Publications

Magnetic imaging of superconductors typically requires a soft-magnetic material placed on top of the superconductor to probe local magnetic fields. For reasonable results the influence of the magnet onto the superconductor has to be small. Thin YBCO films with soft-magnetic coatings are investigated using SQUID magnetometry. Detailed measurements of the magnetic moment as a function of temperature, magnetic field and time have been performed for different heterostructures. It is found that the modification of the superconducting transport in these heterostructures strongly depends on the magnetic and structural properties of the soft-magnetic material. This effect is especially pronounced for an inhomogeneous coating consisting of ferromagnetic nanoparticles.

The present paper reports the dependence of structural and functional properties on the porosity level with values down to 50% in BaTiO3 ceramics. Micro-porosity (pore size below 15 pm) with (0-3) connectivity has been produced by using dried pollen particles as sacrificial template. The properties of such porous ceramics are mostly affected by porosity, but also by possible small doping with foreign ions resulted from the template and by small variations of Ba/Ti stoichiometry at the ceramic-pore interfaces, as observed by a shift of the Curie temperature towards lower values when porosity level increases. The dielectric relaxation evidenced a few processes characterised by different activation energies which seem to be not affected by porosity, i.e. they might be assigned to the ceramic part and not to the ceramic-pore interfaces. When increasing porosity, a regular tilting of P(E) loops and increasing of coercivity and reducing polarization were observed, as result of reduction of active ferroelectric component and to the field inhomogeneity in such ceramics.

Magnetic iron oxides have been used in biomedical applications, such as contrast agents for magnetic resonance imaging, carriers for controlled drug delivery and immunoassays, or magnetic hyperthermia for the past 40 years. Our aim is to investigate the effect of pressure and temperature on the structural, thermal, and magnetic properties of iron oxides prepared by hydrothermal synthesis at temperatures of 100-200 degrees C and pressures of 20-1000 bar. It has been found that pressure influences the type of iron oxide crystalline phase. Thus, the results obtained by Mossbauer characterization are in excellent agreement with X-ray diffraction and optical microscopy characterization, showing that, for lower pressure values (100 bar, the major crystalline phase is goethite. In addition, thermal analysis results are consistent with particle size analysis by X-ray diffraction, confirming the crystallization of the synthesized iron oxides. One order of magnitude higher magnetization has been obtained for sample synthesized at 1000 bar. The same sample provides after annealing treatment, the highest amount of good quality magnetite leading to a magnetization at saturation of 30 emu/g and a coercive field of 1000 Oe at 10 K and 450 Oe at 300 K, convenient for various applications.

A study on clay mineral polymer nanocomposites (CPN), namely polyaniline/montmorillonite-cetyltrimethylammonium bromide (PANI/Mt-CTAB), poly o-anisidine/montmorillonite-cetyltrimethylammonium bromide (poly(o-ANIS)/Mt-CTAB) and poly o-anisidine-co-aniline/montmorillonite-cetyltrimethylammonium bromide (poly(o-ANIS-co-ANI)/Mt-CTAB), synthesized by oxidative chemical polymerization method is presented. The nanocomposites have been characterized by Fourier transform infrared spectroscopy, UV-vis spectroscopy, and cyclic voltammetry, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, cyclic voltammetry and thermogravimetry and differential scanning calorimetry analysis. By UV-vis measurements different electronic transitions for the CPNs were pointed out. The voltammograms indicate that the synthetized materials are electroactive. The FTIR analysis reveals the characteristic bands of the polymers and of the Mt-CTAB. The shift of the bands to higher/lower wavenumbers demonstrate the interaction between the pristine polymers macromolecular chains and the montmorillonite (Mt). The intercalation of the polymers inside the mineral clay was confirmed by the increased interlayer distance connected with the position of the 011 diffraction plane of the Mt., and the intercalation and exfoliation states were highlighted in the scanning and transmission electron microscopy images. The obtained results are encouraging in respect with the purpose to use them in the field of photovoltaic applications.

Thin nanostructured films are the state-of-the-art materials for detection of very low limits of toxic gases. The work presents a comparison between the properties of WO3 thin films obtained by two different deposition techniques: Advanced Gas Deposition (AGD) and DC Reactive Sputtering. Films have been characterized by XRD, SEM and XPS. WO3-based sensors have selective sensitivity in H2S detection at operating temperature of 200 degrees C and relative humidity specific to field applications. The potential interferences with CO2, SO2 and NH3 are negligible, highlighting the application potential of WO3.

Dense samples (94-96%) with starting composition (MgB2)(0.99)(X-acac)(0.01) (X-acac denotes Ga or In acetylacetonate) were obtained by spark plasma sintering. The resulting material is a superconducting composite, where carbon substitutes for boron in the crystal structure of MgB2. Added samples show enhanced critical current density at high magnetic fields and this is reflected in high values of irreversibility field (H-irr) at temperatures below 25 K when compared to a pristine sample. More efficient is In-acac addition and it promotes a H-irr of similar to 12.4T (100 A/cm(2) criterion) at 5 K. Carbon substitution for boron in the crystal structure of MgB2 has a strong influence on the pinning force and its related parameters and promotes in the added samples a grain boundary pinning mechanism as the dominant one, whereas the pristine sample with a low amount of carbon shows a major mechanism of point pinning type. However, our analysis indicates on the synergetic effects of the carbon substituting for boron and of the microstructural details on pinning and critical current density. The result strongly emphasizes the significantly different behavior of the additive during processing of the MgB2 samples, although thermal analysis experiments on both additives show very similar decomposition patterns. (C) 2020 The Authors. Published by Elsevier B.V.

The 1600 nm-extended SWIR photoresponse of SiGe/TiO2 multilayers with Ge-rich SiGe nanocrystals (NCs) is demonstrated. The SiGe NCs based multilayers are obtained by magnetron sputtering deposition of TiO2/ 6x(Ge/SiGe/Ge/TiO2) layers on heated p-Si substrate followed by rapid thermal annealing (RTA). Grazing incidence X-ray diffraction and Raman spectroscopy evidence the formation of cubic Ge-rich SiGe NCs and anatase TiO2. ITO/Ge-rich SiGe NCs based multilayer /p-Si heterostructure diodes, fabricated by depositing top ITO and bottom Al contacts, show n-p behavior. Photocurrent-voltage characteristics measured at 100 K under integral light illumination of reverse biased diode present a photocurrent higher with up to 2 orders of magnitude than the dark current. Spectral photocurrent increases with bias voltage increase and presents a bandgap-related cutoff wavelength of similar to 1600 nm due to the high Ge content of SiGe NCs.

Novel lanthanidomesogens based on lanthanide nitrates carrying three 4-pyridone ligands having two alkoxy chains at the periphery were synthesized and their structure was assigned based on IR spectroscopy and elemental analysis. Their thermal stability was evaluated by TG analysis confirming that the decomposition starts at very high temperatures around 300 degrees C. The liquid crystalline properties were investigated by using a combination of techniques: polarized optical microscopy (POM) and differential scanning calorimetry (DSC) and, for selected compounds, by variable-temperature powder X-ray diffraction. The new liquid crystal display a hexagonal columnar phase (Col(h)) between 63 degrees C and 242 degrees C, depending on the length of the alkyl chain Dielectric spectroscopy on a wide frequency range was used to evaluate the dipolar relaxation processes. The emission properties of a mixture of E7 doped with a selected europium complex filled in a planar cell were investigated on changing the applied voltage, ranging from 0V up to 15V.

Behavior of some wool fabrics as such or functionalized with semiconductor nanoparticles against the photodegradation of Rhodamine B was investigated. The wool samples were commercially purchased, they were chosen to differ by the chemical nature of the yarns, by the size of the 2D texture elements and by the applied pretreatment. The samples were routinely characterized both in the original form and in the form coated with the oxide particles as well to consider the structure, the surface morphology and their changes due to dye deposition. Several techniques were routinely applied: optical microscopy, XRD, SEM, TGA, UV-Vis spectroscopy and FTIR-ATR. Data have shown that TiO2 layer has either an amorphous structure or is highly dispersed. Drops of Rhodamine B solution were deposited by sessile drop method. We have obtained optical images of the wet/colored spot during the radial wicking, collected with a usual camera. Image comparison was made by direct visualisation. The optical images of the spot on fabrics were taken immediately after the dye was applied, after the fabric was dried and afterwards, after the system illumination by UV-vis light as function of the time. The obtained final spots speak about the dye photodegradation in the studied cases.