Publications

We investigate the interlayer coupling between two thin ferromagnetic (F) films mediated by an antiferromagnetic (AF) spacer in F*/AF/F trilayers and show how it transitions between different regimes on changing the AF thickness. Employing layer-selective Kerr magnetometry and ferromagnetic-resonance techniques in a complementary manner enables us to distinguish between three functionally distinct regimes of such ferromagnetic interlayer coupling. The F layers are found to be individually and independently exchange-biased for thick FeMn spacers-the first regime of no interlayer F-F* coupling. F-F* coupling appears on decreasing the FeMn thickness below 9 nm. In this second regime found in structures with 6.0-9.0-nm-thick FeMn spacers, the interlayer coupling exists only in a finite temperature interval just below the effective Neel temperature of the spacer, which is due to magnon-mediated exchange through the thermally softened antiferromagnetic spacer, vanishing at lower temperatures. The third regime, with FeMn thinner than 4 nm, is characterized by a much stronger interlayer coupling in the entire temperature interval, which is attributed to a magnetic-proximity induced ferromagnetic exchange. These experimental results, spanning the key geometrical parameters and thermal regimes of the F*/AF/F nanostructure, complemented by a comprehensive theoretical analysis, should broaden the understanding of the interlayer exchange in magnetic multilayers and potentially be useful for applications in spin thermionics.

Photocatalytic conversion of H2O, CO2 and N-2 represents one promising approach to harvest and store solar energy, for which efficient visible light responsive semiconductors are inevitable. Often, the presence of a small amount of an additional component called a "cocatalyst", is required to synergistically enhance the performance of the photocatalyst. Tremendous efforts were made in the past to identify inexpensive materials to be used as cocatalysts, for which metal oxides (MOs) are one of the traditional choices. Among alternative categories of materials investigated, the recently discovered MXenes display enormous potential owing to their unique 2D layered structure, tuneable composition, abundant surface functionalities and superior electronic conductivity. Specifically, MOs and MXenes encompass a variety of distinct as well as analogous characteristics that allows them to be tailored to different extents. Unfortunately, a comprehensive overview covering the synthetic, structural and photocatalytic aspects of MOs and MXenes is not available as of now. Herein, we intend to summarize the progress achieved so far in these two families of materials to be used as cocatalysts for the photoconversion of H2O, CO2 and N-2. Followed by a general introduction, we briefly outline the fundamental principles and the role of cocatalysts in photocatalytic reactions. A discussion regarding the use of MOs and MXenes as cocatalysts for the conversion of H2O, CO2 and N-2 is then provided in separate sections. Critical assessment regarding structure and morphology control, surface properties and stability concerns can not only help to recognize the challenges that limit further advancement, but can also highlight the future research directions of these materials for the effective transformation of H2O, CO2 and N-2.

We reported on the sequential development of a high-operative photocatalyst with penta-component inorganic bulk heterojunction for improved charge trapping characteristics at particle-particle interfaces for enhanced solar light-driven photocatalytic degradation of active tetracycline antibiotic. Structural, morphological, optical, and electronic properties of the synthesized samples were investigated using a series of complementary char-acterization techniques, such as XRD, FE-SEM, HR-TEM, XPS, as well as hard and soft XAS in both total electron yield (TEY) and fluorescence yield (TFY). For the case of the carbon composite material, SrTiO3@NiFe2O4@-Fe0@Ni0@CNTs, a reduced crystallinity when compared to the starting support material was noticed, although this translated into a significant improvement of the morphology and the photocatalytic performance. The SrTiO3@NiFe2O4@Fe0@Ni0@CNTs fibrous photocatalyst can efficiently achieve a high-to-total degradation of tetracycline antibiotic under visible light irradiation in less than two hours, following a non-linear PFO kinetic model with an apparent reaction rate of about 0.0606 min-1 and an 98% photodegradation activity. The XPS and XAS analysis demonstrated unequivocally the appearance of nanoscale zero-valent iron (Fe0) and zero-valent nickel (Ni0) on the photocatalyst surface, which facilitates the separation of photogenerated e+ and h+ pairs, and the appearance of more active sites.

In this work, we demonstrate that solution-processed In2Se3 nanosheets exhibit exceptional selectivity and sensitivity to NO2 gas, making them a promising candidate for gas detection systems. Theoretical simulations and surface-science experiments reveal the unique surface properties of In2Se3 nanosheets, which prevent physisorption of oxygen, carbon monoxide, and carbon dioxide, making them remarkably stable towards oxidation and CO-poisoning. Moreover, we show that NO2 molecules adsorb stably on In2Se3 nanosheets, particularly on Se vacancies, even at high temperatures. The coadsorption of water further enhances NO2 sticking on the In2Se3 surface, making it an ideal material for gas sensing applications in humid and harsh environments. The fabricated In2Se3 gas sensors exhibit excellent and reversible sensing response to NO2 gas, with a limit of detection of 5 ppb at 300 degrees C, and a highly selective response to NO2 compared to other gases and volatile organic compounds. Our sensors outperform other two-dimensional (2D) semiconductors, metal oxides, and their heterostructures, thanks to the unique surface properties of In2Se3 nanosheets. Importantly, the number of layers and termination of the surface almost have no impact on the sensing performance of In2Se3, which is advantageous for practical applications. The high sensitivity, selectivity, and stability of In2Se3 nanosheets make them an exciting platform for the fabrication of high-performance gas sensors, particularly in harsh environments, such as industrial settings or outdoor monitoring. Moreover, our solution processing approach enables scalable production of the sensors. Additionally, their unique surface properties make them an attractive candidate for developing complex composite nanostructures with tailored gas sensing characteristics for various applications.

Calcium borohydride (Ca(BH4)(2)) is a complex hydride that has been less investigated compared to its lighter counterpart, magnesium borohydride. While offering slightly lower hydrogen storage capacity (11.5 wt% theoretical maximum, 9.6 wt% under actual dehydrogenation conditions), there are many improvement avenues for maximizing the reversible hydrogen storage that have been explored recently, from DFT calculations and polymorph investigations to reactive hydride composites (RHCs) and catalytic and nanosizing effects. The stability of Ca(BH4)(2), the possibility of regeneration from spent products, and the relatively mild dehydrogenation conditions make calcium borohydride an attractive compound for hydrogen storage purposes. The ionic conductivity enhancements brought about by the rich speciation of borohydride anions can extend the use of Ca(BH4)(2) to battery applications, considering the abundance of Ca relative to alkali metal borohydrides typically used for this purpose. The current work aims to review the synthetic strategies, structural considerations of various polymorphs and adducts, and hydrogen storage capacity of composites based on calcium borohydrides and related complex hydrides (mixed anions, mixed cations, additives, catalysts, etc.). Additional applications related to batteries, organic and organometallic chemistry, and catalysis have been briefly described.

The aim of this work is to highlight the influence of blends based on TiO2 nanoparticles and reduced graphene oxide (RGO) on the photodegradation of acetaminophen (AC). To this end, the catalysts of TiO2/RGO blends with RGO sheet concentrations equal 5, 10, and 20 wt. % were prepared by the solid-state interaction of the two constituents. The preferential adsorption of TiO2 particles onto the RGO sheets' surfaces via the water molecules on the TiO2 particle surface was demonstrated by FTIR spectroscopy. This adsorption process induced an increase in the disordered state of the RGO sheets in the presence of the TiO2 particles, as highlighted by Raman scattering and scanning electron microscopy (SEM). The novelty of this work lies in the demonstration that TiO2/RGO mixtures, obtained by the solid-phase interaction of the two constituents, allow an acetaminophen removal of up to 95.18% after 100 min of UV irradiation. This TiO2/RGO catalyst induced a higher photodegradation efficiency of AC than TiO2 due to the presence of RGO sheets, which acted as a capture agent for the photogenerated electrons of TiO2, hindering the electron-hole recombination. The reaction kinetics of AC aqueous solutions containing TiO2/RGO blends followed a complex first-order kinetic model. Another novelty of this work is the demonstration of the ability of PVC membranes modified with Au nanoparticles to act both as filters for the removal of TiO2/RGO blends after AC photodegradation and as potential SERS supports, which illustrate the vibrational properties of the reused catalyst. The reuse of the TiO2/RGO blends after the first cycle of AC photodegradation indicated their suitable stability during the five cycles of pharmaceutical compound photodegradation.

This study aimed to investigate the biological response induced by hydroxyapatite (HAp) and zinc-doped HAp (ZnHAp) in human gingival fibroblasts and to explore their antimicrobial activity. The ZnHAp (with xZn = 0.00 and 0.07) powders, synthesized by the sol-gel method, retained the crystallographic structure of pure HA without any modification. Elemental mapping confirmed the uniform dispersion of zinc ions in the HAp lattice. The size of crystallites was 18.67 +/- 2 nm for ZnHAp and 21.54 +/- 1 nm for HAp. The average particle size was 19.38 +/- 1 nm for ZnHAp and 22.47 +/- 1 nm for HAp. Antimicrobial studies indicated an inhibition of bacterial adherence to the inert substrate. In vitro biocompatibility was tested on various doses of HAp and ZnHAp after 24 and 72 h of exposure and revealed that cell viability decreased after 72 h starting with a dose of 31.25 mu g/mL. However, cells retained membrane integrity and no inflammatory response was induced. High doses (such as 125 mu g/mL) affected cell adhesion and the architecture of F-actin filaments, while in the presence of lower doses (such as 15.625 mu g/mL), no modifications were observed. Cell proliferation was inhibited after treatment with HAp and ZnHAp, except the dose of 15.625 mu g/mL ZnHAp at 72 h of exposure, when a slight increase was observed, proving an improvement in ZnHAp activity due to Zn doping.

The acceptor removal process is the most detrimental effect encountered in irradiated boron-doped silicon. This process is caused by a radiation-induced boron-containing donor (BCD) defect with bistable properties that are reflected in the electrical measurements performed in usual ambient laboratory conditions. In this work, the electronic properties of the BCD defect in its two different configurations (A and B) and the kinetics behind transformations are determined from the variations in the capacitance-voltage characteristics in the 243-308 K temperature range. The changes in the depletion voltage are consistent with the variations in the BCD defect concentration in the A configuration, as measured with the thermally stimulated current technique. The A & RARR;B transformation takes place in non-equilibrium conditions when free carriers in excess are injected into the device. B & RARR;A reverse transformation occurs when the non-equilibrium free carriers are removed. Energy barriers of 0.36 eV and 0.94 eV are determined for the A & RARR;B and B & RARR;A configurational transformations, respectively. The determined transformation rates indicate that the defect conversions are accompanied by electron capture for the A & RARR;B conversion and by electron emission for the B & RARR;A transformation. A configuration coordinate diagram of the BCD defect transformations is proposed.

The Cu-Y2O3 and CuCrZr-Y2O3 materials have been devised as thermal barriers in nuclear fusion reactors. It is expected that in the nuclear environments, the materials should be working on extreme conditions of irradiation. In this work the Cu-Y2O3 and CuCrZr-Y2O3 were prepared and then irradiated in order to understand the surface irradiation resistance of the material. The composites were prepared in a glove box and consolidated with spark plasma sintering. The microstructures revealed regions of Y2O3 dispersion and Y2O3 agglomerates both in the Cu matrix and in the CuCrZr. The irradiated samples did not show any surface modification indicating that the materials seem to be irradiation resistant in the present situation. The thermal conductivity values for all the samples measured are lower than pure Cu and higher than pure W, however are higher than those expected, and therefore, the application of these materials as thermal barriers is compromised.

Energy production, distribution, and storage remain paramount to a variety of applications that reflect on our daily lives, from renewable energy systems, to electric vehicles and consumer electronics. Hydrogen is the sole element promising high energy, emission-free, and sustainable energy, and metal hydrides in particular have been investigated as promising materials for this purpose. While offering the highest gravimetric and volumetric hydrogen storage capacity of all known materials, metal hydrides are plagued by some serious deficiencies, such as poor kinetics, high activation energies that lead to high operating temperatures, poor recyclability, and/or stability, while environmental considerations related to the treatment of end-of-life fuel disposal are also of concern. A strategy to overcome these limitations is offered by nanotechnology, namely embedding reactive hydride compounds in nanosized supports such as graphene. Graphene is a 2D carbon material featuring unique mechanical, thermal, and electronic properties, which all recommend its use as the support for metal hydrides. With its high surface area, excellent mechanical strength, and thermal conductivity parameters, graphene can serve as the support for simple and complex hydrides as well as RHC (reactive hydride composites), producing nanocomposites with very attractive hydrogen storage properties.