National Institute Of Materials Physics - Romania

A recent theory of band ferromagnetism in 3d metals predicts 're-entrant' ferromagnetism at temperatures far above the boiling point of these metals in normal conditions (Teodorescu, C.M., 2021. Spin asymmetry originating from densities of states: Criterion for ferromagnetism, structures and magnetic properties of 3d metals from crystal field based DOSs. Results in Physics 25, 104,241). Metals, and in particular iron rich alloys, are still solid at such extremal temperatures in the Earth's inner solid core. It follows that this piece of the Earth may become ferromagnetic. This hypothesis is investigated in this work in more details, by using densities of states derived by ab initio density functional theory calculations for hexagonal close-packed iron and applying the basic theory of band ferromagnetism derived in the above Reference. The temperature for 're-entrant' ferromagnetism increases with the pressure, ranging between about 6530 and 6640 K for pressures between 330 and 360 GPa; these temperatures are in the range of most estimates for the temperature of the inner solid core of our planet. The dimension of the ferromagnetic "innermost inner core" (IMIC) derived from the estimated Fe magnetic moment are within the dimensions of a IMIC with different anisotropy in the propagation of seismic waves. For body centered cubic Fe no 're-entrant' ferromagnetism is predicted based on the actual model. It follows that the Earth's inner solid core with hexagonal close-packed structure is the main responsible for the geomagnetic field, and also most probably the reversal of this field proceeds by simple rotation of the magnetization of this core, while keeping a non-vanishing magnetic field during the reversal. This might prevent the Earth's surface bombardment with energetic charged particles during the reversals, with beneficial effects for complex lifeforms and for mankind civilization.

Photoelectron spectromicroscopy data cubes with sub-micrometer spatial resolution from a lead zirconate titanate thin film are fitted in each spatial point for several areas investigated, and correlations between the results of the fitting parameters are established, enabling one to suggest that surface band bending manifests also in the case of samples with multiple polarization states. These surface band bendings may be used for preliminary assessment of polarization states by using the contrast in binding energy. However, the individual curve fitting of each spectrum and the analysis of correlations between the derived parameters (binding energies and amplitudes) yields results of deeper significance in deriving the distribution of band bending. This allows in some cases discriminating between the origin of the individual components, assessing charging effects and compensation mechanisms, also enabling one to establish correlations between areas with different polarization. It is found that the major part of the investigated areas consist in regions with outwards polarization and without out-of-plane polarization, with the presence of some isolated metal Pb clusters. On a single area, components attributed to inwards polarization are detected, and their formation occurs at the expense of areas without out-of-plane polarization, mostly for a given proportion of the outwards polarization.

In the present study, we developed chitosan/hyaluronan nanoparticles (CS/HY NPs) for tumor targeting with vinblastine sulfate (VBL), that can be directed to the CD44 transmembrane receptor, over-expressed in cancer cells. NPs were prepared by coating with HY-preformed chitosan/tripolyphosphate (CS/TPP) NPs, or by polyelectrolyte complexation of CS with HY. NPs with a mean hydrodynamic radius (R-H) of 110 nm, 12% polydispersity index and negative zeta potential values were obtained by a direct complexation process. Transmission Electron Microscopy (TEM) images showed spherical NPs with a non-homogeneous matrix, probably due to a random localization of CS and HY interacting chains. The intermolecular interactions occurring between CS and HY upon NPs formation were experimentally evidenced by micro-Raman (mu-Raman) spectroscopy, through the analysis of the spectral changes of characteristic vibrational bands of HY during NP formation, in order to reveal the involvement of specific chemical groups in the process. Optimized NP formulation efficiently encapsulated VBL, producing a drug sustained release for 20 h. In vitro studies demonstrated a fast internalization of labeled CS/HY NPs (within 6 h) on K-562 human myeloid leukemia cells. Pre-saturation of CD44 by free HY produced a slowing-down of NP uptake over 24 h, demonstrating the need of CD44 for the internalization of HY-based NPs.

SnO2 nanoparticles have a great potential in photocatalytic and optoelectronic applications by extending their absorbtion and emission from UV to the visible domain. The effect of annealing at 750 degrees C and 1000 degrees C for 3 h in ambient conditions on structural, optical and electrical properties of F&Zn double doped SnO2 nanoparticles synthesized by continuous wave CO2 laser pyrolysis method were investigated for the first time. X-Ray diffraction studies confirmed the expected crystallite size increasing and also the vanishing of divalent tin phases (SnF2, SnO) upon air annealing. Detailed X ray photoelectron spectroscopy (XPS) analysis confirmed that fluorine disappears completely from SnO2 structure at 1000 degrees C. The annealing also induced a reduction in oxygen vacancies as confirmed by Raman spectroscopy and XPS. Transmission FTIR spectroscopy was used for revealing the existence of Sn-O, O-Sn-O, O-H and H-O-H vibrational modes. The optical band gap energies of all annealed samples are in the visible region, decreasing for those that were initially doped with F, and increasing for the only Zn doped sample. Photoluminescence (PL) measurements showed a broad dominant peak in green visible region, around 530 nm. For the sample with the highest content of Zn, PL spectrum shifted to higher wavelengths, respectively to the orange and red regions. The oxygen vacancies concentrations after annealing are correlated with the electrical conductivity of F, F&Zn, and Zn doped SnO2 samples.

Li-ion batteries, widely used in portable electronics, electric vehicles, and energy storage systems, are an integral element of our daily life. However, the limitation of lithium sources, which leads to high prices, prompts the search for alternatives. Recently there has been noticed a rapid interest in Na-ion batteries technology. Especially, suitable cathode structures are investigated to accumulate larger sodium ions. In this paper, the high entropy layered oxide NaMn0.2Fe0.2Co0.2Ni0.2Ti0.2O2 is presented which achieves superior electrochemical properties with a stable capacity of ca. 180 mAh g(-1). The understanding of its high performance is based on a complex study of the multiphase intercalation mechanism. The combination of advanced structural analysis by XAS, in situ XRD, TEM, and computational DFT modelling gives a new concept on the nature of O3-P3 structure reorganization. The presented experimental and theoretical evidence indicates that the P3 phase of layered oxides is energetically favourable for a lower sodium content for specific transition metal-oxide pair distance. Fundamental understanding of the nature of phase transformation is crucial for tailoring structural composition, where the desirable O3-P3 reorganization will occur, resulting in achieving high-performance cathodes.

The synthesis and characterization of novel ionic liquid crystals based on pyridinium salts with Br- and PF6- counterions are described in this work. These pyridinium salts were derived from 4-hydroxypyridine, both by N- and O-alkylation. The 3,4,5-tri(alkyloxy)-benzyl mesogenic unit was attached to the nitrogen atom of the pyridinium ring. Alkyl chains with a different number of carbon atoms (6, 8, 10, 12 and 14) were employed in order to show the effect on the stability of mesophase. The POM (polarizing optical microscopy) and XRD (powder X-ray diffraction) studies indicated that bromide salts with shorter chains C-6, C-8 and C-10 do not show mesomorphic properties, while longer chain analogues with C-12 and C-14 exhibit two enantiotropic columnar phases. Surprisingly, the pyridinium salts with the larger size PF6- counterion do not exhibit liquid crystal properties.

The use of resorbable magnesium alloys in the design of implants represents a new direction in the healthcare domain. Two main research avenues are currently explored for developing or improving metallic biomaterials: (i) increase of their corrosion resistance by designed compositional and structural modifications, and (ii) functionalization of their surfaces by coating with ceramic or polymeric layers. The main objective of this work was to comparatively assess bio-functional coatings (i.e., highly-crystallized hydroxyapatite and silica-rich glass) deposited by radio-frequency magnetron sputtering (RF-MS) on a biodegradable Mg-0.8Ca alloy (0.8 wt.% of Ca). After probing their morphology (by scanning electron microscopy) and structure (by Fourier transform infrared spectroscopy and grazing incidence X-ray diffraction), the corrosion resistance of the RF-MS coated Mg-0.8Ca substrates was electrochemically tested (in synthetic biological media with different degrees of biomimicry), and their cytocompatibility was assessed in osteoblast and fibroblast cell cultures. By collective assessment, the most promising performances, in terms of mass loss (similar to 7% after 12 days), hydrogen release rate (similar to 6 mL/cm(2) after 12 days), electrochemical corrosion parameters and cytocompatibility, were obtained for the crystalline HA coating.

TiO2-based mixed oxide-carbon composite supports have been suggested to provide enhanced stability for platinum (Pt) electrocatalysts in polymer electrolyte membrane (PEM) fuel cells. The addition of molybdenum (Mo) to the mixed oxide is known to increase the CO tolerance of the electrocatalyst. In this work Pt catalysts, supported on Ti1-xMoxO2-C composites with a 25/75 oxide/carbon mass ratio and prepared from different carbon materials (C: Vulcan XC-72, unmodified and functionalized Black Pearls 2000), were compared in the hydrogen oxidation reaction (HOR) and in the oxygen reduction reaction (ORR) with a commercial Pt/C reference catalyst in order to assess the influence of the support on the electrocatalytic behavior. Our aim was to perform electrochemical studies in preparation for fuel cell tests. The ORR kinetic parameters from the Koutecky-Levich plot suggested a four-electron transfer per oxygen molecule, resulting in H2O. The similarity between the Tafel slopes suggested the same reaction mechanism for electrocatalysts supported by these composites. The HOR activity of the composite-supported electrocatalysts was independent of the type of carbonaceous material. A noticeable difference in the stability of the catalysts appeared only after 5000 polarization cycles; the Black Pearl-containing sample showed the highest stability.

In recent years, iron oxides-based nanostructured composite materials are of particular interest for the preparation of multifunctional thin films and membranes to be used in sustainable magnetic field adsorption and photocatalysis processes, intelligent coatings, and packing or bio-medical applications. In this paper, superparamagnetic iron oxide (core)-silica (shell) nanoparticles suitable for thin films and membrane functionalization were obtained by co-precipitation and ultrasonic-assisted sol-gel methods. The comparative/combined effect of the magnetic core co-precipitation temperature (80 and 95 degrees C) and ZnO-doping of the silica shell on the photocatalytic and nano-sorption properties of the resulted composite nanoparticles were investigated by ultraviolet-visible (UV-VIS) spectroscopy monitoring the discoloration of methylene blue (MB) solution under ultraviolet (UV) irradiation and darkness, respectively. The morphology, structure, textural, and magnetic parameters of the investigated powders were evidenced by scanning electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy, Brunauer-Emmett-Teller (BET) measurements, and saturation magnetization (vibrating sample magnetometry, VSM). The intraparticle diffusion model controlled the MB adsorption. The pseudo- and second-order kinetics described the MB photodegradation. When using SiO2-shell functionalized nanoparticles, the adsorption and photodegradation constant rates are three-four times higher than for using starting core iron oxide nanoparticles. The obtained magnetic nanoparticles (MNPs) were tested for films deposition.