National Institute Of Materials Physics - Romania

Glasses from lithium-aluminum-zinc-boron-phosphorous oxide system co-doped with terbium (Tb3+) and dysprosium (Dy3+) oxides were studied for magneto-optical applications in lasers. The Fourier Transform Infrared and Raman Spectroscopy complementary analysis suggested the depolymerization of the borophosphate glass network by adding and increasing the rare-earth (RE) oxide content. Main UV-vis absorption maxima of Tb and Dy ions were identified at 348 and 1266 nm. Spectroscopic ellipsometry indicated a maximum refractive index of 1.56, at 400 nm, for the highest RE content. The Verdet constant amplified by increasing the RE content, reaching for the 9 mol% RE co-doped sample a value of -0.075 min/Oe/cm at 630 nm. The Faraday rotation angle was additionally confirmed by using a Faraday Cell Device, being also related to the specific paramagnetic behavior evidenced by Superconducting Quantum Interference Device magnetometry. The magneto-optical properties recommend such vitreous co-doped materials for magneto-optical devices.

Cu2ZnSnS4 (CZTS) is a complex quaternary material, and obtaining a single-phase CZTS with no secondary phases is known to be challenging and dependent on the production technique. This work involves the synthesis and characterization of CZTS absorber layers for solar cells. Thin films were deposited on Si and glass substrates by a combined magnetron sputtering (MS) and pulsed laser deposition (PLD) hybrid system, followed by annealing without and with sulfur powder at 500 degrees C under argon (Ar) flow. Three different Cu2S, SnS2, and ZnS targets were used each time, employing a different target for PLD and the two others for MS. The effect of the different target arrangements and the role of annealing and/or sulfurization treatment were investigated. The characterization of the absorber films was performed by grazing incidence X-ray diffraction (GIXRD), X-ray reflectometry (XRR), Raman spectroscopy, scanning electron microscopy, and regular transmission spectroscopy. The film with ZnS deposited by PLD and SnS2 and Cu2S by MS was found to be the best for obtaining a single CZTS phase, with uniform surface morphology, a nearly stoichiometric composition, and an optimal band gap of 1.40 eV. These results show that a new method that combines the advantages of both MS and PLD techniques was successfully used to obtain single-phase Cu2ZnSnS4 films for solar cell applications.

The feasibility of mixed-cation mixed-halogen perovskites of formula A(x)A'1-xPbXyXz'X3-y-z '' is analyzed from the perspective of structural stability, opto-electronic properties and possible degradation mechanisms. Using density functional theory (DFT) calculations aided by machine-learning (ML) methods, the structurally stable compositions are further evaluated for the highest absorption and optimal stability. Here, the role of the halogen mixtures is demonstrated in tuning the contrasting trends of optical absorption and stability. Similarly, binary organic cation mixtures are found to significantly influence the degradation, while they have a lesser, but still visible effect on the opto-electronic properties. The combined framework of high-throughput calculations and ML techniques such as the linear regression methods, random forests and artificial neural networks offers the necessary grounds for an efficient exploration of multi-dimensional compositional spaces.

High-quality ZnS thin films as buffer layer have been successfully synthesized and simulated using the low-cost Mist CVD technique and the SCAPS-1D software for different deposition times (30, 40, 50, and 60 min). The structural, morphological, and optical properties of the prepared ZnS films have been investigated using X-ray diffraction (XRD), scanning electronic microscopy (SEM), atomic force microscopy (AFM), and UV-Vis spectrophotometer. The time deposition effect on ZnS films' efficiency as a buffer layer has been evaluated. XRD pattern confirms the hexagonal/cubic structure of the prepared samples, with (111) as preferred orientation. Raman spectra confirm XRD findings by the two peaks located at 348 cm(-1) and 697 cm(-1) which correspond to ZnS samples' cubic and hexagonal structures. Scanning electronic microscopy (SEM) and atomic force microscopy (AFM) images show densely uniform grains with precise shapes and boundaries covering the entire sample's surface with a relative roughness for all deposition times. The optical transmittance shows an average of 78% in the visual field of light with an optical band gap varying between 3.69 and 3.80 eV. Numerical simulation of ZnO:Al/ZnS/CZTS/Mo cell using SCAPS-1D software shows that the sample deposited for 30 min presents the best performance with an efficiency of up to 8.9%.

ZnS is a wide band gap material which was proposed as a possible candidate to replace CdS as a buffer layer in solar cells. However, the structural and optical properties are influenced by the deposition method. ZnS thin films were prepared using magnetron sputtering (MS), pulsed laser deposition (PLD), and a combined deposition technique that uses the same bulk target for sputtering and PLD at the same time, named MSPLD. The compositional, structural, and optical properties of the as-deposited and annealed films were inferred from Rutherford backscattering spectrometry, X-ray diffraction, X-ray reflectometry, Raman spectroscopy, and spectroscopic ellipsometry. PLD leads to the best stoichiometric transfer from target to substrate, MS makes fully amorphous films, whereas MSPLD facilitates obtaining the densest films. The study reveals that the band gap is only slightly influenced by the deposition method, or by annealing, which is encouraging for photovoltaic applications. However, sulphur vacancies contribute to lowering the bandgap and therefore should be controlled. Moreover, the results add valuable information towards the understanding of ZnS polymorphism. The combined MSPLD method offers several advantages such as an increased deposition rate and the possibility to tune the optical properties of the obtained thin films.

The commercially ubiquitous liquid electrolytes for lithium-ion batteries have several shortcomings in terms of safety. Therefore, development of solid electrolytes, especially those that are glass-based, has been gaining increasing interest in recent times. However, the fundamental understanding of the changes in the glass structure and the corresponding changes in the properties due to the addition of dopants is necessary for the development of glasses. Therefore, here, we report a study on the role of vanadium on the glass structure, ionic conduction, crystallization behavior, and other properties of lithium silicate-based glasses (23Li(2)O-2.64K(2)O-2.64Al(2)O(3)-71.72SiO(2)) as a solid electrolyte for high-temperature Li-ion battery applications. Furthermore, we proposed a mathematical model to describe/quantify the ion-conducting channels' connectivity in glasses. The experimental glass structures were assessed using Si-29, V-51, Al-27 nuclear magnetic resonance, Fourier transform infrared, and ultraviolet-visible spectroscopy techniques. The ionic conductivity was measured by impedance spectroscopy, and the crystallization behavior was studied by optical microscopy and X-ray diffraction. Furthermore, molecular dynamics simulations were also used to gain structural insights of the glasses. In the designed compositions, the addition of vanadium decreased the overall concentration of Li+ ions. However, the results revealed that the ionic conductivity improved with the addition of vanadium in spite of a decrease in the number of charge carriers. This suggests that vanadium makes the pathways easier for the conducting ions. Thus, we conclude that vanadium modifies the conduction channels to promote better hoping of the ions from one site to another.

Hybrid perovskites based solar cells have demonstrated high conversion efficiency but poor long-term stability. This study reports on the results obtained after doping the CH3NH3PbI2.6Cl0.4 mixed halide perovskite with imidazolium (C3N2H5+, denoted IM) on the "A site" position of a perovskite, to improve photovoltaic performances and stability of hybrid perovskite solar cells. The perovskite films were investigated exhaustively by different characterization techniques: X-ray diffraction, Atomic Force Microscopy, Scanning Electron Microscopy, UV-Vis, X-ray Photoelectron Electron Paramagnetic Resonance spectroscopies, Impedance Spectroscopy and Incident Photon-to-Electron Conversion Efficiency. The photovoltaic parameters were determined by measuring the IV curves of the corresponding solar cells. The amount of IM inserted in the perovskite play a key role on the film properties. The calculated new tolerance factors according to the "globularity factor" are experimentally proved and thus at doping concentrations greater than 20% for CH3NH3PbI2.6Cl0.4 perovskite the 3D structure is no longer obtained. However, below this value, the IM substituted perovskite film possesses an improved film quality and crystallinity as compared to the pristine film. Substituting MA+ with IM+ provides a favorable way to reduce recombination processes and shows great potential to achieve high stability, and an improved charge generation, resulting in increased PCE values. We find that the optimal percentage of imidazolium incorporation to achieve better stability of solar cells is 6%.

Polarization switching in ferroelectric films is exploited in many applications, such as non-volatile memories and negative capacitance field affect transistors. This can be inhomogeneous or homogeneous, depending on if ferroelectric domains are forming or not during the switching process. The relation between the polarization switching, the structural quality of the films and the negative capacitance was not studied in depth. Here, Pb(Zr0.2Ti0.8)O-3 (PZT) layers were deposited by pulse laser deposition (PLD) and sol-gel (SG) on single crystal SrTiO3 (STO) and Si substrates, respectively. The structural quality was analyzed by X-ray diffraction and transmission electron microscopy, while the electric properties were investigated by performing hysteresis, dynamic dielectric measurements, and piezo-electric force microscopy analysis. It was found that the PZT layers grown by PLD on SRO/STO substrates are epitaxial while the layers deposited by SG on Pt/Si are polycrystalline. The polarization value decreases as the structure changes from epitaxial to polycrystalline, as well as the magnitude of the leakage current and of the differential negative capacitance, while the switching changes from homogeneous to inhomogeneous. The results are explained by the compensation rate of the depolarization field during the switching process, which is much faster in epitaxial films than in polycrystalline ones.

The frequency and temperature dependence of dielectric properties of CH3NH3PbI3 (MAPI) crystals have been studied and analyzed in connection with temperature-dependent structural studies. The obtained results bring arguments for the existence of ferroelectricity and aim to complete the current knowledge on the thermally activated conduction mechanisms, in dark equilibrium and in the presence of a small external a.c. electric field. The study correlates the frequency-dispersive dielectric spectra with the conduction mechanisms and their relaxation processes, as well as with the different transport regimes indicated by the Nyquist plots. The different energy barriers revealed by the impedance spectroscopy highlight the dominant transport mechanisms in different frequency and temperature ranges, being associated with the bulk of the grains, their boundaries, and/or the electrodes' interfaces.

Cation-substituted hydroxyapatite (HA), standalone or as a composite (blended with polymers or metals), is currently regarded as a noteworthy candidate material for bone repair/regeneration either in the form of powders, porous scaffolds or coatings for endo-osseous dental and orthopaedic implants. As a response to the numerous contradictions reported in literature, this work presents, in one study, the physico-chemical properties and the cytocompatibility response of single cation-doped (Ce, Mg, Sr or Zn) HA nanopowders in a wide concentration range (0.5-5 at.%). The modification of composition, morphology, and structure was multiparametrically monitored via energy dispersive X-ray, X-ray photoelectron, Fourier-transform infrared and micro-Raman spectroscopy methods, as well as by transmission electron microscopy and X-ray diffraction. From a compositional point of view, Ce and Sr were well-incorporated in HA, while slight and pronounced deviations were observed for Mg and Zn, respectively. The change of the lattice parameters, crystallite size, and substituting cation occupation factors either in the Ca(I) or Ca(II) sites were further determined. Sr produced the most important HA structural changes. The in vitro biological performance was evaluated by the (i) determination of leached therapeutic cations (by inductively coupled plasma mass spectrometry) and (ii) assessment of cell behaviour by both conventional assays (e.g., proliferation-3-(4,5-dimethyl thiazol-2-yl) 5-(3-carboxymethoxyphenyl)-2-(4-sulfophenyl)-2H-tetrazolium assay; cytotoxicity-lactate dehydrogenase release assay) and, for the first time, real-time cell analysis (RTCA). Three cell lines were employed: fibroblast, osteoblast, and endothelial. When monophasic, the substituted HA supported the cells' viability and proliferation without signs of toxicity. The RTCA results indicate the excellent adherence of cells. The study strived to offer a perspective on the behaviour of Ce-, Mg-, Sr-, or Zn-substituted HAs and to deliver a well-encompassing viewpoint on their effects. This can be highly important for the future development of such bioceramics, paving the road toward the identification of candidates with highly promising therapeutic effects.