National Institute Of Materials Physics - Romania

Epitaxial La0.7Sr0.3MnO3 films with different thicknesses (9-90 nm) were deposited on SrTiO3 (0 0 1) substrates by pulsed laser deposition. The films have been investigated with respect to morpho-structural, magnetic, and magneto-transport properties, which have been proven to be thickness dependent. Magnetic contributions with different switching mechanisms were evidenced, depending on the perovskite film thickness. The Curie temperature increases with the film thickness. In addition, colossal magnetoresistance effects of up to 29% above room temperature were evidenced and discussed in respect to the magnetic behavior and film thickness.

The chemical precipitation was used to obtain carbon fibers (CF) with surface modified by magnetite particles (Fe3O4). Processing was carried out by employing up to three subsequent coating stages of ultrasonic treatments. After each sonication stage, the coating was 17, 33, and 47 wt. % of the total weight of the modified fibers. Raman spectroscopy indicates the presence in the coating of a mixture of iron II and III states. As-decorated fibers were used to fabricate composites with an epoxy resin (ED-20) matrix cured with PEPA. The quantity of the carbon fiber filler was of 1, 3, and 6 wt %. At room temperature, the saturation magnetization of the soft magnetic samples was 0.37, 0.83, and 1.72 emu/g for the indicated compositions. Carbon fiber reinforced polymer materials with extra functions such as magnetic in this case, are expected to be useful in applications from the power and energy industries.

Alloys possessing nominal compositions Mn53Al45C2 and Mn52Al46C2 were prepared by the melt spinning method and were subjected to complex structural, morphological and magnetic investigations. As these alloys can exhibit tetragonal L1(0)-type and tau phase, they have good potential as rare earth (RE)-free magnets. It is, therefore, important to monitor the epsilon-tau phase transformation and the stability and the magnetic features of the tetragonal phase in an entire temperature interval. By using synchrotron X-ray diffraction, it has been proven that the epsilon-tau phase transformation occurs gradually, with the tau phase becoming predominant only after 450 & DEG;C. Moreover, this phase has been proven to be quite stable without any grain growth even at the highest temperature investigated at 800 & DEG;C. Low temperature behavior was thoroughly investigated by using a complex combination of major and minor hysteresis loops combined with the zero field cooled-field cooled magnetization protocols (ZFC-FC). Two different regimes, blocking and superparamagnetic, were documented. A spin reorientation transition was proven to occur at 55 K while a maximum magnetization observed in ZFC-FC curves proved that at about 75 K, a transition from ferro to superparamagnetic state occurs. The existence of a blocking regime below 55 K that is characteristic to nanogranular systems with superparamagnetic behavior has shown further development towards obtaining RE-free magnets.

In order to prove the usefulness of having a structurally disordered precursor to the formation of FePt L1(0) phase and to facilitate the co-existence of exchange coupled hard and soft magnetic phases with optimized magnetic properties in various conditions of annealing, a Fe-Pt-Zr-B melt spun alloy has been synthesized and detailed structural and magnetic investigations have been undertaken to probe its phase evolution during annealing. The dynamics of formation of the hard magnetic L1(0) phase during the gradual disorder-order phase transformation has been monitored by using a complex combination of X-ray diffraction methods and Fe-57 Mossbauer spectroscopy methods, over a wide range of annealing temperatures. Multiple phases co-existing in the annealed sample microstructures, observed in XRD, have been reconfirmed by the Mossbauer spectra analysis and, moreover, accurate quantitative data have been acquired in what concerns the relative abundance of each of the observed crystalline phases in every stage of annealing. It is shown that the formation of the hard magnetic phase, emerging from the chemically disordered precursor, is gradual and occurs via complex mechanisms, involving the presence of a disordered Fe-Zr-B-rich intergranular region which contributes to an increase in the abundance of the L1(0) phase for higher annealing temperatures. Magnetic measurements have confirmed the good performances of these alloys in terms of coercivity and remanence. These results contribute to the development of these alloys as the next generation of rare earth, free permanent magnets.

Almost all proposed configurations and practical achievements based on superconductor/ferromagnet (S/F) heterostrucutres focus on s-wave superconductors. However, several attempts targeted also high temperature superconductors, most of them using manganite ferromagnets LaXMnO3 (X: Ca or Sr) and Y1Ba2Cu3O7-x (YBCO). Here we propose a new ferromagnetic material that can be used with YBCO for the fabrication of S/F hybrid structures. We show that a ferromagnetic order can be induced in a thin layer (similar to 130 nm thickness) of CaRuO3 grown by pulsed laser deposition on epitaxial YBCO film. Detailed magnetic and structural investigations show that the observations of the weak ferromagnetism are consistent with the magnetic order induced by in-plane tensile strain of about 1.7% and the easy-magnetization axis forms an angle of similar to 180o with the layer plane. The value of the Curie temperature T (Curie) estimated using the Curie-Weiss law was 340 K. An unusual temperature dependence of the magnetic moment around the superconducting transition was observed in both field-cooled and zero-field-cooled configurations which is attributed to the paramagnetic Meissner effect.

The discovery of multifunctional properties related to electro-activity of organic systems of biomolecules is important for a variety of applications, especially for devices in the realm of biocompatible sensors and/or bioactuators. A further step towards such applications is to prepare thin films with the required properties. Here, the investigation is focused on the characterization of films of guanine and cytosine nucleobases, prepared by thermal evaporation-an industrial accessible deposition technique. The cytosine films have an orthorhombic non-centrosymmetric structure and grow in two interconnected nanostructured fractal patterns, of nearly equal proportion. Piezoresponse force microscopy images acquired at room temperature on the cytosine films display large zones with antiparallel alignment of the vertical components of the polarization vector. Guanine films have a dense nano-grained morphology. Our studies reveal electrical polarization switching effects which can be related to ferroelectricity in the films of guanine molecules. Characteristic ferroelectric polarization-electric-field hysteresis loops showing large electrical polarization are observed at low temperatures up to 200 K. Above this temperature, the guanine films have a preponderant paraelectric phase containing residual or locally induced nano-scopic ferroelectric domains, as observed by piezoresponse force microscopy at room temperature.

Pristine high-density bulk disks of MgB2 with added hexagonal BN (10 wt.%) were prepared using spark plasma sintering. The BN-added samples are machinable by chipping them into desired geometries. Complex shapes of different sizes can also be obtained by the 3D printing of polylactic acid filaments embedded with MgB2 powder particles (10 wt.%). Our present work aims to assess antimicrobial activity quantified as viable cells (CFU/mL) vs. time of sintered and 3D-printed materials. In vitro antimicrobial tests were performed against the bacterial strains Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, Staphylococcus aureus ATCC 25923, Enterococcus faecium DSM 13590, and Enterococcus faecalis ATCC 29212; and the yeast strain Candida parapsilosis ATCC 22019. The antimicrobial effects were found to depend on the tested samples and microbes, with E. faecium being the most resistant and E. coli the most susceptible.

The effects of severe plastic deformation (SPD) process via high-speed high-pressure torsion technique on martensitic transformation of Ni-Fe-Ga Heusler shape memory alloy are the subject of this work. The results show that moderate degrees of deformation lead to a decrease in the martensitic transformation temperatures, while the heat of reaction is enhanced only for the sample processed with the lowest degree of deformation. The results are explained by the interplay between the constituent tetragonal L10 and the cubic gamma crystal structures and the evolution of the samples morphology with the severity of deformation. The reduction in the samples granulation due to the progressive increase in the SPD is reflected by the magnetic properties of the samples with decreasing coercivity and Curie temperatures. At the highest applied degree of deformation, sample nanostructuring and a possible amorphization might explain the vanishing of MT.

Glasses from lithium-aluminum-zinc-boron-phosphorous oxide system co-doped with terbium (Tb3+) and dysprosium (Dy3+) oxides were studied for magneto-optical applications in lasers. The Fourier Transform Infrared and Raman Spectroscopy complementary analysis suggested the depolymerization of the borophosphate glass network by adding and increasing the rare-earth (RE) oxide content. Main UV-vis absorption maxima of Tb and Dy ions were identified at 348 and 1266 nm. Spectroscopic ellipsometry indicated a maximum refractive index of 1.56, at 400 nm, for the highest RE content. The Verdet constant amplified by increasing the RE content, reaching for the 9 mol% RE co-doped sample a value of -0.075 min/Oe/cm at 630 nm. The Faraday rotation angle was additionally confirmed by using a Faraday Cell Device, being also related to the specific paramagnetic behavior evidenced by Superconducting Quantum Interference Device magnetometry. The magneto-optical properties recommend such vitreous co-doped materials for magneto-optical devices.

The influence of the rapid solidification technique and heat treatment on the martensitic transformation, magnetic properties, thermo- and magnetic induced strain and electrical resistivity is investigated for the Cu doped NiMnGa Heusler-based ferromagnetic shape memory ribbons. The martensitic transformation temperatures are unexpectedly low (below 90 K-which can be attributed to the disordered texture as well as to the uncertainty in the elements substituted by the Cu), preceded by a premartensitic transformation (starting at around 190 K). A thermal treatment slightly increases the transformation as well as the Curie temperatures. Additionally, the thermal treatment promotes a higher magnetization value of the austenite phase and a lower one in the martensite. The shift of the martensitic transformation temperatures induced by the applied magnetic field, quantified from thermo-magnetic and thermo-magnetic induced strain measurements, is measured to have a positive value of about 1 K/T, and is then used to calculate the transformation entropy of the ribbons. The magnetostriction measurements suggest a rotational mechanism in low fields for the thermal treated samples and a saturation tendency at higher magnetic fields, except for the temperatures close to the phase transition temperatures (saturation is not reached at 5 T), where a linear volume magnetostriction cannot be ruled out. Resistivity and magnetoresistance properties have also been measured for all the samples.