National Institute Of Materials Physics - Romania

Featuring a high hydrogen storage content of up to 20 wt%, complex metal borohydrides remain promising solid state hydrogen storage materials, with the real prospect of reversible behavior for a zero-emission economy. However, the thermodynamic barriers and sluggish kinetics are still barriers to overcome. In this context, nanoconfinement has provided a reliable method to improve the behavior of hydrogen storage materials. The present work describes the thermodynamic and kinetic enhancements of LiBH4 nanoconfined in MFe2O4 (M=Co, Ni) ferrite-catalyzed graphene host. Composites of LiBH4-catalysts were prepared by melt infiltration and investigated by X-ray diffraction, TEM, STEM-EDS and TPD. The role of ferrite additives, metal precursor treatment (Ar, Ar/H-2) and the effect on hydrogen storage parameters are discussed. The thermodynamic parameters for the most promising composite LiBH4-graphene-NiFe2O4 (Ar) were investigated by Kissinger plot method, revealing an E-A = 127 kJ/mol, significantly lower than that of neat LiBH4 (170 kJ/mol). The reversible H-2 content of LiBH4-graphene-NiFe2O4 (Ar) after 5 a/d cycles was similar to 6.14 wt%, in line with DOE's target of 5.5 wt% storage capacity, while exhibiting the lowest desorption temperature peak of 349 degrees C. The composites with catalysts treated in Ar have lower desorption temperature due to better catalyst dispersion than using H-2/Ar.

The p-n junctions are the building blocks of nowadays electronic devices. The n- or p-type conductivity is obtained in classic semiconductors, like Si, by doping with atoms acting as donors or acceptors, respectively. Doping was used in ferroelectrics to influence the transition temperature, magnitude of some physical properties, but not necessarily conduction type. Therefore, comprehensive studies to obtain true ferroelectric p-n junctions by controlled doping are missing. Recently, it has been shown that Pb(Zr0.2Ti0.8)O-3 films doped with & AP;1% atomic Nb (n-type doping) or Fe (p-type doping) have different orientations of polarization in the as-grown state. Knowing that polarization orientation depends on doping type, the next step is to build ferroelectric p-n homojunctions and to study their properties in relation to ferroelectric polarization. p-n and n-p structures were grown for this purpose by successive deposition of Nb-doped and Fe-doped Pb(Zr,Ti)O-3 layers with different thicknesses. We find that these p-n homojunctions are ferroelectric, but the magnitude of the polarization and coercive field, as well as the dominant polarization orientation in the as-grown state, depend on the conduction type of the first grown layer. The I-V characteristics are quasi-linear, although the interfaces with the electrodes behaves as Schottky contacts. The resistance extracted from the I-V characteristics displays an exponential dependence on temperature, with an activation energy in the range of 0.14-0.17 eV. These results are explained assuming that the total current in the junction is the total of electron and hole injections at the electrode interfaces. It is shown that for relatively low doping concentrations, the current density contains a dominant term with a linear voltage dependence and an exponential temperature dependence, as observed experimentally, and a secondary (correction) term that is dependent on the free carrier density and can induce non-linear voltage dependence when this density is significant.

The treatment of wounds occurring accidentally or as a result of chronic diseases most frequently requires the use of appropriate dressings, mainly to ensure tissue regeneration/healing, at the same time as treating or preventing potential bacterial infections or superinfections. Collagen type I-based scaffolds in tandem with adequate antimicrobials can successfully fulfill these requirements. In this work, starting from the corresponding hydrogels, we prepared a series of freeze-dried atelocollagen type I-based matrices loaded with tannic acid (TA) and chlorhexidine digluconate (CHDG) as active agents with a broad spectrum of antimicrobial activity and also as crosslinkers for the collagen network. The primary aim of this study was to design an original and reliable algorithm to in vitro monitor and kinetically analyze the simultaneous release of TA and CHDG from the porous matrices into an aqueous solution of phosphate-buffered saline (PBS, pH 7.4, 37 degrees C) containing micellar carriers of a cationic surfactant (hexadecyltrimethylammonium bromide, HTAB) as a release environment that roughly mimics human extracellular fluids in living tissues. Around this central idea, a comprehensive investigation of the lyophilized matrices (morpho-structural characterization through FT-IR spectroscopy, scanning electron microscopy, swelling behavior, resistance against the collagenolytic action of collagenase type I) was carried out. The kinetic treatment of the release data displayed a preponderance of non-Fickian-Case II diffusion behavior, which led to a general anomalous transport mechanism for both TA and CHDG, irrespective of their concentrations. This is equivalent to saying that the release regime is not governed only by the gradient concentration of the releasing components inside and outside the matrix (like in ideal Fickian diffusion), but also, to a large extent, by the relaxation phenomena of the collagen network (determined, in turn, by its crosslinking degree induced by TA and CHDG) and the dynamic capacity of the HTAB micelles to solubilize the two antimicrobials. By controlling the degree of physical crosslinking of collagen with a proper content of TA and CHDG loaded in the matrix, a tunable, sustainable release profile can be obtained.

Lately, there is a growing interest in organic photovoltaic (OPV) cells due to the organic materials' properties and compatibility with various types of substrates. However, their efficiencies are low relative to the silicon ones; therefore, other ways (i.e., electrode micron/nanostructuring, synthesis of new organic materials, use of additives) to improve their performances are still being sought. In this context, we studied the behavior of the common organic bulk heterojunction (P3HT:PC70BM) deposited by matrix-assisted pulsed laser evaporation (MAPLE) with/without 0.3% of 1,8-diiodooctane (DIO) additive on flat and micro-patterned ITO substrates. The obtained results showed that in the MAPLE process, a small quantity of additive can modify the morphology of the organic films and decrease their roughness. Besides the use of the additive, the micro-patterning of the electrode leads to a greater increase in the absorption of the studied photovoltaic structures. The inferred values of the filling factors for the measured cells in ambient conditions range from 19% for the photovoltaic structures with no additive and without substrate patterning to 27% for the counterpart structures with patterning and a small quantity of additive.

The paper presents a study concerning the role of ferroelectric filler size and clustering in the dielectric properties of 20%BaTiO3-80%PVDF and of 20% (2%Ag-98%BaTiO3)-PVDF hybrid nanocomposites. By finite element calculations, it was shown that using fillers with epsilon > 103 does not provide a permittivity rise in the composites and the effective dielectric constant tends to saturate to specific values determined by the filler size and agglomeration degree. Irrespective of the ferroelectric filler sizes, the addition of metallic ultrafine nanoparticles (Ag) results in permittivity intensification and the effect is even stronger if the metallic nanoparticles are connected to a higher degree with the ferroelectric particles' surfaces. When using coarse ferroelectric fillers, the probability of clustering is higher, thus favoring the permittivity increase by field concentration in small regions close to the interfaces separating dissimilar materials. The modeling results were validated by an experimental dielectric analysis performed in a series of PVDF-based thick films with the same amount of BaTiO3 fillers or with Ag-BaTiO3 hybrid fillers. Similar trends as predicted by simulations were found experimentally but with slightly higher permittivity values which were assigned to the modifications of the polymer phase composition due to the presence of nanofillers and the local sample inhomogeneity (the presence of clustering, in particular for coarse BaTiO3 grains), which create regions with enhanced local fields.

In this study, we report the performance improvement of wound dressings by covering them with magnetite-based nanostructured coatings. The magnetite nanoparticles (Fe3O4 NPs) were functionalized with Nigella sativa (N. sativa) powder/essential oil and dicloxacillin and were synthesized as coatings by matrix assisted pulsed laser evaporation (MAPLE). The expected effects of this combination of materials are: (i) to reduce microbial contamination, and (ii) to promote rapid wound healing. The crystalline nature of core/shell Fe3O4 NPs and coatings was determined by X-ray diffraction (XRD). Differential Scanning Calorimetry (DSC) and Thermo Gravimetric Analysis (TGA) have been coupled to investigate the stability and thermal degradation of core/shell nanoparticle components. The coatings' morphology was examined by scanning electron microscopy (SEM). The distribution of chemical elements and functional groups in the resulting coatings was evidenced by Fourier transform infrared (FTIR) spectrometry. In order to simulate the interaction between wound dressings and epithelial tissues and to evaluate the drug release in time, the samples were immersed in simulated body fluid (SBF) and investigated after different durations of time. The antimicrobial effect was evaluated in planktonic (free-floating) and attached (biofilms) bacteria models. The biocompatibility and regenerative properties of the nanostructured coatings were evaluated in vitro, at cellular, biochemical, and the molecular level. The obtained results show that magnetite-based nanostructured coatings functionalized with N. sativa and dicloxacillin are biocompatible and show an enhanced antimicrobial effect against Gram positive and Gram negative opportunistic bacteria.

In this study, we evaluate the feasibility of using quantum neural networks for classifying gravitational waveforms, using both simulators and quantum computers. The analysis is quite interdisciplinary in its nature, combining knowledge involving astrophysics, quantum information as well as quantum and classical machine learning. We showed that the quantum classifiers and hybrid classical-quantum layers give highly accurate results when tested on a simple dataset and ran on a simulator; also, adding a quantum layer to poorly performing classical neural network can highly improve its accuracy. When running on a real quantum computer, error minimizing algorithms need to be implemented in order to obtain a satisfying accuracy.

A multi-step ion-exchange methodology was developed for the fabrication of Cu(LaTa2O7)(2) lamellar architectures capable of wastewater depollution. The (001) diffraction line of RbLaTa2O7 depended on the guest species hosted by the starting material. SEM and TEM images confirmed the well-preserved lamellar structure for all intercalated layered perovskites. The UV-Vis, XPS, and photocurrent spectroscopies proved that Cu intercalation induces a red-shift band gap compared to the perovskite host. Moreover, the UV-Vis spectroscopy elucidated the copper ions environment in the Cu-modified layered perovskites. H-2-TPR results confirmed that Cu species located on the surface are reduced at a lower temperature while those from the interlayer occur at higher temperature ranges. The photocatalytic degradation of phenol under simulated solar irradiation was used as a model reaction to assess the performances of the studied catalysts. Increased photocatalytic activity was observed for Cu-modified layered perovskites compared to RbLaTa2O7 pristine. This behavior resulted from the efficient separation of photogenerated charge carriers and light absorption induced by copper spacer insertion.

Two novel fluorescent mesoporous silica-based hybrid materials were obtained through the covalent grafting of [4-hydrazinyl-7-nitrobenz-[2,1,3-d]-oxadiazole (NBDH) and N-1-(7-nitrobenzo[c][1,2,5]-oxadiazol-4-yl) benzene-1,2-diamine (NBD-PD), respectively, inside the channels of mesoporous silica SBA-15. The presence of fluorescent organic compounds (nitrobenzofurazan derivatives) was confirmed by infrared spectroscopy (IR), X-ray photoelectron spectroscopy (XPS), thermal analysis (TG), and fluorescence spectroscopy. The nitrogen physisorption analysis showed that the nitrobenzofurazan derivatives were distributed uniformly on the internal surface of SBA-15, the immobilization process having a negligible effect on the structure of the support. Their antioxidant activity was studied by measuring the ability to reduce free radicals DPPH (free radical scavenging activity), in order to formulate potential applications of the materials obtained. Cytotoxicity of the newly synthesized materials, SBA-NBDH and SBA-NBD-PD, was evaluated on human B16 melanoma cells. The morphology of these cells, internalization and localization of the investigated materials in melanoma and fibroblast cells were examined through fluorescence imaging. The viability of B16 (3D) spheroids after treatment with SBA-NBDH and SBA-NBD-PD was evaluated using MTS assay. The results showed that both materials induced a selective antiproliferative effect, reducing to various degrees the viability of melanoma cells. The observed effect was enhanced with increasing concentration. SBA-NBD-PD exhibited a higher antitumor effect compared to SBA-NBDH starting with a concentration of 125 mu g/mL. In both cases, a significantly more pronounced antiproliferative effect on tumor cells compared to normal cells was observed. The viability of B16 spheroids dropped by 40% after treatment with SBA-NBDH and SBA-NBD-PD at 500 mu g/mL concentration, indicating a clear cytotoxic effect of the tested compounds. These results suggest that both newly synthesized biomaterials could be promising antitumor agents for applications in cancer therapy.

The precursor method was employed to prepare ZnAl2_xCrxO4 (x = 0, 0.25, 0.5, 0.75, 1) using tartaric acid as a ligand. Five tartarate compounds were isolated as precursors for the obtaining of zinc aluminate and chromium -substituted zinc aluminate. These coordination compounds were characterized by elemental chemical analysis, infrared (IR) and ultraviolet visible (UV-Vis) spectroscopy, and thermal analysis. The influence of Cr3+ substi-tution on the structure, morphology and optical properties of the synthesized mixed oxides was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), infrared, Raman and UV-Vis spectroscopy, and nitrogen adsorption - desorption analysis. The XRD patterns and Raman spectra confirmed the formation of spinel structure. The mean crystallite size varied from 18 to 22 nm SEM and EDS showed uniform composition and microstructure of the ZnAl2_xCrxO4 nanocrystalline powders. The values of the optical energy bandgap for the samples were found to be in the 3.92 - 2.85 eV range. The photocatalytic performance in the degradation reaction of Eosin Y (EY) under visible light irradiation was evaluated. The Eosin Y degradation efficiency values were obtained between 48% and 80% after 75 min. The best photocatalytic result was obtained for the sample with the highest amount of chromium.