National Institute Of Materials Physics - Romania

NiO-sensitive materials have been synthesized via the hydrothermal synthesis route and calcined in air at 400 degrees C and, alternatively, at 500 degrees C. Structural, morphological, and spectroscopic investigations were involved. As such, the XRD patterns showed a higher crystallinity degree for the NiO calcined at 500 degrees C. Such an aspect is in line with the XPS data indicating a lower surface hydroxylation relative to NiO calcined at 400 degrees C. An HRTEM microstructural investigation revealed that the two samples differ essentially at the morphological level, having different sizes of the crystalline nanoparticles, different density of the surface defects, and preferential faceting according to the main crystallographic planes. In order to identify their specific gas-sensing mechanism towards CO exposure under the in-field atmosphere, the simultaneous evaluation of the electrical resistance and contact potential difference was carried out. The results allowed the decoupling of the water physisorption from the chemisorption of the ambient oxygen species. Thus, the specific CO interaction mechanism induced by the calcination temperature of NiO has been highlighted.

In this study curcumin was immobilized in a silica matrix to overcome its poor aqueous solubility and rapid degradation profile. Two kinds of sol-gel powders based on colloidal silica were synthesized and characterized, one prepared with an ethanolic solution of curcumin and the other using cethyltrimethylammonium bromide (CTAB) to solubilize the dye. The successful integration of curcumin in the matrix as well as the interaction with the components of the composite powders was validated by different analysis methods (DSC, FTIR). The samples morphology was evaluated by SEM. UV-Vis and fluorescence studies showed that curcumin was stable, in its enol configuration in both matrices. The sensitivity to ammonia was proved by exposing the powders to NH3 vapors in a sealed vessel. Color changes were measured with a colorimeter. UV-Vis spectra showed that the enol form of the dye in EtOH/CTAB based SiO2 matrices was energetically stable under NH3 atmosphere, even after being kept a few days at low temperature. A fluorescence quenching of both samples was noticed due to interaction curcumin-ammonia. Both samples have antimicrobial properties, the CTAB containing one being more efficient. The EtOH/CTAB based SiO2 powders may represent a novel signaling and antimicrobial system, useful for food or pharmaceutical applications. [GRAPHICS] .

For high-field power applications of high-temperature superconductors, it became obvious in recent years that nano-engineered artificial pinning centers are needed for increasing the critical current and pinning potential. As opposed to the artificial pinning centers obtained by irradiation with various particles, which is a quite expensive approach, we have studied superconducting samples having self-assembled defects, created during the sample fabrication, that act as effective pinning centers. We introduced a simple, straight-forward method of estimating the frequency-dependent critical current density by using frequency-dependent AC susceptibility measurements, in fixed temperatures and DC magnetic fields, from the positions of the maxima in the dependence of the out-of-phase susceptibility on the amplitude of AC excitation magnetic field. The results are compatible with a model that stipulates a logarithmic dependence of the pinning potential on the probing current. A mathematical derivation allowed us to estimate from the experimental data the pinning potentials in various samples, and in various DC magnetic fields. The resulted values indicate large pinning potentials, leading to very small probability of magnetic flux escaping the pinning wells, hence, leading to very high critical currents in high magnetic fields.

In the present work, the effectiveness of vacuum deposition technique for obtaining composite thin films based on chitosan-coated magnesium-doped hydroxyapatite Ca10-xMgx(PO4)(6) (OH)(2) with x(Mg) = 0.025 (MgHApCh) was proved for the first time. The prepared samples were exposed to three doses (0, 3, and 6 Gy) of gamma irradiation. The MgHApCh composite thin films nonirradiated and irradiated were evaluated by scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) studies. The biological evaluation of the samples was also presented. All the results obtained from this study showed that the vacuum deposition method allowed for obtaining uniform and homogeneous layers. Fine cracks were observed on the MgHApCh composite thin films' surface after exposure to a 6 Gy irradiation dose. Additionally, after gamma irradiation, a decrease in Ca, P, and Mg content was noticed. The MgHApCh composite thin films with doses of 0 and 3 Gy of gamma irradiation showed a cellular viability similar to that of the control. Samples with 6 Gy doses of gamma irradiation did not cause significantly higher fibroblast cell death than the control (p > 0.05). On the other hand, the homogeneous distribution of pores that appeared on the surface of coatings after 6 Gy doses of gamma irradiation did not prevent the adhesion of fibroblast cells and their spread on the coatings. In conclusion, we could say that the thin films could be suitable both for use in bone implants and for other orthopedic and dentistry applications.

Iron-oxide-doped polyaniline (PANI-IO) thin films were obtained by the polymerization of aniline monomers and iron oxide solutions in direct current glow discharge plasma in the absence of a buffer gas for the first time. The PANI-IO thin films were deposited on optical polished Si wafers in order to study surface morphology and evaluate their in vitro biocompatibility. The characterization of the coatings was accomplished using scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), atomic force microscopy (AFM), metallographic microscopy (MM), and X-ray photoelectron spectroscopy (XPS). In vitro biocompatibility assessments were also conducted on the PANI-IO thin films. It was observed that a uniform distribution of iron oxide particles inside the PANI layers was obtained. The constituent elements of the coatings were uniformly distributed. The Fe-O bonds were associated with magnetite in the XPS studies. The surface morphology of the PANI-IO thin films was assessed by atomic force microscopy (AFM). The AFM topographies revealed that PANI-IO exhibited the morphology of a uniformly distributed and continuous layer. The viability of Caco-2 cells cultured on the Si substrate and PANI-IO coating was not significantly modified compared to control cells. Moreover, after 24 h of incubation, we observed no increase in LDH activity in media in comparison to the control. In addition, our results revealed that the NO levels for the Si substrate and PANI-IO coating were similar to those found in the control sample.

An original photodetector system based on self-connected CuO-ZnO radial core-shell heterojunction nanowire arrays grown on metallic interdigitated electrodes, operating as visible-light photodetector was developed by combining simple preparation approaches. Metallic interdigitated electrodes were fabricated on Si/SiO2 substrates using a conventional photolithography process. Subsequently, a Cu layer was electrodeposited on top of the metallic interdigitated electrodes. The CuO nanowire arrays (core) were obtained by thermal oxidation in air of the Cu layer. Afterwards, a ZnO thin film (shell) was deposited by RF magnetron sputtering covering the surface of the CuO nanowires. The morphological, structural, compositional, optical, electrical and photoelectrical properties of the CuO nanowire arrays and CuO-ZnO core-shell nanowire arrays grown on metallic interdigitated electrodes were investigated. The performances of the devices were evaluated by assessing the figures of merit of the photodetectors based on self-connected CuO-ZnO core-shell heterojunction nanowire arrays grown on the metallic interdigitated electrodes. The radial p-n heterojunction formed between CuO and ZnO generates a type II band alignment that favors an efficient charge separation of photogenerated electron-hole pairs at the CuO-ZnO interface, suppressing their recombination and consequently enhancing the photoresponse and the photoresponsivity of the photodetectors. The electrical connections in the fabricated photodetector devices are made without any additional complex and time-consuming lithographic step through a self-connecting approach for CuO-ZnO core-shell heterojunction nanowire arrays grown directly onto the Ti/Pt metallic interdigitated electrodes. Therefore, the present study provides an accessible path for employing low dimensional complex structures in functional optoelectronic devices such as photodetectors.

The present study aimed to assess the feasibility of developing low-cost multipurpose iron oxide/TiO2 nanocomposites (NCs) for use in combined antitumor therapies and water treatment applications. Larger size (approximate to 100 nm) iron oxide nanoparticles (IONPs) formed magnetic core-TiO2 shell structures at high Fe/Ti ratios and solid dispersions of IONPs embedded in TiO2 matrices when the Fe/Ti ratio was low. When the size of the iron phase was comparable to the size of the crystallized TiO2 nanoparticles (approximate to 10 nm), the obtained nanocomposites consisted of randomly mixed aggregates of TiO2 and IONPs. The best inductive heating and ROS photogeneration properties were shown by the NCs synthesized at 400 degrees C which contained the minimum amount of alpha-Fe2O3 and sufficiently crystallized anatase TiO2. Their cytocompatibility was assessed on cultured human and murine fibroblast cells and analyzed in relation to the adsorption of bovine serum albumin from the culture medium onto their surface. The tested nanocomposites showed excellent cytocompatibility to human fibroblast cells. The results also indicated that the environment (i.e. phosphate buffer or culture medium) used to disperse the nanomaterials prior to performing the viability tests can have a significant impact on their cytotoxicity.

The electronic structure as well as the mechanism underlying the high-mobility two-dimensional electron gases (2DEGs) at complex oxide interfaces remain elusive. Herein, using soft X-ray angle-resolved photoemission spectroscopy (ARPES), we present the band dispersion of metallic states at buffered LaAlO3/SrTiO3 (LAO/STO) heterointerfaces where a single-unit-cell LaMnO3 (LMO) spacer not only enhances the electron mobility but also renders the electronic structure robust toward X-ray radiation. By tracing the evolution of band dispersion, orbital occupation, and electron-phonon interaction of the interfacial 2DEG, we find unambiguous evidence that the insertion of the LMO buffer strongly suppresses both the formation of oxygen vacancies as well as the electron-phonon interaction on the STO side. The latter effect makes the buffered sample different from any other STO-based interfaces and may explain the maximum mobility enhancement achieved at buffered oxide interfaces.

The research efforts focused on the implementation of Heusler materials into spintronic heterostructures triggered the investigations on the half-metallic and magnetic properties on Zr2CrAl ferrimagnetic com-pound.The theoretical investigations based on Density Functional Theory were performed on the tetragonal,orthorhombic and rhombohedral distortions of the typical inverse-Heusler cubic crystalline structure, previously reported. The compound exhibits half-metallic characteristics for all deformations considered. The slight variations in volume of the unit cell do not destroy the high spin polarization state.The band gap from minority spin channel slightly decreases in orthorhombic and rhombohedral deformations.The total magnetic moment calculated per formula unit is integer (equal to 1(mu B)/f.u.) and follows the Slater-Pauling rule for all cases investigated. The antiferromagnetic coupling between the Zr and Cratoms was preserved. The functionality of ferrimagnetic full-Heusler alloys to be used as overlayers in the production of epitaxially deposited heterostructures on substrates with crystalline structures other than cubic was proven. (C) 2021 Elsevier B.V. All rights reserved.

The concentration of thyroxine hormone is linked to a large variety of medical conditions, where the best therapy is hormone substitution, through administration of levothyroxine (LT4) medication. Herewith, the detection of these biomolecules still lacks a simple, reliable tool, such as label-free sensors.In this work, the performances of commercial screen-printed carbon electrodes, containing different nanostructured materials (carbon nanotubes, graphene, and gold nanoparticles), used as sensors for LT4 detection, were described and compared. Electrochemical methods were used for the characterization of the nanostructure-based sensors. Several optimization steps were undertaken to achieve optimum performances for selective LT4 quantification. The redox behaviour of LT4 at sensors surface together with the interfacial changes, which occur due to the interaction between nanostructures and LT4, were studied by electrochemical impedance spectroscopy (EIS) and cyclic voltammetry (CV). Differential pulse voltammetry (DPV) was used for LT4 detection, where best performances were obtained in the presence of carbon nanotubes, with a detection limit of 30 nM.