National Institute Of Materials Physics - Romania

Rhombohedral phase HfxZr1-xO2 (HZO, x from 0 to 1) films are promising for achieving robust ferroelectric polarization without the need for an initial wake-up pre-cycling, as is normally the case for the more commonly studied orthorhombic phase. However, a large spontaneous polarization observed in rhombohedral films is not fully understood, and there are also large discrepancies between experimental and theoretical predictions. In this work, in rhombohedral ZrO2 thin films, we show that oxygen vacancies are not only a key factor for stabilizing the phase, but they are also a source of ferroelectric polarization in the films. This is shown experimentally through the investigation of the structural properties, chemical composition and the ferroelectric properties of the films before and after an annealing at moderate temperature (400 degrees C) in an oxygen environment to reduce the V-O concentration compared. The experimental work is supported by density functional theory (DFT) calculations which show that the rhombohedral phase is the most stable one in highly oxygen defective ZrO2 films. The DFT calculations also show that V-O contribute to the ferroelectric polarization. Our findings reveal the importance of V-O for stabilizing rhombohedral ZrO2 thin films with superior ferroelectric properties.

Properties of surface species of the nematic mixture E7 in contact with inorganic oxides (especially those containing more or less aluminium ions) are in detail investigated by infrared spectroscopy and thermogravimetry. The absorption infrared peaks were decomposed into Gaussian components, the procedure allowing an easier comparison with the behaviour of related composites. We worked at enough small concentrations of the E7 relatively to support this ratio permitting the (partial) elimination of the species belonging to the bulk. Species put here in evidence are species that are hydrogen bonded to the surface of OH groups, molecules randomly oriented on the surface, some species bonded by involvement of pi electrons of the CN group to the aluminium ions, thus implying a strong interaction to the support. Supramolecular assemblies of E7 molecules are thus followed up.

Properties of surface species of the nematic mixture E7 in contact with inorganic oxides (especially those containing more or less aluminium ions) are in detail investigated by infrared spectroscopy and thermogravimetry. The absorption infrared peaks were decomposed into Gaussian components, the procedure allowing an easier comparison with the behaviour of related composites. We worked at enough small concentrations of the E7 relatively to support this ratio permitting the (partial) elimination of the species belonging to the bulk. Species put here in evidence are species that are hydrogen bonded to the surface of OH groups, molecules randomly oriented on the surface, some species bonded by involvement of pi electrons of the CN group to the aluminium ions, thus implying a strong interaction to the support. Supramolecular assemblies of E7 molecules are thus followed up.

A new approach for the stabilization of the ferroelectric orthorhombic ZrO2 films is demonstrated through nanosecond laser annealing (NLA) of as-deposited Si/SiOx/W(14 nm)/ZrO2(8 nm)/W(22 nm), grown by ion beam sputtering at low temperatures. The NLA process optimization is guided by COMSOL multiphysics simulations. The films annealed under the optimized conditions reveal the presence of the orthorhombic phase, as confirmed by X-ray diffraction, electron backscatter diffraction, and transmission electron microscopy. Macroscopic polarization-electric field hysteresis loops show ferroelectric behavior, with saturation polarization of 12.8 mu C cm(-2), remnant polarization of 12.7 mu C cm(-2) and coercive field of 1.2 MV cm(-1). The films exhibit a wake-up effect that is attributed to the migration of point defects, such as oxygen vacancies, and/or a transition from nonferroelectric (monoclinic and tetragonal phase) to the ferroelectric orthorhombic phase. The capacitors demonstrate a stable polarization with an endurance of 6.0 x 10(5) cycles, demonstrating the potential of the NLA process for the fabrication of ferroelectric memory devices with high polarization, low coercive field, and high cycling stability.

Historically, titanium dioxide (TiO2) has been one of the most extensively studied metal oxide photocatalysts; however, it suffers from a large bandgap and fast charge recombination. We report the use of green, rapid, single-step continuous hydrothermal flow synthesis for the preparation of TiO2, and TiO2 hybrids with reduced graphene oxide (rGO) and/or N-doped carbon quantum dots (NCQDs) with significant enhancement in photocatalytic activity. Using a solar light generator under ambient conditions with no extra oxygen gas added, we observed the evolution reaction of the model pollutant (methylene blue) in real time. Tailoring of the light absorption to match that of the solar spectrum was achieved by a combination of materials of nano-TiO2 hybrids of nitrogen-doped carbon quantum dots and graphene in its reduced form with a photocatalytic rate constant of ca. 25 x 10(-5) s(-1). Using a diversity of state-of-the-art techniques including high-resolution transmission electron microscopy, transient photoluminescence, X-ray photoelectron spectroscopy and high accuracy, sophisticated hybrid density functional theory calculations we have gained substantial insight into the charge transfer and modulation of the energy band edges of anatase due to the presence of graphene or carbon dots, parameters which play a key role in improving drastically the photocatalytic efficiencies when compared to pristine titania. More importantly, we prove that a combination of features and materials displays the best photocatalytic behaviour. This performance is delivered in a greener synthetic process that not only produces photocatalytic materials with optimised properties and tailored visible light absorption and efficiency but also provides a path to industrialization.

Nonmagnetic chiral crystals are a new class of systems hosting Kramers-Weyl Fermions, arising from the combination of structural chirality, spin- orbit coupling (SOC), and time-reversal symmetry. These materials exhibit nontrivial Fermi surfaces with SOC-induced Chern gaps over a wide energy range, leading to exotic transport and optical properties. In this study, we investigate the electronic structure and transport properties of CdAs2, a newly reported chiral material. We use synchrotron-based angle-resolved photoelectron spectroscopy (ARPES) and density functional theory (DFT) to determine the Fermiology of the (110)-terminated CdAs2 crystal. Our results, together with complementary magnetotransport measurements, suggest that CdAs2 is a promising candidate for novel topological properties protected by the structural chirality of the system. Our work sheds light on the details of the Fermi surface and topology for this chiral quantum material, providing useful information for engineering novel spintronic and optical devices based on quantized chiral charges, negative longitudinal magnetoresistance, and nontrivial Chern numbers.

Rhombohedral phase HfxZr1-xO2 (HZO, x from 0 to 1) films are promising for achieving robust ferroelectric polarization without the need for an initial wake-up pre-cycling, as is normally the case for the more commonly studied orthorhombic phase. However, a large spontaneous polarization observed in rhombohedral films is not fully understood, and there are also large discrepancies between experimental and theoretical predictions. In this work, in rhombohedral ZrO2 thin films, we show that oxygen vacancies are not only a key factor for stabilizing the phase, but they are also a source of ferroelectric polarization in the films. This is shown experimentally through the investigation of the structural properties, chemical composition and the ferroelectric properties of the films before and after an annealing at moderate temperature (400 degrees C) in an oxygen environment to reduce the V-O concentration compared. The experimental work is supported by density functional theory (DFT) calculations which show that the rhombohedral phase is the most stable one in highly oxygen defective ZrO2 films. The DFT calculations also show that V-O contribute to the ferroelectric polarization. Our findings reveal the importance of V-O for stabilizing rhombohedral ZrO2 thin films with superior ferroelectric properties.

Background: Based on the current configuration of the International Thermonuclear Experimental Reactor, tungsten (W) was chosen as the armour material. Nevertheless, during operation, the expected power and temperature of plasma can trigger the formation of W dust in the plasma chamber. According to the scenario for a Loss Of Vacuum Accident (LOVA), in the case of confinement failure dust is released, which can lead to occupational or accidental exposure.Methods: For a first evidence of potential risks, fusion devices relevant W dust has been produced on purpose, using a magnetron sputtering gas aggregation source. We aimed to assess the in vitro cytotoxicity of synthesized tungsten nanoparticles (W-NPs) with diameters of 30 and 100 nm, on human BJ fibroblasts. That was systematically investigated using different cytotoxic endpoints (metabolic activity, cellular ATP, AK release and caspase-3/7 activity) and by direct observation with optical and scanning electron microscopy.Results: Increasing concentrations of W-NPs of both sizes induced cell viability decrease, but the effect was significantly higher for large W-NPs, starting from 200 mu g/mL. In direct correlation with the effect on the cell membrane integrity, high concentrations of large W-NPs appear to increase AK release in the first 24 h of treatment. On the other hand, activation of the cellular caspase 3/7 was found significantly increased after 16 h of treatment solely for low concentra-tions of small W-NPs. SEM images revealed an increased tendency of agglomeration of small W -NPs in liquid medium, but no major differences in cells development and morphology were observed after treatment. An apparent internalization of nanoparticles under the cell membrane was also identified.Conclusion: These results provide evidence for different toxicological outputs identified as mechanistic responses of BJ fibroblasts to different sizes of W-NPs, indicating also that small W -NPs (30 nm) display lower cytotoxicity compared to larger ones (100 nm).

Herein, a new direct synthesis route leading to a mesoporous NiWO4 with crystalline framework and NiWO4 -graphene nanoplatelets (GNP) composite is reported. Ni and W assembled into a mesoporous tungstate type of symmetry by co-precipitation synthesis route and its composite with GNP were used as supports for electrocatalysts, with reduced Pt content (8 wt.%), in oxygen reduction reaction (ORR) and hydrogen oxidation reaction (HOR) in acidic medium. A comprehensive assessment of the modifications related to the crystalline and porous structures, morphological aspects as well as the surface chemistry aiming to explain the electrochemical properties was performed. It was found that the presence of GNP during the synthesis process leads, mainly, to the enhanced growth of NiWO4 nanocrystallites, as well as induces changes in the surface chemistry. The elec-trochemical results show that the introduction of GNPs into the NiWO4 composite support leads to a significant improvement in the activity of the Pt electrocatalyst in ORR and HOR compared to both initial NiWO4 and Pt/NiWO4 samples, as well as mechanical mixtures of these catalysts with carbon. Mass activity for hydrogen oxidation, determined in a mixed kinetic-diffusion controlled region, obtained on the 8 wt.% Pt/NiWO4-GNP catalyst was significantly higher compared to the commercial 20 wt.% Pt/C Quintech catalyst. Our comprehensive structural and surface chemistry assessments indicate this composite material as a viable electrocatalyst for PEMFCs using a broader type of fuels.& COPY; 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Hybrid layers consisting of Fe oxide, Fe hydroxide, and nitrogen doped graphene-like platelets have been synthesized by an eco-friendly laser-based method for photocatalytic applications. The complex composite layers show high photodecomposition efficiency towards degradation of antibiotic molecules under visible light irradiation. The photodecomposition efficiency was investigated as a function of relative concentrations of base materials, Fe oxide nanoparticles and graphene oxide platelets used for the preparation of target dispersions submitted to laser irradiation. Although reference pure Fe oxide/Fe hydroxide layers have high absorption in the visible spectral region, their photodecomposition efficiency is negligible under the same irradiation conditions. The high photocatalytic decomposition efficiency of the nanohybrid layer, up to 80% of the initial antibiotic molecules was assigned to synergistic effects between the constituent materials, efficient separation of the electron-hole pairs generated by visible light irradiation on the surface of Fe oxide and Fe hydroxide nanoparticles, in the presence of conducting graphene-like platelets. Nitrogen doped graphene-like platelets contribute also to the generation of electron-hole pairs under visible light irradiation, as demonstrated by the photocatalytic activity of pure, reference nitrogen doped graphene-like layers. The results also showed that adsorption processes do not contribute significantly to the removal of antibiotic molecules from the test solutions. The decrease of the antibiotic concentration under visible light irradiation was assigned primarily to photocatalytic decomposition mechanisms.