National Institute Of Materials Physics - Romania

In this work, polyvinylidene fluoride (PVDF) fibres loaded with mineral powders, such as titanium dioxide (TiO2), barium titanate (BaTiO3), and calcium magnesium silicate (CaxMgSi2Oy), were prepared by electrospinning polymeric suspensions containing 20 wt.% PVDF and 3 wt.% powder. The piezoelectric polymer was combined with powders having antibacterial, piezoelectric, or bioactive properties, respectively, in the desire to obtain multifunctional materials compatible with the requirements of the medical field. All powders were characterized in terms of morphology and crystalline structure, which confirmed the nanometric character of TiO2 samples and micrometric one for the other two, as well as the lower crystallite size for TiO2 specimens as against BaTiO3 and CaxMgSi2Oy. The final fibrous scaffolds were homogeneous, composed of individual fibres with a diameter below 1 mu m and decorated with aggregates of inorganic particles, placed either inside the fibres or attached to their surface. The biological evaluation demonstrated the superiority of the composites towards the plain polymer in terms of cell viability.

In the present work, stannite Cu2CoSnS4 (CCTS) films were elaborated using spray pyrolysis method on soda-lime glass, at different deposition temperatures (T-d = 250, 300, and 350 degrees C), followed by different chosen sulfurization temperatures (T-s = 450, 500, and 550 degrees C). X-ray diffraction (XRD) revealed the nearly single-phase formation of CCTS films at 300 degrees C deposition temperature. After sulfurization in argon flow, the XRD lines become narrower, the average crystallite size expanding above 70 nm. The Raman spectroscopy analysis confirmed the stannite structure formation, as well as the presence CoS2 secondary phases, which reduces at higher sulfurization temperature (550 degrees C). The energy dispersive spectroscopy results indicated atomic ratios of Cu/Co/Sn/S close to the ideal stoichiometric ratio 2:1:1:4. The room temperature photoluminescence emission is recorded with maximum in the 1.35-1.40 eV range. Thermoelectric properties are measured up to 130 degrees C, the films show poor power factor as a result of small positive Seebeck coefficients 10-45 Of K -1 and low electrical conductivity despite of having relatively high carrier concentration (similar to 10(20) cm(-3)).

Understanding the phonon anharmonicity and temperature-dependent behavior of phonons that affect the thermal transport properties in 2D materials is crucial for developing efficient thermoelectric and memristor devices. SnSe has attracted significant interest because of its potential applications for developing such novel devices. Here, orthorhombic SnSe nanoflakes with a thickness of less than 100 nm and oriented along the [100] crystal axis were obtained using physical vapor transport at atmospheric pressure. Polarization-resolved Raman spectroscopy of SnSe nanoflakes was performed at a temperature of 5 K. Temperature-dependent frequencies and linewidths of Raman modes in tin selenide were fitted according to the anharmonic phonon coupling theory. The results indicate that both two and three order processes are responsible for the phonon decay in tin selenide. The memristive property was confirmed by electrical measurements of SnSe devices. SnSe memristors have an operating current of 10-4 A, similar to other transition-metal dichalcogenide memristors, but are more energy efficient than memristors based on defect migration, with a threshold voltage of 3 V.

Designing complex electrochemical artificial muscles aims towards novel devices which besides excellent actuation capabilities should also present the ability to self-sense the modification of environmental parameters. In order to improve efficiency, mimicking the structure of natural muscles, synthetic actuators should have a similar fibrillary morphology. The importance of using materials based on fiber building blocks in actuators aimed at soft robotics field was demonstrated in the present report by comparing a fibrillary artificial muscle with one based on a classical film structure. Nylon electrospun fiber meshes and films were covered in the same conditions with a thin polypyrrole (PPy) layer. The fibrillary electrospun web morphology mimics that of natural muscles and the structure performs a fast, ample bending movement in liquid electrolyte when switching an applied electric potential between -0.6 and +0.6 V. Using the same actuation conditions, no movement of a film based artificial muscle was observed. In order to check the sensing ability of both fibrillary and film like electroactive architectures, their response i.e. PPy reaction when potential cycles were applied in different concentrations of LiClO4 electrolyte were recorded. The obtained results suggest that the ion exchange of the fibrillary artificial muscle is more efficient due to its higher active surface and such devices could work also as dual device (sensor/artificial muscle).

Embedding electronic and optoelectronic devices in common, daily use objects is a fast developing field of research. New architectures are needed for migrating from the classic wafer- based substrates. Novel types of flexible PMMA/Au/Alq(3)/LiF/Al structures were obtained starting from electrospun polymer fibers. Thus, using an electrospinning process poly (methyl metacrylate) (PMMA) nanofibers were fabricated. A thin Au layer deposition rendered the fiber array conductive, this being further employed as the anode. The next steps consisted of the thermal evaporation of tris(8-hydroxyquinolinato) aluminum (Alq(3)) and aluminum deposition as the cathode. The Au covered PMMA nanofiber layer had a similar behavior with an indium tin oxide film i.e. low sheet resistance 10.6 omega/sq and high transparency. The low electrode resistivities allow an electron drift mobility of about 10(-6) cm(2) V-1 s(-1) at a low applied field, similar to the counterpart structures based on thin films. Concerning the relaxation processes in these structures, the Cole-Cole plots exhibit a slightly deformed semicircle, indicating a more complex equivalent circuit for the processes between metal electrodes and the active layer. This equivalent circuit includes reactance equivalent processes at the anode, cathode, in the active layer and most probably originates from the roughness of the metallic electrodes.

Shikonin, a natural compound with pharmaceutical properties, has attracted interest due to its anti-oxidant properties, potential anti-cancer activity and activity over several biological pathways, such as dsDNA transcription/replication of cancer cells and inhibition of pyruvate kinase M2. The electrochemical behavior of shikonin in aqueous media was investigated at glassy carbon electrodes by cyclic and differential pulse voltammetry. The reduction involves the quinone moiety and formation of a semiquinone intermediate. In the absence of dissolved oxygen, the reduction is reversible while in normal atmosphere leads to formation of superoxide cation. The oxidation occurs at the dihydroxy moiety and reversibility was only observed in acid electrolytes. A redox mechanism was proposed. The interaction between shikonin and dsDNA was evaluated in incubated solutions and in situ with the dsDNA-electrochemical biosensor. The mechanism of interaction is time-dependent and follows an initial binding step at the grooves of the double strand leading to conformational modifications recognized through the variation of guanine and adenine oxidation peaks. The in-situ electrochemical production of the semiquinone intermediate leads to a preferential interaction with guanine residues, promoting their oxidation and consequently occurrence 8-oxo-guanine. An interaction mechanism was proposed.

A non-conventional, bioinspired device based on polypyrrole coated electrospun fibrous microstructures, which simultaneously works as artificial muscle and mechanical sensor is reported. Fibrous morphology is preferred due to its high active surface which can improve the actuation/sensing properties, its preparation still being challenging. Thus, a simple fabrication algorithm based on electrospinning, sputtering deposition and electrochemical polymerization produced electroactive aligned ribbon meshes with analogous characteristics as natural muscle fibers. These can simultaneously generate a movement (by applying an electric current/potential) and sense the effort of holding weights (by measuring the potential/current while holding objects up to 21.1 mg). Electroactivity was consisting in a fast bending/curling motion, depending on the fiber strip width. The amplitude of the movement decreases by increasing the load, a behavior similar with natural muscles. Moreover, when different weights were hung on the device, it senses the load modification, demonstrating a sensitivity of about 7 mV/mg for oxidation and - 4 mV/mg for reduction. These results are important since simultaneous actuation and sensitivity are essential for complex activity. Such devices with multiple functionalities can open new possibilities of applications as e.g. smart prosthesis or lifelike robots.

IV-VI semiconductor quantum dots embedded into an inorganic matrix represent nanostructured composite materials with potential application in temperature sensor systems. This study explores the optical, structural, and morphological properties of a novel PbS quantum dots (QDs)-doped inorganic thin film belonging to the Al2O3-SiO2-P2O5 system. The film was synthesized by the sol-gel method, spin coating technique, starting from a precursor solution deposited on a glass substrate in a multilayer process, followed by drying of each deposited layer. Crystalline PbS QDs embedded in the inorganic vitreous host matrix formed a nanocomposite material. Specific investigations such as X-ray diffraction (XRD), optical absorbance in the ultraviolet (UV)-visible (Vis)-near infrared (NIR) domain, NIR luminescence, Raman spectroscopy, scanning electron microscopy-energy dispersive X-ray (SEM-EDX), and atomic force microscopy (AFM) were used to obtain a comprehensive characterization of the deposited film. The dimensions of the PbS nanocrystallite phase were corroborated by XRD, SEM-EDX, and AFM results. The luminescence band from 1400 nm follows the luminescence peak of the precursor solution and that of the dopant solution. The emission of the PbS-doped film in the NIR domain is a premise for potential application in temperature sensing systems.

(1) Background: The treatment of dental cavities and restoration of tooth shape requires specialized materials with specific clinical properties, including being easy to model, light-cured, having a natural color, reduced shrinkage, a hardness similar to hydroxyapatite, and no leakage. The dimensional stability of resin composite materials is affected by polymerization shrinkage, degree of conversion (number of pi carbon bonds converted into sigma ones), thermal contraction and expansion, and interactions with an aqueous environment. (2) Methods: The materials used in our investigation were two composite resins with similar polymer matrices, but different filler (micro/nano filler). To evaluate the properties of samples, we employed the pycnometer technique (pycnometer from Paul Marienfeld Gmbh, Lauda-Konigshofen, Germany), RAMAN spectroscopy technique (MiniRam Equipment from B&W Tek Inc., Plainsboro Township, NJ, USA; 785 nm laser source), SEM and EDX (FEI Inspect S.). (3) Results: The size of the filler plays an important role in the polymerization: for the pycnometric results, the larger particle filler (Sample 1) seems to undergo a rapid polymerization during the 45 s curing, while the nanoparticle filer (Sample 2) needs additional curing time to fully polymerize. This is related to a much larger porosity, as proved by SEM images. The lower degree of conversion, as obtained by Raman spectroscopy, in the same geometry means that the same volume is probed for both samples, but Sample 1 is more porous, which means less amount of polymer is probed for Sample 1. (4) Conclusions: For the two composites, we obtained a degree of conversion of 59% for Sample 1 and 93% for Sample 2, after 45 s of curing.

This is the first report regarding the effect of gamma irradiation on chitosan-coated magnesium-doped hydroxyapatite (x(Mg) = 0.1; 10 MgHApCh) layers prepared by the spin-coating process. The stability of the resulting 10 MgHApCh gel suspension used to obtain the layers has been shown by ultrasound measurements. The presence of magnesium and the effect of the irradiation process on the studied samples were shown by X-ray photoelectron spectroscopy (XPS). The XPS results obtained for irradiated 10 MgHApCh layers suggested that the magnesium and calcium contained in the surface layer are from tricalcium phosphate (TCP; Ca-3(PO4)(2)) and hydroxyapatite (HAp). The XPS analysis has also highlighted that the amount of TCP in the surface layer increased with the irradiation dose. The energy-dispersive X-ray spectroscopy (EDX) evaluation showed that the calcium decreases with the increase in the irradiation dose. In addition, a decrease in crystallinity and crystallite size was highlighted after irradiation. By atomic force microscopy (AFM) we have obtained images suggesting a good homogeneity of the surface of the non-irradiated and irradiated layers. The AFM results were also sustained by the scanning electron microscopy (SEM) images obtained for the studied samples. The effect of gamma-ray doses on the Fourier transform infrared spectroscopy (ATR-FTIR) spectra of 10 MgHApCh composite layers was also evaluated. The in vitro antifungal assays proved that 10 MgHApCh composite layers presented a strong antifungal effect, correlated with the irradiation dose and incubation time. The study of the stability of the 10 MgHApCh gel allowed us to achieve uniform and homogeneous layers that could be used in different biomedical applications.