National Institute Of Materials Physics - Romania

Composites of BaTiO3 (BT) and doped-PZT (d-PZT) micro-particles randomly dispersed in a PDMS matrix were prepared by a molding process. The morpho-structural characterization, performed by SEM and XRD, showed ceramic micro-grains of cubic BT and orthorhombic d-PZT, randomly dispersed in the PDMS matrix. Polarization (P) as a function of the applied field (E) was measured for composite samples, as well as for polymer samples. Hysteresis loops typical for a dielectric material were obtained, but also atypical ones, especially for higher fraction of polymer in composite, lower fields and shorter measuring periods, as a result of the dielectric relaxation in polymer and the presence of interfacial polarization charges at the contact between polymer and ferroelectric. All these composites show very low polarizations (less than 0.2 mu C/cm(2) and 0.05 mu C/cm(2) the maximum and remnant polarization, respectively), caused by the very low dielectric constant of the polymer (less than 10), which drastically reduces, up to 100 times, the electric field effectively applied to the ferroelectric. Weak pyroelectric response was recorded on BT/PDMS, but a typical behavior of a pyroelectric detector was observed. A figure of merit of the material which exceeds 10(-4) m(2) /C was estimated.

Graded structures with different architectures were obtained by spark plasma sintering from (Ba1-xSrx)TiO3 (BST, x = 0.10; 0.20; 0.30) powders. The presence of the composition gradient was confirmed by structural and compositional investigations using X-ray diffraction and electron microscopy combined with energy dispersive X-ray spectroscopy. The concentration gradient was either asymmetric (3 layers, starting with x = 0.10 and ending with x = 0.30) or symmetric (5 or 6 layers, starting and ending with x = 0.10, and with a single or double x = 0.30 layer in the middle, respectively). Electrical measurements reveal a decrease of the dielectric constant with increasing the number of the layers. It was found that the symmetric graded structure with 6 layers has the best thermal stability of both, the dielectric constant (variation of only 8% between zero and 100 degrees C) and the py-roelectric coefficient (6% variation between zero and 80 degrees C). In addition, an enhancement of the pyroelectric signal for frequencies above 100 Hz is obtained in symmetric structures, an effect that is attributed to the additive contributions of the signals originated from the layers with different Sr content. (C) 2021 The Author(s). Published by Elsevier B.V.

We fabricated Sn-doped TiO2 nanotubular film via annealing of anodized TiO2 nanotubes grown on F-SnO2 (FTO) glass. Annealing was carried out at 500 degrees C in ambient air. Anatase crystal structure was achieved with no change in nanotubular morphology in respect to as-anodized amorphous TiO(2 )nanotubes. The X-ray photoelectron spectroscopy analysis revealed Sn on the surface of TiO2 film, following the thermal treatment, probably caused by the diffusion from FTO glass. Depth profile examination of the film chemical composition was conducted by elastic recoil detection analysis, which showed that in addition to the diffusion of Sn from FTO, diffusion of Ti to FTO concurrently occurred. Thus, a higher concentration of Sn was found at the bottom of the tubes, while a lower concentration was present on the tubes' surface top. This explains the improved optical response revealed by a diffuse reflectance spectroscopy. The absorption enhancement demonstrated that Sn-doped TiO2 film was efficient in the degradation of methyl orange dye under visible light.

We report on new biomaterials with promising bone and cartilage regeneration potential, from sustainable, cheap resources of fish origin. Thin films were fabricated from fish bone-derived bi-phasic calcium phosphate targets via pulsed laser deposition with a KrF * excimer laser source (lambda = 248 nm, tau(FWHM) <= 25 ns). Targets and deposited nanostructures were characterized by SEM and XRD, as well as by Energy Dispersive X-ray (EDX) and FTIR spectroscopy. Films were next assessed in vitro by dedicated cytocompatibility and antimicrobial assays. Films were Ca-deficient and contained a significant fraction of beta-tricalcium phosphate apart from hydroxyapatite, which could contribute to an increased solubility and an improved biocompatibility for bone regeneration applications. The deposited structures were biocompatible as confirmed by the lack of cytotoxicity on human gingival fibroblast cells, making them promising for fast osseointegration implants. Pulsed laser deposition (PLD) coatings inhibited the microbial adhesion and/or the subsequent biofilm development. A persistent protection against bacterial colonization (Escherichia coli) was demonstrated for at least 72 h, probably due to the release of the native trace elements (i.e., Na, Mg, Si, and/or S) from fish bones. Progress is therefore expected in the realm of multifunctional thin film biomaterials, combining antimicrobial, anti-inflammatory, and regenerative properties for advanced implant coatings and nosocomial infections prevention applications.

This work presents a new synthesis and characterization of Kesterite Cu2ZnSnS4 films by one step electrodeposition with free sulfurization annealing treatment at different applied potentials. This study highlights the effect of applied potential and annealing treatment on the properties of CZTS deposited films. X-ray Diffraction and Raman spectroscopy were employed to assess the structure and composition of the films elaborated at -1V, -1.1V, and -1.2V vs Saturated Calomel Electrode (SCE). The morphological and optical properties were studied using Scanning Electron microscopy and photoluminescence spectroscopy (PL), respectively. The structural properties are improved by annealing treatment, while -1.1V vs SCE was found to be the optimum applied potential to prepare the Kesterite CZTS thin film with a bandgap around 1.5 eV. (C) 2020 Elsevier B.V. All rights reserved.

In this work, the metal and semiconducting nanoparticles (AgNPs, ZnONPs and AgZnONPs) were phyto-synthesized using aqueous vegetal extracts from: Caryophyllus aromaticus L. (cloves) and Citrus reticulata L. (mandarin) peels. The morphological, structural, compositional, optical and biological properties (antibacterial activity, and cytotoxicity) of the prepared composites were investigated. The most effective sample proved to be AgZnONPs, derived from cloves, with a minimum inhibitory concentration (MIC) value of 0.11 mg/mL and a minimum bactericidal concentration (MBC) value of 2.68 mg/mL. All the other three composites inhibited bacterial growth at a concentration between 0.25 mg/mL and 0.37 mg/mL, with a bactericidal concentration between 3 mg/mL and 4 mg/mL. The obtained composites presented biocidal activity against Staphylococcus aureus, and biocompatibility (on human fibroblast BJ cells) and did not damage the human red blood cells. Additionally, an important result is that the presence of silver in composite materials improved the bactericidal action of these nanomaterials against the most common nosocomial pathogen, Staphylococcus aureus.

Silica-based bioactive glasses (SBG) hold great promise as bio-functional coatings of metallic endo-osseous implants, due to their osteoproductive potential, and, in the case of designed formulations, suitable mechanical properties and antibacterial efficacy. In the framework of this study, the FastOs(R)BG alkali-free SBG system (mol%: SiO2-38.49, CaO-36.07, P2O5-5.61, MgO-19.24, CaF2-0.59), with CuO (2 mol%) and Ga2O3 (3 mol%) antimicrobial agents, partially substituting in the parent system CaO and MgO, respectively, was used as source material for the fabrication of intentionally silica-enriched implant-type thin coatings (similar to 600 nm) onto titanium (Ti) substrates by radio-frequency magnetron sputtering. The physico-chemical and mechanical characteristics, as well as the in vitro preliminary cytocompatibility and antibacterial performance of an alkali-free silica-rich bio-active glass coating designs was further explored. The films were smooth (R-RMS < 1 nm) and hydrophilic (water contact angle of similar to 65 degrees). The SBG coatings deposited from alkali-free copper-gallium co-doped FastOs(R)BG-derived exhibited improved wear performance, with the coatings eliciting a bonding strength value of similar to 53 MPa, Lc3 critical load value of similar to 4.9 N, hardness of similar to 6.1 GPa and an elastic modulus of similar to 127 GPa. The Cu and Ga co-doped SBG layers had excellent cytocompatibility, while reducing after 24 h the Staphylococcus aureus bacterial development with 4 orders of magnitude with respect to the control situations (i.e., nutritive broth and Ti substrate). Thereby, such SBG constructs could pave the road towards high-performance bio-functional coatings with excellent mechanical properties and enhanced biological features (e.g., by coupling cytocompatibility with antimicrobial properties), which are in great demand nowadays.

Cu2ZnSnS4 (CZTS) is an economically and environmentally friendly alternative to other toxic and expensive materials used for photovoltaics, however, the variation in the composition during synthesis is often followed by the occurrence of the secondary binary and ternary crystalline phases. These phases produce changes in the optical absorption edge important in cell efficiency. We explore here the secondary phases that emerge in a combinatorial Cu2S-ZnS-SnS2 thin films library. Thin films with a composition gradient were prepared by simultaneous magnetron sputtering from three binary chalcogenide targets (Cu2S, SnS2 and ZnS). Then, the samples were crystallized by sulfurization annealing at 450 degrees C under argon flow. Their composition was measured by energy dispersive X-ray spectroscopy (EDX), whereas the structural and optical properties were investigated by grazing incidence X-ray diffraction (GIXRD), Raman spectroscopy and optical transmission measurements. As already known, we found that annealing in a sulfur environment is beneficial, increasing the crystallinity of the samples. Raman spectroscopy revealed the presence of CZTS in all the samples from the library. Secondary crystalline phases such as SnS2, ZnS and Cu-S are also formed in the samples depending on their proximity to the binary chalcogenide targets. The formation of ZnS or Cu-S strongly correlates with the Zn/Sn and Cu/Zn ratio of the total sample composition. The presence of these phases produces a variation in the bandgap between 1.41 eV and 1.68 eV. This study reveals that as we go further away from CZTS in the composition space, in the quasi-ternary Cu2S-ZnS-SnS2 diagram, secondary crystalline phases arise and increase in number, whereas the bandgap takes values outside the optimum range for photovoltaic applications.