National Institute Of Materials Physics - Romania

This article's objective is the synthesis of new composites based on thermoplastic polyurethane (TPU) and TiO2 nanowires (NWs) as free-standing films, highlighting their structural and optical properties. The free-standing TPU-TiO2 NW films were prepared by a wet chemical method accompanied by a thermal treatment at 100 degrees C for 1 h, followed by air-drying for 2 h. X-ray diffraction (XRD) studies indicated that the starting commercial TiO2 NW sample contains TiO2 tetragonal anatase (A), cubic Ti0.91O (C), and orthorhombic Ti2O3 (OR), as well as monoclinic H2Ti3O7 (M). In the presence of TPU, an increase in the ratio between the intensities of the diffraction peaks at 43.4 degrees and 48 degrees belonging to the C and A phases of titanium dioxide, respectively, is reported. The increase in the intensity of the peak at 43.4 degrees is explained to be a consequence of the interaction of TiO2 NWs with PTU, which occurs when the formation of suboxides takes place. The variation in the ratio of the absorbance of the IR bands peaked at 765-771 cm(-1) and 3304-3315 cm(-1) from 4.68 to 4.21 and 3.83 for TPU and the TPU-TiO2 NW composites, respectively, with TiO2 NW concentration equal to 2 wt.% and 17 wt.%, indicated a decrease in the higher-order aggregates of TPU with a simultaneous increase in the hydrogen bonds established between the amide groups of TPU and the oxygen atoms of TiO2 NWs. The decrease in the ratio of the intensity of the Raman lines peaked at 658 cm(-1) and 635 cm(-1), which were assigned to the vibrational modes E-g in TiO2 A and E-g in H2Ti3O7 (ITiO2-A/I-H2Ti3O7), respectively, from 3.45 in TiO2 NWs to 0.94-0.96 in the TPU-TiO2 NW composites, which indicates that the adsorption of TPU onto TiO2 NWs involves an exchange reaction of TPU in the presence of TiO2 NWs, followed by the formation of new hydrogen bonds between the -NH- of the amide group and the oxygen atoms of TixO2x-mn, Ti2O3, and Ti0.91O. Photoluminescence (PL) studies highlighted a gradual decrease in the intensity of the TPU emission band, which is situated in the spectral range 380-650 nm, in the presence of TiO2 NW. After increasing the TiO2 NW concentration in the TPU-TiO2 NW composite mass from 0 wt.% to 2 wt.% and 17 wt.%, respectively, a change in the binding angle of the TPU onto the TiO2 NW surface from 12.6 degrees to 32 degrees and 45.9 degrees, respectively, took place.

Pb(Zr,Ti)O-3 (PZT) is the most common ferroelectric (FE) material widely used in solid-state technology. Despite intense studies of PZT over decades, its intrinsic band structure, electron energy depending on 3D momentum k, is still unknown. Here, Pb(Zr0.2Ti0.8)O-3 using soft-X-ray angle-resolved photoelectron spectroscopy (ARPES) is explored. The enhanced photoelectron escape depth in this photon energy range allows sharp intrinsic definition of the out-of-plane momentum k and thereby of the full 3D band structure. Furthermore, the problem of sample charging due to the inherently insulating nature of PZT is solved by using thin-film PZT samples, where a thickness-induced self-doping results in their heavy doping. For the first time, the soft-X-ray ARPES experiments deliver the intrinsic 3D band structure of PZT as well as the FE-polarization dependent electrostatic potential profile across the PZT film deposited on SrTiO3 and LaxSrMn1-xO3 substrates. The negative charges near the surface, required to stabilize the FE state pointing away from the sample (P+), are identified as oxygen vacancies creating localized in-gap states below the Fermi energy. For the opposite polarization state (P-), the positive charges near the surface are identified as cation vacancies resulting from non-ideal stoichiometry of the PZT film as deduced from quantitative XPS measurements.

The technology of perovskite solar cells (PSC) is getting close to breaching the consumer market. Yet, one of the current challenges is to reduce the toxicity during their fabrication by reducing the use of the toxic solvents involved in the perovskite fabrication process. A good solubilization of lead halides used in hybrid perovskite preparation is required, and it is only possible with polar solvents. A mixture of dimethylformamide (DMF) and dimethyl sulfoxide (DMSO) is the most popular solvent combination for a perovskite precursor solution. DMF is necessary to ensure a good dissolution of lead iodide, but it is also the most toxic solvent. In this paper, we study the replacement of the dimethylformamide with presumably less toxic alternatives, such as N-methyl-2-Pyrrolidone (NMP) and ethyl acetate (EA), for the preparation of the K(0.1)FA(0.7)MA(0.2)PbI(2.8)Cl(0.2) (KFAMA) hybrid perovskite. The perovskite thin films were investigated by various characterization techniques: X-ray diffraction, atomic force microscopy, scanning electron microscopy, and UV-vis spectroscopy, while the photovoltaic parameters were determined by measuring the IV curves of the corresponding solar cells. The present study shows that by keeping the same deposition parameters as when only DMF solvent is used, the partial solvent substitution with NMP and EA gives promising results for reducing the toxicity of the fabrication process of KFAMA-based PSCs. Thus, with no specific optimization of the deposition process, and for the maximum possible partial substitution of DMF with NMP and EA solvents, the loss in the power conversion efficiency (PCE) value is only 35% and 18%, respectively, associated with the more structural defects promoted by NMP and EA.

In this paper, the stability of magnesium-doped hydroxyapatite/chitosan (MHC) suspension obtained with the sol-gel approach was evaluated using nondestructive ultrasound measurements. The MHC coatings obtained by the spin-coating technique were characterized before and after immersion for 7 and 14 days, respectively, in Dulbecco's modified eagle medium (DMEM) by scanning electron microscopy, equipped with an EDAX detector. Also, the functional groups present on the MHC coatings surface were analyzed with the aid of attenuated total reflection (ATR) Fourier transform infrared (FTIR) spectroscopy. The surface microstructure was evaluated using two commentary techniques, namely atomic force microscopy (AFM) and metallographic microscopy (MM). The influence of immersion in DMEM on the biological properties was studied with in vitro studies using primary osteoblast and HCT-8 cell lines. Our results revealed that both surface morphology and chemical composition of the MHC coatings allow rapid development of a new apatite layer on their surface after immersion in DMEM. Preliminary in vitro biological studies underlined the noncytotoxic effect of the studied samples on the proliferation of primary osteoblast and HCT-8 cell lines, which makes them a promising candidate for applications in fields such as orthopedics or dentistry. The antifungal assay of the MHC coatings was assessed using Candida albicans ATCC 10231 and their results showed a good inhibitory effect. The coatings made on the basis of the MHC composite could contribute to increasing the degree of success of implants by decreasing the risk of infections and postoperative inflammation.

Pb(Zr,Ti)O-3 (PZT) is the most common ferroelectric (FE) material widely used in solid-state technology. Despite intense studies of PZT over decades, its intrinsic band structure, electron energy depending on 3D momentum k, is still unknown. Here, Pb(Zr0.2Ti0.8)O-3 using soft-X-ray angle-resolved photoelectron spectroscopy (ARPES) is explored. The enhanced photoelectron escape depth in this photon energy range allows sharp intrinsic definition of the out-of-plane momentum k and thereby of the full 3D band structure. Furthermore, the problem of sample charging due to the inherently insulating nature of PZT is solved by using thin-film PZT samples, where a thickness-induced self-doping results in their heavy doping. For the first time, the soft-X-ray ARPES experiments deliver the intrinsic 3D band structure of PZT as well as the FE-polarization dependent electrostatic potential profile across the PZT film deposited on SrTiO3 and LaxSrMn1-xO3 substrates. The negative charges near the surface, required to stabilize the FE state pointing away from the sample (P+), are identified as oxygen vacancies creating localized in-gap states below the Fermi energy. For the opposite polarization state (P-), the positive charges near the surface are identified as cation vacancies resulting from non-ideal stoichiometry of the PZT film as deduced from quantitative XPS measurements.

This article's objective is the synthesis of new composites based on thermoplastic polyurethane (TPU) and TiO2 nanowires (NWs) as free-standing films, highlighting their structural and optical properties. The free-standing TPU-TiO2 NW films were prepared by a wet chemical method accompanied by a thermal treatment at 100 degrees C for 1 h, followed by air-drying for 2 h. X-ray diffraction (XRD) studies indicated that the starting commercial TiO2 NW sample contains TiO2 tetragonal anatase (A), cubic Ti0.91O (C), and orthorhombic Ti2O3 (OR), as well as monoclinic H2Ti3O7 (M). In the presence of TPU, an increase in the ratio between the intensities of the diffraction peaks at 43.4 degrees and 48 degrees belonging to the C and A phases of titanium dioxide, respectively, is reported. The increase in the intensity of the peak at 43.4 degrees is explained to be a consequence of the interaction of TiO2 NWs with PTU, which occurs when the formation of suboxides takes place. The variation in the ratio of the absorbance of the IR bands peaked at 765-771 cm(-1) and 3304-3315 cm(-1) from 4.68 to 4.21 and 3.83 for TPU and the TPU-TiO2 NW composites, respectively, with TiO2 NW concentration equal to 2 wt.% and 17 wt.%, indicated a decrease in the higher-order aggregates of TPU with a simultaneous increase in the hydrogen bonds established between the amide groups of TPU and the oxygen atoms of TiO2 NWs. The decrease in the ratio of the intensity of the Raman lines peaked at 658 cm(-1) and 635 cm(-1), which were assigned to the vibrational modes E-g in TiO2 A and E-g in H2Ti3O7 (ITiO2-A/I-H2Ti3O7), respectively, from 3.45 in TiO2 NWs to 0.94-0.96 in the TPU-TiO2 NW composites, which indicates that the adsorption of TPU onto TiO2 NWs involves an exchange reaction of TPU in the presence of TiO2 NWs, followed by the formation of new hydrogen bonds between the -NH- of the amide group and the oxygen atoms of TixO2x-mn, Ti2O3, and Ti0.91O. Photoluminescence (PL) studies highlighted a gradual decrease in the intensity of the TPU emission band, which is situated in the spectral range 380-650 nm, in the presence of TiO2 NW. After increasing the TiO2 NW concentration in the TPU-TiO2 NW composite mass from 0 wt.% to 2 wt.% and 17 wt.%, respectively, a change in the binding angle of the TPU onto the TiO2 NW surface from 12.6 degrees to 32 degrees and 45.9 degrees, respectively, took place.

Hydrogen production from methanol decomposition to syngas (H2 + CO) is a promising alternative route for clean energy transition. One major challenge is related to the quest for stable, cost-effective, and selective catalysts operating below 400 degrees C. We illustrate an investigation of the surface reactivity of a Ni3Sn4 catalyst working at 250 degrees C, by combining density functional theory, operando X-ray absorption spectroscopy, and high-resolution transmission electron microscopy. We discovered that the catalytic reaction is driven by surface tin-oxide phases, which protects the underlying Ni atoms from irreversible chemical modifications, increasing the catalyst durability. Moreover, we found that Sn content plays a key role in enhancing the H2 selectivity, with respect to secondary products such as CO2. These findings open new perspectives for the engineering of scalable and low-cost catalysts for hydrogen production.

Shape memory alloys, especially ferromagnetic shape memory alloys, are interesting new materials for the manufacturing of stents. Iron-palladium alloys in particular can be used to manufacture self-expanding temporary stents due to their optimum rate of degradation, which is between that of magnesium and pure iron, two metals commonly used in temporary stent research. In order to avoid blood clotting upon the introduction of the stent, they are often coated with anticoagulants. In this study, sulfated pectin, a heparin mimetic, was synthesized in different ways and used as coating on multiple iron-palladium alloys. The static and dynamic prothrombin time (PT) and activated partial thromboplastin time (APTT) of the prepared materials were compared to samples uncoated or coated with polyethylene glycol. While no large differences were observed in the prothrombin time measurements, the activated partial thromboplastin time increased significantly with all alloys coated with sulfated pectin. Aside from that, sulfated pectin synthesized by different methods also caused slight changes in the activated partial thromboplastin time. These findings show that iron-palladium alloys can be coated with anticoagulants to improve their utility as material for temporary stents. Sulfated pectin was characterized by nuclear magnetic resonance (NMR) and Fourier-transform infrared (FTIR) spectroscopy, and the coated alloys by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX).

As metasurfaces begin to find industrial applications there is a need to develop scalable and cost-effective fabrication techniques which offer sub-100 nm resolution while providing high throughput and large area patterning. Here we demonstrate the use of UV-Nanoimprint Lithography and Deep Reactive Ion Etching (Bosch and Cryogenic) towards this goal. Robust processes are described for the fabrication of silicon rectangular pillars of high pattern fidelity. To demonstrate the quality of the structures, metasurface lenses, which demonstrate diffraction limited focusing and close to theoretical efficiency for NIR wavelengths lambda is an element of (1.3 mu m, 1.6 mu m), are fabricated. We demonstrate a process which removes the characteristic sidewall surface roughness of the Bosch process, allowing for smooth 90-degree vertical sidewalls. We also demonstrate that the optical performance of the metasurface lenses is not affected adversely in the case of Bosch sidewall surface roughness with 45 nm indentations (or scallops). Next steps of development are defined for achieving full wafer coverage.

Iron oxide nanoparticles are one of the most promising tools for theranostic applications of pancreatic cancer due to their unique physicochemical and magnetic properties making them suitable for both diagnosis and therapy. Thus, our study aimed to characterize the properties of dextran-coated iron oxide nanoparticles (DIO-NPs) of maghemite (gamma-Fe2O3) type synthesized by co-precipitation and to investigate their effects (low-dose versus high-dose) on pancreatic cancer cells focusing on NP cellular uptake, MR contrast, and toxicological profile. This paper also addressed the modulation of heat shock proteins (HSPs) and p53 protein expression as well as the potential of DIO-NPs for theranostic purposes. DIO-NPs were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), dynamic light scattering analyses (DLS), and zeta potential. Pancreatic cancer cells (PANC-1 cell line) were exposed to different doses of dextran-coated gamma-Fe2O3 NPs (14, 28, 42, 56 mu g/mL) for up to 72 h. The results revealed that DIO-NPs with a hydrodynamic diameter of 16.3 nm produce a significant negative contrast using a 7 T MRI scanner correlated with dose-dependent cellular iron uptake and toxicity levels. We showed that DIO-NPs are biocompatible up to a concentration of 28 mu g/mL (low-dose), while exposure to a concentration of 56 mu g/mL (high-dose) caused a reduction in PANC-1 cell viability to 50% after 72 h by inducing reactive oxygen species (ROS) production, reduced glutathione (GSH) depletion, lipid peroxidation, enhancement of caspase-1 activity, and LDH release. An alteration in Hsp70 and Hsp90 protein expression was also observed. At low doses, these findings provide evidence that DIO-NPs could act as safe platforms in drug delivery, as well as antitumoral and imaging agents for theranostic uses in pancreatic cancer.