National Institute Of Materials Physics - Romania

The discovery of multifunctional properties related to electro-activity of organic systems of biomolecules is important for a variety of applications, especially for devices in the realm of biocompatible sensors and/or bioactuators. A further step towards such applications is to prepare thin films with the required properties. Here, the investigation is focused on the characterization of films of guanine and cytosine nucleobases, prepared by thermal evaporation-an industrial accessible deposition technique. The cytosine films have an orthorhombic non-centrosymmetric structure and grow in two interconnected nanostructured fractal patterns, of nearly equal proportion. Piezoresponse force microscopy images acquired at room temperature on the cytosine films display large zones with antiparallel alignment of the vertical components of the polarization vector. Guanine films have a dense nano-grained morphology. Our studies reveal electrical polarization switching effects which can be related to ferroelectricity in the films of guanine molecules. Characteristic ferroelectric polarization-electric-field hysteresis loops showing large electrical polarization are observed at low temperatures up to 200 K. Above this temperature, the guanine films have a preponderant paraelectric phase containing residual or locally induced nano-scopic ferroelectric domains, as observed by piezoresponse force microscopy at room temperature.

The physico-chemical properties of two anhydrous AZA forms and their interaction with typical pharmaceutical excipients were assessed by applying various methods (such as PXRD, HPLC, TG/DSC, IR, Raman, PL or UV-Vis) in order to highlight new directions for drug formulation. The stability assessment of AZA anhydrous forms I and II was performed in order to determine the risk of degradation of the active ingredient by accidental exposure to nonstandard conditions in the industrial environment, under different storage, transport or processing conditions. The benefits of form II include increased resistance to chemical degradation over a wide range of pH, but further control of storage and processing conditions is necessary to avoid polymorphic transformation into form I. The solubility assessment on the AZA solid forms in different environments that simulate the conditions of the gastrointestinal tract has the advantage of a significantly increased solubility of form II compared with the commercial form I due to the modification of the crystalline structure. In the case of capsules compared to AZA form I or II as powder, an improvement in their solubility was observed, promoted by the presence of one or more excipients in the formulation mixture.

One major warning emerging during the first worldwide combat against healthcare-associated infections concerns the key role of the surface in the storage and transfer of the virus. Our study is based on the laser coating of surfaces with an inorganic/organic composite mixture of amorphous calcium phosphate-chitosan-tetracycline that is able to fight against infectious agents, but also capable of preserving its activity for a prolonged time, up to several days. The extended release in simulated fluids of the composite mixture containing the drug (tetracycline) was demonstrated by mass loss and UV-VIS investigations. The drug release profile from our composite coatings proceeds via two stages: an initial burst release (during the first hours), followed by a slower evolution active for the next 72 h, and probably more. Optimized coatings strongly inhibit the growth of tested bacteria (Enterococcus faecalis and Escherichia coli), while the drug incorporation has no impact on the in vitro composite's cytotoxicity, the coatings proving an excellent biocompatibility sustaining the normal development of MG63 bone-like cells. One may, therefore, consider that the proposed coatings' composition can open the prospective of a new generation of antimicrobial coatings for implants, but also for nosocomial and other large area contamination prevention.

Nanocomposites of isotactic polypropylene loaded by various amounts of vapor-grown carbon nanotubes ranging from 0 to 20% wt. were obtained by extrusion. Raman investigations on these nanocomposites are reported. The nanocomposites were irradiated using a Co-60, with an integral dose of 1 kGy/h up to integral doses of 9 kGy, 18 kGy, and 27 kGy, in air, at room temperature. Raman measurements were performed by using a Bruker Senterra confocal Raman spectrometer operating at 785 nm. The research is focused on the information contained within the D and G Raman lines of these nanocomposites as a function of nanotube loading for various integral doses. The experimental data revealed the graduate silencing of the molecular motions assigned to the polymeric matrix due to the nanofiller and ionizing radiation. Based on experimental data, it is concluded that the positions of the D and G lines exhibit faint shifts due to the irradiation and that (on average) these shifts are consistent with the changes of the positions of D and G lines upon the increase of the loading with vapor-grown carbon nanofibers. Raman data suggest that the irradiation relaxes the pressure exerted on the nanofiller by the polymeric matrix, indicating a path to improve the physical features of polymer-carbon nanostructure nanocomposites. The research demonstrates the capability of Raman spectroscopy to sense the modifications of molecular vibrations in polymer-based nanocomposites, for both the polymeric matrix and the nanofiller. (c) 2021 The Authors. Published by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/)

Orthorhombic HfO2 exhibits nanoscale ferroelectricity that opens the perspective of ultra-scalable CMOS integration of ferroelectric memories. However, many aspects of the metastable orthorhombic crystallization mechanisms still need to be elucidated and new fabrication methods are of high interest. In this paper, the atomically resolved crystal structure of HfO2 is a 3-layer structure with a Ge-rich HfO2 intermediate layer capped by a top (cap) HfO2 layer and cladded by a bottom HfO2 layer. There is a continuity of crystal growth from the top and bottom HfO2 layers into the intermediate layer. A spatial transition from a monoclinic phase to an orthorhombic phase was revealed within a region of a few atomic layers at the interface between capped and intermediate HfO2 layers. This result suggests the mechanism of orthorhombic and monoclinic phase formation by a martensitic-like transformation of the initially grown tetragonal phase. The sample fabrication method we used involved magnetron sputtering deposition of the 3-layer structures, i.e. a stack of top HfO2/Ge-rich HfO2 intermediate/bottom HfO2 layers, followed by rapid thermal annealing. It results in self-optimized orthorhombic crystallization of HfO2 by Ge nanoparticle segregation in the intermediate layer. The ferroelectric effects are revealed by polarization-voltage hysteresis loops and piezoresponse force microscopy measurements. The atomistic computations performed by using the density functional theory support the experimental results by showing that the Ge doping of HfO2 leads to orthorhombic phase stabilization and increased Berry phase polarization.

ZnS is a wide band gap material which was proposed as a possible candidate to replace CdS as a buffer layer in solar cells. However, the structural and optical properties are influenced by the deposition method. ZnS thin films were prepared using magnetron sputtering (MS), pulsed laser deposition (PLD), and a combined deposition technique that uses the same bulk target for sputtering and PLD at the same time, named MSPLD. The compositional, structural, and optical properties of the as-deposited and annealed films were inferred from Rutherford backscattering spectrometry, X-ray diffraction, X-ray reflectometry, Raman spectroscopy, and spectroscopic ellipsometry. PLD leads to the best stoichiometric transfer from target to substrate, MS makes fully amorphous films, whereas MSPLD facilitates obtaining the densest films. The study reveals that the band gap is only slightly influenced by the deposition method, or by annealing, which is encouraging for photovoltaic applications. However, sulphur vacancies contribute to lowering the bandgap and therefore should be controlled. Moreover, the results add valuable information towards the understanding of ZnS polymorphism. The combined MSPLD method offers several advantages such as an increased deposition rate and the possibility to tune the optical properties of the obtained thin films.

Cu2ZnSnS4 (CZTS) is a complex quaternary material, and obtaining a single-phase CZTS with no secondary phases is known to be challenging and dependent on the production technique. This work involves the synthesis and characterization of CZTS absorber layers for solar cells. Thin films were deposited on Si and glass substrates by a combined magnetron sputtering (MS) and pulsed laser deposition (PLD) hybrid system, followed by annealing without and with sulfur powder at 500 degrees C under argon (Ar) flow. Three different Cu2S, SnS2, and ZnS targets were used each time, employing a different target for PLD and the two others for MS. The effect of the different target arrangements and the role of annealing and/or sulfurization treatment were investigated. The characterization of the absorber films was performed by grazing incidence X-ray diffraction (GIXRD), X-ray reflectometry (XRR), Raman spectroscopy, scanning electron microscopy, and regular transmission spectroscopy. The film with ZnS deposited by PLD and SnS2 and Cu2S by MS was found to be the best for obtaining a single CZTS phase, with uniform surface morphology, a nearly stoichiometric composition, and an optimal band gap of 1.40 eV. These results show that a new method that combines the advantages of both MS and PLD techniques was successfully used to obtain single-phase Cu2ZnSnS4 films for solar cell applications.

In this work, the structural, thermal, vibrational, morphological, magnetic and optical properties of LaPO4:Ce/RE/Me (RE=Nd3+, Tb3+; Me-Cr3+, Mn2+) and LaPO4:Yb3+/Er3+ phosphors prepared by the co-precipitation method are presented. The obtained materials crystallized in monoclinic structure with the P2(1)/n space group and the particles were of nanorod shape with about 200 nm in length and the diameter approximately 19 nm. The presence of dopant ions was confirmed by both electron paramagnetic resonance (EPR) and UV-visible spectroscopies. In addition, the down-conversion (DC) and up-conversion (UC) of the LaPO4 nanophosphors via the 275 and 980 nm excitations, respectively, were considered, and a wide range of electronic transitions was observed. Based on the photoluminescence (PL) spectra, there is an efficient energy transfer (ET) process from Ce3+ donors to Nd3+ and Tb3+ acceptors, and the computed ET efficiency was 70% and 88%, respectively. The Ce3+/Cr3+ and Ce3+/Mn2+ doped LaPO4 showed weak far-red and green luminescence with much smaller ET efficiency of about 3.7 and 0.4%, respectively. LaPO4:Yb3+/Er3+ showed UC luminescence under the 980 nm laser radiation, and the resulted red and green light was attributed to the Er3+ transitions.

This study presents the design and manufacture of metasurface lenses optimized for focusing light with 1.55 mu m wavelength. The lenses are fabricated on silicon substrates using electron beam lithography, ultraviolet-nanoimprint lithography and cryogenic deep reactive-ion etching techniques. The designed metasurface makes use of the geometrical phase principle and consists of rectangular pillars with target dimensions of height h = 1200 nm, width w = 230 nm, length l = 354 nm and periodicity p = 835 nm. The simulated efficiency of the lens is 60%, while the master lenses obtained by using electron beam lithography are found to have an efficiency of 45%. The lenses subsequently fabricated via nanoimprint are characterized by an efficiency of 6%; the low efficiency is mainly attributed to the rounding of the rectangular nanostructures during the pattern transfer processes from the resist to silicon due to the presence of a thicker residual layer.

Surface plasmon resonance containing amorphous As2S3 film is proposed as a chemical sensor to highlight several liquid hydrocarbons. Method is label-free and is based on detection of small changes in the refractive index. As2S3 operates as plasmonic waveguide which confines the probing beam to the interface with liquid hydrocarbons. The method can easily distinguish hydrocarbons with very close refractive indices. The film thicknesses were optimized to obtain the best sensitivity and resolving power Minimum reflectance of SPR less than 1 % was found for optimal calculated film thicknesses, the sensitivity to the refractive index changes being 2.10(-5).