National Institute Of Materials Physics - Romania

This work presents a new synthesis and characterization of Kesterite Cu2ZnSnS4 films by one step electrodeposition with free sulfurization annealing treatment at different applied potentials. This study highlights the effect of applied potential and annealing treatment on the properties of CZTS deposited films. X-ray Diffraction and Raman spectroscopy were employed to assess the structure and composition of the films elaborated at -1V, -1.1V, and -1.2V vs Saturated Calomel Electrode (SCE). The morphological and optical properties were studied using Scanning Electron microscopy and photoluminescence spectroscopy (PL), respectively. The structural properties are improved by annealing treatment, while -1.1V vs SCE was found to be the optimum applied potential to prepare the Kesterite CZTS thin film with a bandgap around 1.5 eV. (C) 2020 Elsevier B.V. All rights reserved.

Sn nanoparticles (NPs) are usually obtained by difficult chemical routes in several steps followed by thermal treatments. Here, a simple and clean method, to obtain Sn NPs directly on the substrate, is developed based on a vapor transport technique. The method is versatile, thus can be easily adjusted to obtain Sn NPs of different size, areal density and morphology, by controlling the deposition conditions. NPs are grown on Si/SiO2 substrate and characterized. Water contact angle measurements show that Sn nanoparticles increase the surface hydrophobicity by 20%. Thus, NPs cleanly obtained from a low-cost, earth-abundant, and environmentally friendly material, can be used to modulate the wettability of surfaces. (C) 2020 Elsevier B.V. All rights reserved.

The influence of Ag and Au nanoparticles and reduced graphene oxide (RGO) sheets on the photodegradation of alpha-lipoic acid (ALA) was determined by UV-VIS spectroscopy. The ALA photodegradation was explained by considering the affinity of thiol groups for the metallic nanoparticles synthesized in the presence of trisodium citrate. The presence of excipients did not induce further changes when ALA interacts with Ag and Au nanoparticles with sizes of 5 and 10 nm by exposure to UV light. Compared to the Raman spectrum of ALA powder, changes in Raman lines' position and relative intensities when ALA has interacted with films obtained from Au nanoparticles with sizes between 5 and 50 nm were significant. These changes were explained by considering the chemical mechanism of surface-enhanced Raman scattering (SERS) spectroscopy. The photodegradation of ALA that had interacted with metallic nanoparticles was inhibited in the presence of RGO sheets.

Almost six decades ago, in Romania a small group of physicists begun to study chalcogenide compositions, motivated primarily by the desire to understand the phase-change phenomenon in these materials, discovered recently, at that time, by Stanford R. Ovshinsky. It took not too long for them to realize the challenges these materials set to the research. With newcomers to the field, the research was broadened. In some cases just for basic research, to model, and to understand the chalcogenide materials, whereas in other cases, the applicative potential was revealed and used. Herein, the evolution of the field of these somewhat exotic materials is followed, listing the main contributions done in Romania, both in basic and applied research.

In this work, the metal and semiconducting nanoparticles (AgNPs, ZnONPs and AgZnONPs) were phyto-synthesized using aqueous vegetal extracts from: Caryophyllus aromaticus L. (cloves) and Citrus reticulata L. (mandarin) peels. The morphological, structural, compositional, optical and biological properties (antibacterial activity, and cytotoxicity) of the prepared composites were investigated. The most effective sample proved to be AgZnONPs, derived from cloves, with a minimum inhibitory concentration (MIC) value of 0.11 mg/mL and a minimum bactericidal concentration (MBC) value of 2.68 mg/mL. All the other three composites inhibited bacterial growth at a concentration between 0.25 mg/mL and 0.37 mg/mL, with a bactericidal concentration between 3 mg/mL and 4 mg/mL. The obtained composites presented biocidal activity against Staphylococcus aureus, and biocompatibility (on human fibroblast BJ cells) and did not damage the human red blood cells. Additionally, an important result is that the presence of silver in composite materials improved the bactericidal action of these nanomaterials against the most common nosocomial pathogen, Staphylococcus aureus.

Silica-based bioactive glasses (SBG) hold great promise as bio-functional coatings of metallic endo-osseous implants, due to their osteoproductive potential, and, in the case of designed formulations, suitable mechanical properties and antibacterial efficacy. In the framework of this study, the FastOs(R)BG alkali-free SBG system (mol%: SiO2-38.49, CaO-36.07, P2O5-5.61, MgO-19.24, CaF2-0.59), with CuO (2 mol%) and Ga2O3 (3 mol%) antimicrobial agents, partially substituting in the parent system CaO and MgO, respectively, was used as source material for the fabrication of intentionally silica-enriched implant-type thin coatings (similar to 600 nm) onto titanium (Ti) substrates by radio-frequency magnetron sputtering. The physico-chemical and mechanical characteristics, as well as the in vitro preliminary cytocompatibility and antibacterial performance of an alkali-free silica-rich bio-active glass coating designs was further explored. The films were smooth (R-RMS < 1 nm) and hydrophilic (water contact angle of similar to 65 degrees). The SBG coatings deposited from alkali-free copper-gallium co-doped FastOs(R)BG-derived exhibited improved wear performance, with the coatings eliciting a bonding strength value of similar to 53 MPa, Lc3 critical load value of similar to 4.9 N, hardness of similar to 6.1 GPa and an elastic modulus of similar to 127 GPa. The Cu and Ga co-doped SBG layers had excellent cytocompatibility, while reducing after 24 h the Staphylococcus aureus bacterial development with 4 orders of magnitude with respect to the control situations (i.e., nutritive broth and Ti substrate). Thereby, such SBG constructs could pave the road towards high-performance bio-functional coatings with excellent mechanical properties and enhanced biological features (e.g., by coupling cytocompatibility with antimicrobial properties), which are in great demand nowadays.

Organic bulk heterojunctions (BHJ) based on zinc phthalocyanine (ZnPc), fullerene compounds (C60 fullerene and [6,6]-phenyl C71 butyric acid methyl ester (PC70BM)), and 5,6,11,12-tetraphenylnaphthacene (rubrene) were fabricated through the matrix-assisted pulsed-laser evaporation (MAPLE) technique. Thus, ZnPc:C60 and ZnPc:PC70BM binary BHJ and ZnPc:rubrene:PC70BM ternary BHJ were deposited as thin films on various substrates. The preservation of the chemical structure of the organic compounds during the MAPLE deposition was confirmed by infrared spectroscopy. The structural, optical, and morphological properties of the deposited layers were investigated by X-ray diffraction (XRD), UV-Vis spectroscopy, photoluminescence (PL), field emission scanning electron microscopy (FESEM), and atomic force microscopy (AFM), respectively. Further, the electrical properties of the developed structures based on ZnPc:C60, ZnPc:PC70BM, and ZnPc:rubrene:PC70BM were evaluated. The J-V characteristics of the organic structures, recorded under illumination, show that an increase in the open-circuit voltage (V-OC) is achieved in the case of the ternary blend in comparison with that obtained for the binary blends. The results evidenced that MAPLE-deposited thin films containing binary and ternary organic bulk heterojunctions can find applications in the field of photovoltaic devices.

Cu2ZnSnS4 (CZTS) is an economically and environmentally friendly alternative to other toxic and expensive materials used for photovoltaics, however, the variation in the composition during synthesis is often followed by the occurrence of the secondary binary and ternary crystalline phases. These phases produce changes in the optical absorption edge important in cell efficiency. We explore here the secondary phases that emerge in a combinatorial Cu2S-ZnS-SnS2 thin films library. Thin films with a composition gradient were prepared by simultaneous magnetron sputtering from three binary chalcogenide targets (Cu2S, SnS2 and ZnS). Then, the samples were crystallized by sulfurization annealing at 450 degrees C under argon flow. Their composition was measured by energy dispersive X-ray spectroscopy (EDX), whereas the structural and optical properties were investigated by grazing incidence X-ray diffraction (GIXRD), Raman spectroscopy and optical transmission measurements. As already known, we found that annealing in a sulfur environment is beneficial, increasing the crystallinity of the samples. Raman spectroscopy revealed the presence of CZTS in all the samples from the library. Secondary crystalline phases such as SnS2, ZnS and Cu-S are also formed in the samples depending on their proximity to the binary chalcogenide targets. The formation of ZnS or Cu-S strongly correlates with the Zn/Sn and Cu/Zn ratio of the total sample composition. The presence of these phases produces a variation in the bandgap between 1.41 eV and 1.68 eV. This study reveals that as we go further away from CZTS in the composition space, in the quasi-ternary Cu2S-ZnS-SnS2 diagram, secondary crystalline phases arise and increase in number, whereas the bandgap takes values outside the optimum range for photovoltaic applications.

In this work, new evidence for the photodegradation reactions of acetaminophen (AC) is reported by photoluminescence (PL), Raman scattering and FTIR spectroscopy. Under excitation wavelength of 320 nm, AC shows a PL band in the spectral range of 340-550 nm, whose intensity decreases by exposure to UV light. The chemical interaction of AC with the NaOH solutions, having the concentration ranging between 0.001 and 0.3 M, induces a gradual enhancement of the photoluminescence excitation (PLE) and PL spectra, when the exposure time of samples at the UV light increases until 140 min, as a result of the formation of p-aminophenol and sodium acetate. This behavior is not influenced by the excipients or other active compounds in pharmaceutical products as demonstrated by PLE and PL studies. Experimental arguments for the obtaining of p-aminophenol and sodium acetate, when AC has interacted with NaOH, are shown by Raman scattering and FTIR spectroscopy.