National Institute Of Materials Physics - Romania

Biopolymers provide versatile platforms for designing naturally-derived wound care dressings through eco-friendly pathways. Eggshell membrane (ESM), a widely available, biocompatible biopolymer based structure features a unique 3D porous interwoven fibrous protein network. The ESM was functionalized with inorganic compounds (Ag, ZnO, CuO used either separately or combined) using a straightforward deposition technique namely radio frequency magnetron sputtering. The functionalized ESMs were characterized from morphological, structural, compositional, surface chemistry, optical, cytotoxicity and antibacterial point of view. It was emphasized that functionalization with a combination of metal oxides and exposure to visible light results in a highly efficient antibacterial activity against Escherichia coli when compared to the activity of individual metal oxide components. It is assumed that this is possible due to the fact that an axial p-n junction is created by joining the two metal oxides. This structure separates into components the charge carrier pairs promoted by visible light irradiation that further can influence the generation of reactive oxygen species which ultimately are responsible for the bactericide effect. This study proves that, by employing inexpensive and environmentally friendly materials (ESM and metal oxides) and fabrication techniques (radio frequency magnetron sputtering), affordable antibacterial materials can be developed for potential applications in chronic wound healing device area.

Due to the extraordinary versatility of the perovskite structure in accommodating different dopant ions in its structure, in recent years a huge number of multifunctional perovskite materials have been developed. In this work we aim to obtain high temperature-stable and huge dielectric constant materials for supercapacitors by doping divalent Mg2+ and trivalent Sb3+ ions into the octahedral sites, and divalent Sr2+ ions into the dodecahedral sites of lead zirconate-titanate perovskite. The resulting (Pb0.95Sr0.05)(Zr0.425Ti0.45Mg0.042Sb0.083)O3-delta is examined by X-ray diffraction, energy-dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy (XPS), high resolution transmission electron microscopy (HRTEM), dielectric spectroscopy (DS) and resonance dielectric spectroscopy (RDS) in order to correlate composition, local structure, ion valence and chemical environment of the doped material with the dielectric properties. HRTEM evidences that a composite structure, with co-existent ferroelectric domains and relaxor nanodomains, is formed by doping. XPS shows that Sb3+ and Mg2+ substitute for the Ti4+/Zr4+ ions, pointing to these strong defects as the main cause for the appearance of the relaxor phase. DS and RDS found that the ferroelectric lead zirconate-titanate transforms into a re-entrant relaxorferroelectric composite with a huge dielectric constant of about 10(4) which remains stable (within +/- 10%) in the high temperature range up to 250 degrees C, pointing to this mechanism of relaxor phase re-entrance below the normal ferroelectric phase transition, as being responsible for the enhancement. (C) 2020 Elsevier Ltd. All rights reserved.

ZnO nanostructures with intrinsic and extended defects were prepared by rapid decomposition of zinc-propio-nate and annealing at 400 degrees C-970 degrees C. The correlation between the structure/morphology, type of native defects (photoluminescence (PL), EPR) and ferromagnetism was investigated, together with ammonia adsorption capacity. All the samples show room temperature ferromagnetism (RTFM). Crystallite size increases while the unit cell volume, c-axis constant, microstrain and saturation magnetization relax with increasing temperature; morphology varies from aggregated nanoparticles to frameworks of well-welded crystals. 400 degrees C-800 degrees C annealed samples show a broad visible and/or a prominent violet-blue PL emission and, two narrow g = 2.0065 and g = 1.9632 EPR signals. 800 degrees C-970 degrees C annealed samples exhibit very intense green-yellow photoluminescence. The intrinsic defects in conjunction with a deformed lattice and/or pinned by grain-boundaries appear responsible for RTFM and Curie temperature exceeding 700 degrees C. Tuning the morphology, PL intensity and ferromagnetic signal by choice of annealing temperature can find applications in (gas) sensing, photonic/optoelectronic and spintronic devices.

Silica-based bioactive glasses (SBG) hold great promise as bio-functional coatings of metallic endo-osseous implants, due to their osteoproductive potential, and, in the case of designed formulations, suitable mechanical properties and antibacterial efficacy. In the framework of this study, the FastOs(R)BG alkali-free SBG system (mol%: SiO2-38.49, CaO-36.07, P2O5-5.61, MgO-19.24, CaF2-0.59), with CuO (2 mol%) and Ga2O3 (3 mol%) antimicrobial agents, partially substituting in the parent system CaO and MgO, respectively, was used as source material for the fabrication of intentionally silica-enriched implant-type thin coatings (similar to 600 nm) onto titanium (Ti) substrates by radio-frequency magnetron sputtering. The physico-chemical and mechanical characteristics, as well as the in vitro preliminary cytocompatibility and antibacterial performance of an alkali-free silica-rich bio-active glass coating designs was further explored. The films were smooth (R-RMS < 1 nm) and hydrophilic (water contact angle of similar to 65 degrees). The SBG coatings deposited from alkali-free copper-gallium co-doped FastOs(R)BG-derived exhibited improved wear performance, with the coatings eliciting a bonding strength value of similar to 53 MPa, Lc3 critical load value of similar to 4.9 N, hardness of similar to 6.1 GPa and an elastic modulus of similar to 127 GPa. The Cu and Ga co-doped SBG layers had excellent cytocompatibility, while reducing after 24 h the Staphylococcus aureus bacterial development with 4 orders of magnitude with respect to the control situations (i.e., nutritive broth and Ti substrate). Thereby, such SBG constructs could pave the road towards high-performance bio-functional coatings with excellent mechanical properties and enhanced biological features (e.g., by coupling cytocompatibility with antimicrobial properties), which are in great demand nowadays.

In this work, new evidence for the photodegradation reactions of acetaminophen (AC) is reported by photoluminescence (PL), Raman scattering and FTIR spectroscopy. Under excitation wavelength of 320 nm, AC shows a PL band in the spectral range of 340-550 nm, whose intensity decreases by exposure to UV light. The chemical interaction of AC with the NaOH solutions, having the concentration ranging between 0.001 and 0.3 M, induces a gradual enhancement of the photoluminescence excitation (PLE) and PL spectra, when the exposure time of samples at the UV light increases until 140 min, as a result of the formation of p-aminophenol and sodium acetate. This behavior is not influenced by the excipients or other active compounds in pharmaceutical products as demonstrated by PLE and PL studies. Experimental arguments for the obtaining of p-aminophenol and sodium acetate, when AC has interacted with NaOH, are shown by Raman scattering and FTIR spectroscopy.

The development of robust, safe, cost-effective and efficient photocatalytic systems for water splitting should take into account the presence of a proper and powerful photon absorber and an efficient, low-cost and earth-abundant electrocatalyst to perform the reaction at high conversions. In this study, Ni-Zn/TiO(2)ternary composites with high photocatalytic activity for water splitting under UV irradiation were successfully prepared via a simple and low-cost deposition-precipitation route. Thus, different Ni : Zn molar ratios (1 : 0, 1 : 1, 3 : 1, 6 : 1, 9 : 1, and 0 : 1) were deposited on TiO(2)in order to reach a total metal loading of 50 wt. %. The obtained composites were characterized using several techniques, such as: X-ray diffraction, UV-Vis spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The most active synthesized composite, namely Ni-Zn/TiO2(9 : 1), exhibits H(2)generation rate above 17 mmols g(-1) h(-1), which is nearly one thousand times higher than that obtained with TiO(2)Evonik P25. Our study demonstrates that TiO(2)becomes a degenerated semiconductor in the presence of Ni and ZnO, with remarkable photocatalytic properties. Thus, the obtained results can open new opportunities in the preparation of very active materials for hydrogen production based on the optimization of three-component structures.

The development of robust, safe, cost-effective and efficient photocatalytic systems for water splitting should take into account the presence of a proper and powerful photon absorber and an efficient, low-cost and earth-abundant electrocatalyst to perform the reaction at high conversions. In this study, Ni-Zn/TiO(2)ternary composites with high photocatalytic activity for water splitting under UV irradiation were successfully prepared via a simple and low-cost deposition-precipitation route. Thus, different Ni : Zn molar ratios (1 : 0, 1 : 1, 3 : 1, 6 : 1, 9 : 1, and 0 : 1) were deposited on TiO(2)in order to reach a total metal loading of 50 wt. %. The obtained composites were characterized using several techniques, such as: X-ray diffraction, UV-Vis spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The most active synthesized composite, namely Ni-Zn/TiO2(9 : 1), exhibits H(2)generation rate above 17 mmols g(-1) h(-1), which is nearly one thousand times higher than that obtained with TiO(2)Evonik P25. Our study demonstrates that TiO(2)becomes a degenerated semiconductor in the presence of Ni and ZnO, with remarkable photocatalytic properties. Thus, the obtained results can open new opportunities in the preparation of very active materials for hydrogen production based on the optimization of three-component structures.

The objective of the present study is the valorization of natural resources and the recycling of vegetal wastes by converting them into novel plasmonic bio-active hybrids. Thus, a "green" approach was used to design pectin-coated bio-nanosilver. Silver nanoparticles were generated from two common garden herbs (Mentha piperitaandAmaranthus retroflexus), and pectin was extracted from lemon peels. The samples were characterized by the following methods: Ultraviolet-visible (UV-Vis) absorption spectroscopy, Fourier Transform Infrared (FT-IR), X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), dynamic light scattering (DLS), Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM)-Energy-dispersive X-ray Spectroscopy (EDX), and zeta potential measurements. Microscopic investigations revealed the spherical shape and the nano-scale size of the prepared biohybrids. Their bioperformances were checked in terms of antioxidant and antibacterial activity. The developed plasmonic materials exhibited a strong ability to scavenge short-life (96.1% divided by 98.7%) and long-life (39.1% divided by 91%) free radicals. Microbiological analyses demonstrated an impressive antibacterial effectiveness of pectin-based hybrids againstEscherichia coli. The results are promising, and the obtained biomaterials could be used in many bio-applications, especially as antioxidant and antimicrobial biocoatings.