This study addresses the deposition with improved adhesion of TiO2:N/SiO(2)mixture, with different concentrations of the nano-powders (NPs) (1:0,5; 1:1 and 1:1,5) on 100% cotton fabrics. The characteristics of the deposited thin films were investigated by scanning electron microscopy (SEM), Rutherford backscattering spectrometry (RBS), Raman scattering, FTIR, and UV-VIS absorption spectroscopy. To improve the treatment durability to the external factors, the different crosslinking methods were used. Photocatalytic activity of functionalized textile fabrics was evaluated by determining the photodegradation efficiency of the methylene blue (MB) dye and forest juice, measuring the color difference of the irradiated samples compared with non-irradiated samples. Washing durability of the samples was achieved qualitatively by determining the photocatalytic activity remaining on the textile fabrics after 1 and 5 washing cycles. The samples treated with the mixture of TiO2:N/SiO(2)have demonstrated improved self-cleaning properties, the highest photocatalytic activity being obtained for the highest value of TiO2:N/SiO(2)NPs molar concentrations equal to 1:1.

To enhance the spectral response of solar cells, an experimental study on LaPO4:0.01Ce(3+)/xNd(3+) (x = 0, 2, 4 mol%) was carried out, where structural and morphological properties of the prepared samples were well characterized by the means of X-ray diffraction, Fourier transform infrared spectroscopy, and scanning electronic microscope. Additionally, the photoluminescence behavior of phosphors in ultraviolet-visible (UV-VIS) and Near-infrared (NIR) regions were investigated to confirm the energy transfer (ET) from Ce3+ to Nd3+. Moreover, the quantum efficiency of Ce3+/Nd3+-co-doped samples was estimated as high as similar to 172% and the possible ET process was described. Accordingly, the LaPO4:Ce3+/Nd3+ phosphors can convert the UV light (275 nm) into NIR photons (approx. 1059 nm) through the possible two-pathway energy transfer processes from Ce3+ sensitizer ions to Nd3+ activators. Obtained NIR down-conversion emissions are suitable for improving the conversion efficiency of c-Si solar cells.