Alexandra ROTARU

The paper presents a study concerning the role of ferroelectric filler size and clustering in the dielectric properties of 20%BaTiO3-80%PVDF and of 20% (2%Ag-98%BaTiO3)-PVDF hybrid nanocomposites. By finite element calculations, it was shown that using fillers with epsilon > 103 does not provide a permittivity rise in the composites and the effective dielectric constant tends to saturate to specific values determined by the filler size and agglomeration degree. Irrespective of the ferroelectric filler sizes, the addition of metallic ultrafine nanoparticles (Ag) results in permittivity intensification and the effect is even stronger if the metallic nanoparticles are connected to a higher degree with the ferroelectric particles' surfaces. When using coarse ferroelectric fillers, the probability of clustering is higher, thus favoring the permittivity increase by field concentration in small regions close to the interfaces separating dissimilar materials. The modeling results were validated by an experimental dielectric analysis performed in a series of PVDF-based thick films with the same amount of BaTiO3 fillers or with Ag-BaTiO3 hybrid fillers. Similar trends as predicted by simulations were found experimentally but with slightly higher permittivity values which were assigned to the modifications of the polymer phase composition due to the presence of nanofillers and the local sample inhomogeneity (the presence of clustering, in particular for coarse BaTiO3 grains), which create regions with enhanced local fields.

Flexible composites containing BaTiO3 nanoparticles into Gelatin bio-polymer matrix were designed and investigated. Following the idea that the electric field concentration in corners/edges at the interfaces between dissimilar materials give rise to enhanced effective permittivity in composites, cuboid-like BaTiO3 nanoparticles have been employed as nanofillers into Gelatin matrix by using an inexpensive solution-based processing method. As predicted by finite element method simulations developed for cubic-like inclusions into a homogeneous polymer matrix, the experimental permittivity of xBT-(1-x)Gelatin composites increases when increasing the high-permittivity filler addition. For the composition x = 40 wt% (corresponding to 12 vol% BaTiO3 addition), permittivity reaches epsilon r -15.7 with respect to epsilon r -9.8 of pure Gelatine (measured at 105 Hz), while the average piezoelectric coefficient d33 as determined by piezoelectric force microscopy shows a remarkable increase up to 21 pm/V in composites with x = 40 wt%, in comparison to -7 pm/V in pure Gelatin. By using the experimentally determined material constants, the simulated piezoelectric voltage output vs. time has shown a similar increase (about a doubling of its amplitude) of the harvesting signal in the composite with x = 40 wt% BT, with respect to one of the polymer matrix, thus demonstrating the beneficial role of embedding BT nanoparticles into the biopolymer for increasing the mechanical harvesting response.

The role of Ag addition on the structural, dielectric, and mechanical harvesting response of 20%(xAg - (1 - x)BaTiO3) - 80%PVDF (x = 0, 2, 5, 7 and 27 vol.%) flexible composites is investigated. The inorganic fillers were realized by precipitating fine (similar to 3 nm) silver nanoparticles onto BaTiO3 nanoparticles (similar to 60 nm average size). The hybrid admixtures with a total filling factor of 20 vol.% were embedded into the PVDF matrix. The presence of filler enhances the amount of beta-PVDF polar phase and the BaTiO3 filler induces an increase of the permittivity from 11 to 18 (1 kHz) in the flexible composites. The addition of increasing amounts of Ag is further beneficial for permittivity increase; with the maximum amount (x = 27 vol.%), permittivity is three times larger than in pure PVDF (epsilon(r) similar to 33 at 1 kHz) with a similar level of tangent losses. This result is due to the local field enhancement in the regions close to the filler-PVDF interfaces which are additionally intensified by the presence of silver nanoparticles. The metallic addition is also beneficial for the mechanical harvesting ability of such composites: the amplitude of the maximum piezoelectric-triboelectric combined output collected in open circuit conditions increases from 0.2 V/cm(2) (PVDF) to 30 V/cm(2) for x = 27 vol.% Ag in a capacitive configuration. The role of ferroelectric and metallic nanoparticles on the increasing mechanical-electric conversion response is also been explained.