Radu-Constantin CERCEL

In this work, three methods for the synthesis of composites based on poly(ortho-toluidine) (POT) and WS2 are reported: (a) the solid-state interaction (SSI) of POT with WS2 nanoparticles (NPs); (b) the in situ chemical polymerization (ICP) of ortho-toluidine (OT); and (c) the electrochemical polymerization (ECP) of OT. The preparation of WS2 sheets was performed by the ball milling of the WS2 NPs followed by ultrasonication in the solvent N,N'-dimethyl formamide. During the synthesis of the POT/WS2 composites by SSI and ICP, an additional exfoliation of the WS2 NPs was reported. In this work, we demonstrated the following: (a) the ICP method leads to POT/WS2 composites, which contain repeating units of POT in the leucoemeraldine salt (LS) state, while (b) the ECP method leads to POT/WS2 composites, which contain repeating units of POT in the emeraldine salt (ES) state. Capacitances equal to 123.5, 465.76, and 751.6 mF cm-2 in the cases of POT-ES/WS2 composites, synthesized by SSI, ICP, and ECP, respectively, were reported.

In this work, applications of nanohybrid composites based on titanium dioxide (TiO2) with anatase crystallin phase and single-walled carbon nanohorns (SWCNHs) as promising catalysts for the photodegradation of amoxicillin (AMOX) are reported. In this order, TiO2/SWCNH composites were prepared by the solid-state interaction of the two chemical compounds. The increase in the SWCNH concentration in the TiO2/SWCNH composite mass, from 1 wt.% to 5 wt.% and 10 wt.% induces (i) a change in the relative intensity ratio of the Raman lines located at 145 and 1595 cm(-1), which are attributed to the E-g(1) vibrational mode of TiO2 and the graphitic structure of SWCNHs; and (ii) a gradual increase in the IR band absorbance at 1735 cm(-1) because of the formation of new carboxylic groups on the SWCNHs' surface. The best photocatalytic properties were obtained for the TiO2/SWCNH composite with a SWCNH concentration of 5 wt.%, when approx. 92.4% of AMOX removal was achieved after 90 min of UV irradiation. The TiO2/SWCNH composite is a more efficient catalyst in AMOX photodegradation than TiO2 as a consequence of the SWCNHs' presence, which acts as a capture agent for the photogenerated electrons of TiO2 hindering the electron-hole recombination. The high stability of the TiO2/SWCNH composite with a SWCNH concentration of 5 wt.% is proved by the reusing of the catalyst in six photodegradation cycles of the 98.5 mu M AMOX solution, when the efficiency decreases from 92.4% up to 78%.

New aspects concerning the photodegradation (PD) of ampicillin are reported by photoluminescence (PL), Raman scattering and FTIR spectroscopy. The exposure of ampicillin in the absence (AM) and in the presence of the excipient (AMP) to UV light leads to an intensity diminution of the photoluminescence excitation (PLE) and photoluminescence (PL) spectra and the emergence of a new IR band at 3450 cm(-1). The photoluminescence studies demonstrate that the AM PD is amplified in the presence of excipients and an alkaline medium. In this last case, the PD process of AM involves the emergence of new compounds, whose presence is highlighted by: (i) the emergence of the isosbestic point at 300 nm in the UV-VIS spectra; (ii) a change in the ratio between the absorbance of IR bands situated in the spectral ranges 1200-1660 and 3250-3450 cm(-1); and (iii) a change in the ratio between the intensities of the Raman lines localized in the spectral ranges 1050-1800 and 2750-3100 cm(-1). A chemical mechanism of the PD processes of AM in an alkaline medium is proposed.

In this work, new optical evidences concerning the changes induced of the UV light on pantoprazole sodium (PS), in solid state and as aqueous solution, are reported by UV-VIS spectroscopy, photoluminescence (PL), Raman scattering and FTIR spectroscopy. New evidences concerning the products of the PS photodegradation pathways are reported by the correlated studies of thermogravimetry and mass spectrometry. The influence of the excipients and alkaline medium on the PS photodegradation is also studied. New aspects regarding the chemical mechanism of the PS photodegradation in the presence of the water vapor and oxygen form air and the alkaline medium are shown. Our results confirm that the PS photodegradation induced of the water vapors and oxygen from air leads to the generation of 5-difluoromethoxy-3H-benzimidazole-2-thione sodium, 5-difluoromethoxy-3H-benzimidazole sodium, 2-thiol methyl-3, 4-dimethoxypyridine and 2-hydroxymethyl-3, 4-dimethoxypyridine, while in the alkaline medium, compounds of the type of the 2-oxymethyl-3,4-dimethoxypyridine sodium salts are resulted.

In this work, new films containing composite materials based on blends of thermoplastic polymers of the polyurethane (TPU) and polyolefin (TPO) type, in the absence and presence of BaTiO3 nanoparticles (NPs) with the size smaller 100 nm, were prepared. The vibrational properties of the free films depending on the weight ratio of the two thermoplastic polymers were studied. Our results demonstrate that these films are optically active, with strong, broad, and adjustable photoluminescence by varying the amount of TPU. The crystalline structure of BaTiO3 and the influence of thermoplastic polymers on the crystallization process of these inorganic NPs were determined by X-ray diffraction (XRD) studies. The vibrational changes induced in the thermoplastic polymer's matrix of the BaTiO3 NPs were showcased by Raman scattering and FTIR spectroscopy. The incorporation of BaTiO3 NPs in the matrix of thermoplastic elastomers revealed the shift dependence of the photoluminescence (PL) band depending on the BaTiO3 NP concentration, which was capable of covering a wide visible spectral range. The dependencies of the dielectric relaxation phenomena with the weight of BaTiO3 NPs in thermoplastic polymers blends were also demonstrated.

The effect of UV light on the cationic photopolymerization of the SU8 negative photoresist is shown by photoluminescence (PL) studies. Our results demonstrate that the cationic photopolymerization reaction of the SU8 photoresist takes place predominantly under the influence of the UVA light. Using UVA light, the influence of carbon nanotubes [of the types single-walled carbon nanotubes (SWNTs), double-walled carbon nanotubes (DWNTs), multiwalled carbon nanotubes (MWNTs), and SWNTs functionalized with carboxyl groups (SWNTs-COOH)] on the cationic photopolymerization process of the SU8 photoresist is shown by PL studies. The cationic photopolymerization of the SU8 photoresist is monitored by the variations of the two emission bands with maxima at similar to 400-429 nm and 523-556 nm. The increase in the relative intensity of the PL band at similar to 523-556 nm is dependent on (i) the carbon nanotube concentration in the SU8 photoresist matrix; (ii) the type of carbon nanotubes, i.e., SWNTs, DWNTs, and MWNTs; and (iii) the nonfunctionalized and functionalized state of SWNTs. The results reported in this work demonstrate that PL can be used as a complementary method to Raman scattering and IR spectroscopy in the investigation of the cationic photopolymerization reaction of the SU8 negative photoresist. A decrease in the wrapping angle of carbon nanotubes with the SU8 photoresist is highlighted by anisotropic PL studies.

The influence of Ag and Au nanoparticles and reduced graphene oxide (RGO) sheets on the photodegradation of alpha-lipoic acid (ALA) was determined by UV-VIS spectroscopy. The ALA photodegradation was explained by considering the affinity of thiol groups for the metallic nanoparticles synthesized in the presence of trisodium citrate. The presence of excipients did not induce further changes when ALA interacts with Ag and Au nanoparticles with sizes of 5 and 10 nm by exposure to UV light. Compared to the Raman spectrum of ALA powder, changes in Raman lines' position and relative intensities when ALA has interacted with films obtained from Au nanoparticles with sizes between 5 and 50 nm were significant. These changes were explained by considering the chemical mechanism of surface-enhanced Raman scattering (SERS) spectroscopy. The photodegradation of ALA that had interacted with metallic nanoparticles was inhibited in the presence of RGO sheets.