to obtain the desired granular structures is based on electron beam emitted by an externally heated cathode, accelerated by a high anodic potential. The work consisted in preparing two sets of samples, first being a combination between Fe-Co as magnetic materials embedded in a Cu matrix, with a total thickness of 200 nm. The second structure was a combination between Fe-Co (50%-50%) alloy, embedded in a matrix of Cu combined with MgO with a thickness of 200 nm. Both sets of samples were obtained by three simultaneous types of discharges. Because of the substrate positioning in respect with the three anode-cathode systems, different material concentrations were obtained, confirmed by Energy Dispersive Spectroscopy (EDS) measurement results. Structural and morphological properties were investigated using Scanning Electron Microscopy; Atomic Force Microscopy and EDS. Electrical properties of the obtained samples were studied using the 4 point measurement method. The magnetic properties were first studied using a non-destructive optical method called MOKE (Magneto-Optical Kerr Effect). Electrical resistance behavior of the granular type structures was studied for different values of the magnetic field, up to 03 T, at different values of the sample temperature. The magnetoresistive effect obtained for the two sets of samples varied from 1.5% to 81% in respect with the substrate positioning and sample temperature for a constant magnetic field. (C) 2014 The Authors. Published by Elsevier B.V. All rights reserved.

In order to study specific phenomena at ferromagnetic/semiconducting interfaces, of potentially high interest in spintronics and information technology, structural aspects and magnetic properties of Fe thin films grown on Si(001) substrates by RF sputtering have been investigated using Fe-57 conversion electron Mossbauer spectroscopy (CEMS) and magneto-optic Keer effect (MOKE). Films of different thicknesses have been deposited either directly on crystalline Si substrates or on Cu buffer layers. An inherent Fe oxide layer is observed in all as prepared films, with a relative thickness decreasing drastically with the deposition time. The Cu buffer layer does not diminish either the interfacial diffusion or the oxidation process. An efficient method to prepare sharper oxygen- and silicon-free interfaces for an improved spin injection, via thermal treatment in hydrogen atmosphere, is proposed. Accordingly, the hydrogenation treatments are very efficient in the modification of the ferromagnetic film structure, phase composition, magnetic properties and interfacial mixing. (C) 2013 Elsevier B.V. All rights reserved.

The FePt system has important perspectives as high-temperature corrosion-resistant magnets. In the form of rapidly solidified melt-spun ribbons, FePt-based magnets may exhibit in certain cases a two-phase hard-soft magnetic behaviour. The present paper deals with a microstructural and magnetic study of FePtAgB alloys with increasing Ag content. The aim is to identify and confirm the effect of Ag addition in decreasing the temperature of the FePt disorder-order structural phase transformation. A detailed high-resolution transmission electron microscopy study is employed, and the alternative disposal of hard and soft regions within the two-phase microstructure is observed and interpreted with respect to the X-ray diffraction results. In the as-cast Ag-containing samples, it is shown that there is an optimum of the Ag content for which best magnetic properties are obtained. Ag addition creates a nonlinear behaviour of the coercive field and the ordering parameter, similar to the RKKY interaction-induced interlayer exchange coupling (IEC) observed in magnetic layers separated by non-magnetic spacer layers. Direct formation of the L1(0) phase from the as-cast state in the FePtAgB alloys is reported with magnetic parameters compatible to other exchange spring permanent nanomagnets. These findings open novel perspectives into utilization of such alloys in applications requiring magnets operating in high-temperature industrial environments.

We report the synthesis of a room temperature ferromagnetic Mn-Ge system obtained by simple deposition of manganese on Ge(001), heated at relatively high temperature (starting with 250 degrees C). The samples were characterized by low energy electron diffraction (LEED), scanning tunneling microscopy (STM), high resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), superconducting quantum interference device (SQUID), and magneto-optical Kerr effect (MOKE). Samples deposited at relatively elevated temperature (350 degrees C) exhibited the formation of similar to 5-8 nm diameter Mn5Ge3 and Mn11Ge8 agglomerates by HRTEM, while XPS identified at least two Mn-containing phases: the agglomerates, together with a Ge-rich MnGe similar to 2.5 phase, or manganese diluted into the Ge(001) crystal. LEED revealed the persistence of long range order after a relatively high amount of Mn (100 nm) deposited on the single crystal substrate. STM probed the existence of dimer rows on the surface, slightly elongated as compared with Ge-Ge dimers on Ge(001). The films exhibited a clear ferromagnetism at room temperature, opening the possibility of forming a magnetic phase behind a nearly ideally terminated Ge surface, which could find applications in integration of magnetic functionalities on semiconductor bases. SQUID probed the co-existence of a superparamagnetic phase, with one phase which may be attributed to a diluted magnetic semiconductor. The hypothesis that the room temperature ferromagnetic phase might be the one with manganese diluted into the Ge crystal is formulated and discussed.

Thin films of Bi2Sr2CuO6 (Bi-2201) with (001) or (115) orientation were grown on SrTiO3 substrates. These films are expected to be useful as component films of heterostructures and devices (e.g. as insulators). We used two chemical routes, namely spin coating followed by thermal annealing and MOCVD. For both routes we demonstrated growth of c-axis and non-c axis thin films depending on the selected orientation of the SrTiO3 substrate. To our knowledge, films of (115) Bi2201 obtained by spin coating or MOCVD are reported for the first time.

Low dimensional nanostructures represent a hot scientific field nowadays due mainly to the tremendous potential for applications. Low dimensions open the possibilities for both ultra-miniaturization and increase in functionality. Numerous procedures were developed for fabricating such nanostructures. Template replication represents a highly effective method in fabricating metallic nanowires and nanotubes. The approach is characterized by the excellent control in obtaining nano objects with the desired shape and dimensions. A large variety of templates are available ranging from viruses and proteins to nanoporous membranes fabricated by using swift heavy ion accelerators. In the following chapter the main steps involved in employing the method for fabricating metalic nanowires and nanotubes by replicating ion track nanoporous membranes were described. The steps include here membrane fabrication and replication and involve track etching and electrochemical metal deposition. The influence of the process parameters on the properties of the nanoobjects prepared by this approach was reviewed. It was found that simple experimental parameters can be chosen in such a way that the functionality of the nanowires or nanotubes can be finely tuned.

One of the focal subjects in insulin delivery is the development of insulin formulations that protect the native insulin from degradation under acidic pH in the stomach. In this work we show, for the first time, that a graphene oxide (GO) based matrix can ensure the stability of insulin at low pH. GO and GO modified with 2-nitrodopamine coated magnetic particle (GO-MPdop) matrices loaded with insulin were prepared and the pH triggered release of the insulin was studied. The loading of insulin on the GO nanomaterials proved to be extremely high at pH < 5.4 with a loading capacity of 100 +/- 3% on GO and 88 +/- 3% on GO-MPdop. The insulin-containing GO matrices were stable at acidic pH, while insulin was released when exposed to basic solutions (pH = 9.2). Using Xenopus laevis oocytes as a model we showed that the meiotic resumption rate of GO and GO-MPdop remained unaltered when pre-treated in acidic conditions, while pre-incubated insulin (without GO nanomaterials) has lost almost entirely its maturation effect. These results suggest that GO based nanomatrices are promising systems for the protection of insulin.

Finite size effects and interfacial interactions as well as their influence on the magnetic properties of nanosized systems are discussed by starting from very basic principles of magnetism. Some preparation and subsequent processing tools for a proper engineering of the properties of such magnetic nanosized systems are introduced together with specific characterization tools. A summary of the most important technological applications related to size effects and interfacial interactions, with exemplifications starting from bio-medical applications of magnetic fluids to magnetoresitive multilayers for sensor applications are also provided.

Vortex pinning on natural and artificial defects is essential for large scale applications of superconducting materials. One of the most promising solutions for the creation of efficient pinning structures is to combine the strong pinning supplied by columnar defects (with the radius of the order of the superconducting coherence length) and the presence of random quenched disorder, which inhibits the detrimental vortex kink formation. A strong pinning is revealed by high values of the vortex activation energy in the magnetic relaxation process. We present a critical analysis of the interpretation of the relaxation data at long- and short time scales, by extracting the so called normalized vortex-creep activation energy. This allowed us to find the actual temperature interval for the characteristic vortex excitations in YBa2Cu3O7 films with embedded BaZrO3 nanorods 9preferentially oriented along the c axis), and to unambiguously determine the characteristic vortex pinning energy. The observed drastic change of magnetic relaxation at short time scales (attained in standard AC measurements) is attributed to a large contribution of the pinning enhanced viscosity to the vortex hopping activation energy.