National Institute Of Materials Physics - Romania

The crystalline structure and Fe local environment in a Co-doped Ni-Fe-Ga Heusler alloy, prepared by the melt-spinning technique, were investigated by X-ray diffraction (XRD) and EXAFS at room and low temperatures. The characteristic temperatures of the austenite-martensite phase transitions were determined by differential scanning calorimetry via cooling and heating cycles of the alloy ribbons. As shown by room-temperature XRD, the austenitic phase of the alloy has the chemically ordered L2(1) Heusler structure. This was confirmed by EXAFS, although this technique was not able to conclusively distinguish between the L2(1) and B2 structures of the austenite for the analyzed alloy. The low-temperature martensitic phase and its structural evolution towards austenite with increasing temperature were studied by high-energy X-ray diffraction, which evinced the martensite modulation. However, the Fe environment could be fitted by EXAFS with the tetragonal L1(0) structure of the non-modulated martensite. This proves that the martensite modulation has structural effects on a long-range scale, without significant changes in the short-range order around the atoms. The changes in the local structure around iron on martensitic transformation were correlated with changes in the electronic structure, described by XANES spectroscopy at the Fe K edge.

In this work, synthesis and optical properties of a new composite based on poly(o-phenylenediamine) (POPD) fiber like structures, poly(vinylidene fluoride) (PVDF) spheres and double-walled carbon nanotubes (DWNTs) are reported. As increasing the PVDF weight in the mixture of the chemical polymerization reaction of o-phenylenediamine, the presence of the PVDF spheres onto the POPD fibers surface is highlighted by scanning electron microscopy (SEM). The down-shift of the Raman line from 1421 cm(-1) to 1415 cm(-1) proves the covalent functionalization of DWNTs with the POPD-PVDF blends. The changes in the absorbance of the IR bands peaked around 840, 881, 1240 and 1402 cm(-1) indicate hindrance steric effects induced of DWNTs to the POPD fiber like structures and the PVDF spheres, as a consequence of the functionalization process of carbon nanotubes with macromolecular compounds. The presence of the PVDF spheres onto the POPD fiber like structures surface induces a POPD photoluminescence (PL) quenching process. An additional PL quenching process of the POPD-PVDF blends is reported to be induced in the presence of DWNTs. The studies of anisotropic PL highlight a change of the angle of the binding of the PVDF spheres onto the POPD fiber like structures surface from 50.2 degrees to 38 degrees when the carbon nanotubes concentration increases in the POPD-PVDF/DWNTs composites mass up to 2 wt.%.

FeRAM memories constitute themselves as a robust counterpart to the mainstream NVRAM memories. Their unique properties, such as radiation resilience and low voltage operation, together with high speed writing and reading, high and long lasting remanence and very good endurance to cycling endorse them in the data storage domain. However price, poor scalability, the destructive way of reading and the necessary consequent re-writing represent technical drawbacks that diminish their practical value. This paper presents a new paradigm of completing previous efforts towards fast nondestructive reading of FeRAMs. An intermittent low intensity IR (infrared) laser diode generates a pyroelectric signal in the ferroelectric material. The amplitude and phase of this response depends on the state of polarisation of the ferroelectric. Comparing the phase of the electric response with the phase of the illuminating radiation (on/off), a decisive indication of the poling sense in the ferroelectric is given. Aiming to circumvent the notorious slowness of the pyroelectric response the array is continuously illuminated with the pulsating laser, which ensures a prompt answer from every bit of memory. The reading speed is, practically, limited by the electronics.

Achieving thermoelectric devices with high performance based on low-cost and nontoxic materials is extremely challenging. Moreover, as we move toward an Internet-of-Things society, a miniaturized local power source such as a thermoelectric generator (TEG) is desired to power increasing numbers of wireless sensors. Therefore, in this work, an all-oxide p-n junction TEG composed of low-cost, abundant, and nontoxic materials, such as n-type ZnO and p-type SnOx thin films, deposited on borosilicate glass substrate is proposed. A type II heterojunction between SnOx and ZnO films was predicted by density functional theory (DFT) calculations and confirmed experimentally by X-ray photoelectron spectroscopy (XPS). Moreover, scanning transmission electron microscopy (STEM) combined with energy-dispersive X-ray spectroscopy (EDS) show a sharp interface between the SnOx and ZnO layers, confirming the high quality of the p-n junction even after annealing at 523 K. ZnO and SnOx thin films exhibit Seebeck coefficients (alpha) of similar to 121 and similar to 258 mu V/K, respectively, at 298 K, resulting in power factors (PF) of 180 mu W/m K-2 (for ZnO) and 37 mu W/m K-2 (for SnOx). Moreover, the thermal conductivities of ZnO and SnOx films are 8.7 and 1.24 W/m K, respectively, at 298 K, with no significant changes until 575 K. The four pairs all-oxide TEG generated a maximum power output (P-out) of 1.8 nW (approximate to 126 mu W/cm(2)) at a temperature difference of 160 K. The output voltage (V-out) and output current (I-ou(t)) at the maximum power output of the TEG are 124 mV and 0.0146 mu A, respectively. This work paves the way for achieving a high-performance TEG device based on oxide thin films.

In this work, the photodegradation process of atorvastatin calcium (ATC) is reported as depending on: (1) the presence and the absence of excipients in the solid state; (2) the chemical interaction of ATC with phosphate buffer (PB) having pH equal to 7 and 8; and (3) hydrolysis reaction of ATC in the presence of aqueous solution of NaOH. The novelty of this work consists in the monitoring of the ATC photodegradation by photoluminescence (PL). The exposure of ATC in solid state to UV light induces the photo-oxygenation reactions in the presence of water vapors and oxygen from air. According to the X-ray photoelectron spectroscopic studies, we demonstrate that the photo-oxygenation reaction leads to photodegradation compounds having a high share of C=O bonds compared to ATC before exposure to UV light. Both in the presence of PB and NaOH, the photodegradation process of ATC is highlighted by a significant decrease in the intensity of the PL and photoluminescence excitation (PLE) spectra. According to PLE spectra, the exposure of ATC in the presence of NaOH to UV light leads to the appearance of a new band in the spectral range 340-370 nm, this belonging to the photodegradation products. Arguments concerning the chemical compounds, that resulted in this last case, are shown by Raman scattering and FTIR spectroscopy.

Energy harvesting for Internet of Things applications, comprising sensing, life sciences, wearables, and communications, requires efficient thermoelectric (TE) materials, ideally semiconductors compatible with Si technology. In this work, we investigate the potential of GeSn/Ge layers, a group IV material system, as TE material for low-grade heat conversion. We extract the lattice thermal conductivity, by developing an analytical model based on Raman thermometry and heat transport model, and use it to predict thermoelectric performances. The lattice thermal conductivity decreases from 56 W/(m.K) for Ge to 4 W/(m.K) by increasing the Sn atomic composition to 14%. The bulk cubic Ge0.86Sn0.14 alloy features a TE figure of merit of ZT similar to 0.4 at 300 K and an impressive 1.04 at 600 K. These values are extremely promising in view of the use of GeSn/Ge layers operating in the typical on-chip temperature range.

The Laser-induced Thermionic Vacuum Arc method was applied to optimize magnesium-silver (Mg:Ag) alloys, which can be potentially used as stable metallic cathodes for optoelectronic devices. Besides lowering the cathode work function given by the magnesium that improves the electron injection, Mg:Ag alloys induce a higher electrical conductivity, estimated here to be 3.42 x 10(7) S m(-1) for AgMg3, compared with 2.64 x 10(7) S m(-1), estimated here for Mg thin films. Mg:Ag alloys avoid the critical issue of Mg oxidation for better charge injection in optoelectronic active layers. By improving the Thermionic Vacuum Arc technique with the laser beam, this method enables the control of the silver concentration in these alloys due to photonic processes. The uniformity of metallic thin films, compactness, and high purity are the primary advantages of the Laser-induced Thermionic Vacuum Arc method. (C) 2021 Elsevier B.V. All rights reserved.

Metal-organic frameworks (MOFs) are a class of porous coordination networks extraordinarily varied in physicochemical characteristics such as porosity, morphologies, and compositions. These peculiarities make MOFs widely exploited in a large array of applications, such as catalysis, chemicals and gas sensing, drug delivery, energy storage, and energy conversion. MOFs can also serve as nanostructured precursors of metal oxides with peculiar characteristics and controlled shapes. In this work, starting from MIL125-(Ti), a 1,4-benzenedicarboxylate (BDC)-based MOF with Ti as metallic center, mesoporous TiO2 powders containing both anatase and rutile crystalline phases were produced. A challenging utilization of these porous MOF-derived Ti-based oxides is the optically-based quantitative detection of molecular oxygen (O-2) in gaseous and/or aqueous media. In this study, the photoluminescence (PL) intensity changes during O-2 exposure of two MOF-derived mixed-phase TiO2 powders were probed by exploiting the opposite response of rutile and anatase in VIS-PL and NIR-PL wavelength intervals. This result highlights promising future possibilities for the realization of MOF-derived doubly-parametric TiO2-based optical sensors.

Ge2Sb2Te5 (GST-225) is a chalcogenide material with applications in nonvolatile memories. However, chalcogenide material properties are dependent on the deposition technique. GST-225 thin films were prepared using three deposition methods: magnetron sputtering (MS), pulsed laser deposition (PLD) and a deposition technique that combines MS and PLD, namely MSPLD. In the MSPLD technique, the same bulk target is used for sputtering but also for PLD at the same time. The structural and optical properties of the as-deposited and annealed thin films were characterized by Rutherford backscattering spectrometry, X-ray reflectometry, X-ray diffraction, Raman spectroscopy and spectroscopic ellipsometry. MS has the advantage of easily leading to fully amorphous films and to a single crystalline phase after annealing. MS also produces the highest optical contrast between the as-deposited and annealed films. PLD leads to the best stoichiometric transfer, whereas the annealed MSPLD films have the highest mass density. All the as-deposited films obtained with the three methods have a similar optical bandgap of approximately 0.7 eV, which decreases after annealing, mostly in the case of the MS sample. This study reveals that the properties of GST-225 are significantly influenced by the deposition technique, and the proper method should be selected when targeting a specific application. In particular, for electrical and optical phase change memories, MS is the best suited deposition method.

In the present study, we report the synthesis of a dextran coated iron oxide nanoparticles (DIO-NPs) thin layer on glass substrate by an adapted method. The surface morphology of the obtained samples was analyzed by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), optical, and metallographic microscopies. In addition, the distribution of the chemical elements into the DIO-NPs thin layer was analyzed by Glow Discharge Optical Emission Spectrometry (GDOES). Furthermore, the chemical bonds formed between the dextran and iron oxide nanoparticles was investigated by Fourier Transform Infrared Spectroscopy (FTIR). Additionally, the HepG2 viability incubated with the DIO-NPs layers was evaluated at different time intervals using MTT (3-(4, 5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay. The goal of this study was to obtain a DIO-NPs thin layer which could be used as a coating for medical devices such as microfluidic channel, microchips, and catheter. The results of the surface morphology investigations conducted on DIO-NPs thin layer suggests the presence of a continuous and homogeneous layer. In addition, the GDOES results indicate the presence of C, H, Fe, and O signal intensities characteristic to the DIO-NPs layers. The presence in the IR spectra of the Fe-CO metal carbonyl vibration bonds prove that the linkage between iron oxide nanoparticles and dextran take place through carbon-oxygen bonds. The cytotoxicity assays highlighted that HepG2 cells morphology did not show any noticeable modifications after being incubated with DIO-NPs layers. In addition, the MTT assay suggested that the DIO-NPs layers did not present any toxic effects towards HEpG2 cells.