National Institute Of Materials Physics - Romania

In this study, we report on the synthesis of L-Cysteine (L-Cys)-coated magnetic iron oxide nanoparticles (NPs) loaded with doxorubicin (Dox). The Fe3O4-L-Cys-Dox NPs were extensively characterized for their compositional and morpho-structural features using EDS, SAED, XRD, FTIR and TEM. XPS, Mossbauer spectroscopy and SQUID measurements were also performed to determine the electronic and magnetic properties of the Fe3O4-L-Cys-Dox nanoparticles. Moreover, by means of a FO-SPR sensor, we evidenced and confirmed the binding of Dox to L-Cys. Biological tests on mouse (B16F10) and human (A375) metastatic melanoma cells evidenced the internalization of magnetic nanoparticles delivering Dox. Half maximum inhibitory concentration IC50 values of Fe3O4-L-Cys-Dox were determined for both cell lines: 4.26 mu g/mL for A375 and 2.74 mu g/mL for B16F10, as compared to 60.74 and 98.75 mu g/mL, respectively, for unloaded controls. Incubation of cells with Fe3O4-L-Cys-Dox modulated MAPK signaling pathway activity 3 h post-treatment and produced cell cycle arrest and increased apoptosis by 48 h. We show that within the first 2 h of incubation in physiological (pH = 7.4) media, similar to 10-15 mu M Dox/h was released from a 200 mu g/mL Fe3O4-L-Cys-Dox solution, as compared to double upon incubation in citrate solution (pH = 3), which resembles acidic environment conditions. Our results highlight the potential of Fe3O4-L-Cys-Dox NPs as efficient drug delivery vehicles in melanoma therapy.

A novel electrochemical biosensor was developed to monitor fibroblast cells stress levels for the first time in situ under external stimuli based on the recognition of superoxide anion released upon cell damage. The biosensor comprised metallized polycaprolactone electrospun fibers covered with zinc oxide for improved cell adhesion and signal transduction, whilst stable bioconjugates of mercaptobenzoic acid-functionalized gold nanoparticles/ superoxide dismutase were employed as recognition bioelements. Biosensors were first tested and optimized for in situ generated superoxide detection by fixed potential amperometry at +0.3 V, with minimal interferences from electroactive species in cell culture media. L929 fibroblast cells were then implanted on the optimized biosensor surface and the biosensor morphologically characterized by scanning electron microscopy (SEM) and fluorescence microscopy, which illustrated the network-type pattern of fibroblasts adjacent to the fiber scaffold. Fibroblast stress was induced by zymosan and monitored at the cells integrated biosensor using fixed potential amperometry (CA) with a sensitivity of 26 nA cm-2 mu g mL-1 zymosan and electrochemical impedance spectros-copy (EIS), with similar sensitivity of the biosensor considering the Rs and Z' parameters of around 0.13 omega cm2 mu g-1 mL and high correlation factors R2 of 0.9994. The obtained results underline the applicability of the here developed biosensor for the electrochemical screening of the fibroblast cells stress. The concept in using low-cost biocompatible polymeric fibers as versatile scaffolds for both enzyme immobilization and cell adhesion, opens a new path in developing biosensors for the in-situ investigation of a variety of cellular events.

The microscopic mechanism of the occurrence of ferroelectric properties in M-type barium hexaferrites is investigated by experimental and first-principle computation methods. The analysis of magnetic, X-ray, and Mossbauer measurements of BaFe12O19 samples ascertains the correlation between the thermal factor in the process of annealing samples and their functional properties. The occurrence of the remnant polarization in barium hexaferrites at room temperature contradicts the description of their crystal structure in the fra-mework of centrosymmetric space group P63/mmc (No. 194), in which one of the symmetry operations is inversion center. Therefore, the crystal structure of BaFe12O19 was analyzed in the frameworks of SG P63/mmc (No. 194) and non-centrosymmetric SG P63mc (No. 186). The computed value of polarization for a non-centrosymmetric unit cell is similar to 3.5 mu C/cm2. The analysis of polarization was carried out on a path connecting the polar P63mc and non-polar P63/mmc structures and considered in terms of the total energy barrier. Our result allows ascertaining a direct relationship between the remnant polarization of the unit cell and the broken spatial-inversion symmetry in the crystal structure of M-type barium hexaferrite.(c) 2022 Elsevier B.V. All rights reserved.

In this study, we report the performance improvement of wound dressings by covering them with magnetite-based nanostructured coatings. The magnetite nanoparticles (Fe3O4 NPs) were functionalized with Nigella sativa (N. sativa) powder/essential oil and dicloxacillin and were synthesized as coatings by matrix assisted pulsed laser evaporation (MAPLE). The expected effects of this combination of materials are: (i) to reduce microbial contamination, and (ii) to promote rapid wound healing. The crystalline nature of core/shell Fe3O4 NPs and coatings was determined by X-ray diffraction (XRD). Differential Scanning Calorimetry (DSC) and Thermo Gravimetric Analysis (TGA) have been coupled to investigate the stability and thermal degradation of core/shell nanoparticle components. The coatings' morphology was examined by scanning electron microscopy (SEM). The distribution of chemical elements and functional groups in the resulting coatings was evidenced by Fourier transform infrared (FTIR) spectrometry. In order to simulate the interaction between wound dressings and epithelial tissues and to evaluate the drug release in time, the samples were immersed in simulated body fluid (SBF) and investigated after different durations of time. The antimicrobial effect was evaluated in planktonic (free-floating) and attached (biofilms) bacteria models. The biocompatibility and regenerative properties of the nanostructured coatings were evaluated in vitro, at cellular, biochemical, and the molecular level. The obtained results show that magnetite-based nanostructured coatings functionalized with N. sativa and dicloxacillin are biocompatible and show an enhanced antimicrobial effect against Gram positive and Gram negative opportunistic bacteria.

Drinking water contamination has become a worldwide problem due to the highly negative effects that pollutants can have on human organisms and the environment. Hydroxyapatite (HAp) has the appropriate properties for the immobilization of various pollutants, being considered amongst the most cost-effective materials for water decontamination. The main objective of this study was to use synthesized hydroxyapatite for the elimination of Sr2+ ions from contaminated solutions. The hydroxyapatite used in the decontamination process was synthesized in the laboratory using an adapted method. The hydroxyapatite powder (HAp) resulting from the synthesis was analyzed both before and after the elimination of Sr2+ ions from contaminated solutions. The efficiency of the HAp nanoparticles in removing Sr2+ ions from contaminated solution was determined by batch adsorption experiments. X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) were used to study the HAp samples before and after the removal of Sr2+ ions. The ability of HAp nanoparticles to eliminate strontium ions from contaminated solutions was established. Moreover, the removal of Sr2+ ions from the contaminated aqueous solutions was highlighted by ultrasound measurements. The value of the stability parameter calculated by ultrasonic measurements after the removal of Sr2+ ions from the contaminated solution was similar to that of double distilled water whose stability was used as reference. The outcomes of the batch experiments and the parameters obtained from Langmuir and Freundlich models indicated that the HAp nanoparticles had a strong affinity for the elimination of Sr2+ ions from polluted solutions. These results emphasized that HAp nanoparticles could be excellent candidates in the development of new technologies for water remediation. More than that, the outcomes of the cytotoxic assays proved that HAp nanoparticles did not induce any noticeable harmful effects against HeLa cells and did not affect their proliferation after 1 day and 7 days of incubation.

In our work, the kinetics of martensitic transformations and the influence of thermal treatments on martensitic transformations, as well as the related magnetic properties of the Ni49Mn32Ga19 ferromagnetic shape memory melt-spun ribbons, have been investigated. Thermal treatments at 673 K for 1, 4 and 8 h can be considered an instrument for fine-tuning the performance parameters of alloys. One-hour thermal treatments promote an improvement in the crystallinity of these otherwise highly textured ribbons, reducing internal defects and stress induced by the melt-spinning technique. Longer thermal treatments induce an important magnetization rise concomitantly with a slight and continuous increase in martensitic temperatures and transformation enthalpy. The activation energy, evaluated from differential scanning calorimeter experimental data with a Friedman model, significantly increases after thermal treatments as a result of the multi-phase coexistence and stabilization of the non-modulated martensitic phase, which increases the reverse martensitic transformation hindrance.

The p-n junctions are the building blocks of nowadays electronic devices. The n- or p-type conductivity is obtained in classic semiconductors, like Si, by doping with atoms acting as donors or acceptors, respectively. Doping was used in ferroelectrics to influence the transition temperature, magnitude of some physical properties, but not necessarily conduction type. Therefore, comprehensive studies to obtain true ferroelectric p-n junctions by controlled doping are missing. Recently, it has been shown that Pb(Zr0.2Ti0.8)O-3 films doped with & AP;1% atomic Nb (n-type doping) or Fe (p-type doping) have different orientations of polarization in the as-grown state. Knowing that polarization orientation depends on doping type, the next step is to build ferroelectric p-n homojunctions and to study their properties in relation to ferroelectric polarization. p-n and n-p structures were grown for this purpose by successive deposition of Nb-doped and Fe-doped Pb(Zr,Ti)O-3 layers with different thicknesses. We find that these p-n homojunctions are ferroelectric, but the magnitude of the polarization and coercive field, as well as the dominant polarization orientation in the as-grown state, depend on the conduction type of the first grown layer. The I-V characteristics are quasi-linear, although the interfaces with the electrodes behaves as Schottky contacts. The resistance extracted from the I-V characteristics displays an exponential dependence on temperature, with an activation energy in the range of 0.14-0.17 eV. These results are explained assuming that the total current in the junction is the total of electron and hole injections at the electrode interfaces. It is shown that for relatively low doping concentrations, the current density contains a dominant term with a linear voltage dependence and an exponential temperature dependence, as observed experimentally, and a secondary (correction) term that is dependent on the free carrier density and can induce non-linear voltage dependence when this density is significant.

Glassy nanocomposites containing Yb3+/Er3+-doped GdF3 and LiGdF4 nanocrystals have been prepared by controlled crystallization of the xerogel and the structural, up-conversion luminescence, and magnetic properties were analyzed and discussed. Structural and morphological analysis showed uniform distribution of both GdF3 and LiGdF4 nanocrystals (tens of nm size), embedded in silica glass matrix as the result of thermal decomposition of the trifluoracetates, revealed as a strong exothermic peak at about 300 degrees C; the Li-ions co-doping showed a strong influence on the GdF3 and LiGdF4 nanocrystalline fraction. The energy dispersive spectrometry mapping showed Gd, F and Yb, Er within the nanocrystals but not in the silica glass matrix. X-ray diffraction pattern analysis indicated the crystalline lattice distortion consistent with the Yb/Er incorporation in both fluoride nanocrystals. The "green" ((H-2(11/2), S-4(3/2)) -> I-4(15/2)) and "red" (F-4(9/2)-> I-4(15/2)) up-conversion luminescences at 525, 545, and 660 nm observed under 980 nm laser light pumping were assigned to the Er3+ ions deexcitation through a two-photon process. The magnetic properties of the nanocomposite are strongly temperature dependent. The magnetization hysteresis loops show a ferromagnetic behavior at low temperatures (5K) related to the rare-earth ions contribution and the saturation magnetization of 39 emu/g. At 300 K a paramagnetic behavior was observed that was ascribed to the non-interacting localized nature of the magnetic moment of the rare-earth ions. Hence, such novel, multifunctional magnetic and optical materials can allow the intertwining between magnetism and photonics and might offer new opportunities for new magneto-optical device development.

Pb(Zr,Ti)O-3 (PZT) is the most common ferroelectric (FE) material widely used in solid-state technology. Despite intense studies of PZT over decades, its intrinsic band structure, electron energy depending on 3D momentum k, is still unknown. Here, Pb(Zr0.2Ti0.8)O-3 using soft-X-ray angle-resolved photoelectron spectroscopy (ARPES) is explored. The enhanced photoelectron escape depth in this photon energy range allows sharp intrinsic definition of the out-of-plane momentum k and thereby of the full 3D band structure. Furthermore, the problem of sample charging due to the inherently insulating nature of PZT is solved by using thin-film PZT samples, where a thickness-induced self-doping results in their heavy doping. For the first time, the soft-X-ray ARPES experiments deliver the intrinsic 3D band structure of PZT as well as the FE-polarization dependent electrostatic potential profile across the PZT film deposited on SrTiO3 and LaxSrMn1-xO3 substrates. The negative charges near the surface, required to stabilize the FE state pointing away from the sample (P+), are identified as oxygen vacancies creating localized in-gap states below the Fermi energy. For the opposite polarization state (P-), the positive charges near the surface are identified as cation vacancies resulting from non-ideal stoichiometry of the PZT film as deduced from quantitative XPS measurements.

We present the multifrequency measurements of the surface resistance of spark-plasma-sintered MgB2 performed through a dielectric loaded resonator operating at 16.5 and 26.7 GHz. By normally applying magnetic fields <= 1.2 T to the sample surface, we drove it in the mixed state. By means of data-rooted analysis, we found that the sample vortex dynamics could be fully described within a single-component approach. Pinning phenomena were present and characterized by a depinning frequency smaller than the measurement ones. The multiband nature of the superconductor emerged in the flux-flow resistivity, whose field dependence could be interpreted well within theoretical models. By exploiting them, the upper critical field was extracted in the low-temperature range, which exhibited a consistent temperature trend with the values obtained at the onset of the resistive transition near Tc, and was well in line with literature data on other polycrystalline samples.