National Institute Of Materials Physics - Romania

Cu2SnSe3 (CTSe) is a polyvalent material that can be used as an absorber layer for thin film solar cells or as a starting layer for the synthesis of CZTSe or CZTSSe compounds. Obtaining CTSe single phase films with opti-mized properties for thin film solar cells is a difficult task. A systematic study using both metallic and binary chalcogenides precursors for the formation of the CTSe phase was not performed. The films consisting of four different stacks (Sn\Cu, SnSe2\Cu, Sn\Cu2Se, and SnSe2\Cu2Se) were prepared by magnetron sputtering on soda lime glass (SLG) and molybdenum (Mo) coated SLG substrates, followed by annealing at 550 degrees C under Sn + Se atmosphere. X-ray diffraction and Raman spectroscopy results indicated the formation of a single CTSe phase in most of the stacks deposited on both substrates. Scanning electron microscopy images showed compact surfaces with large grains in the films deposited on Mo substrate, while the films on SLG have more voids on their sur-faces. The elemental analysis measured by energy dispersive spectroscopy revealed stoichiometric films on Mo, and copper and tin rich compositions on SLG substrates. The band gap values inferred by conventional spec-troscopy are between 0.81 and 1.95 eV. It was found that the SnSe2\Cu and Sn\Cu2Se stacks are preferred for the formation of a single CTSe phase, with dense surface morphology, a stoichiometric composition, and an optimal absorber layer band gap. This study opens the way to comprehend the formation reactions during the seleni-zation of metallic and binary chalcogenides precursors towards the optimization of kesterite absorber for photovoltaic device fabrication.

Photocatalytic conversion of H2O, CO2 and N-2 represents one promising approach to harvest and store solar energy, for which efficient visible light responsive semiconductors are inevitable. Often, the presence of a small amount of an additional component called a "cocatalyst", is required to synergistically enhance the performance of the photocatalyst. Tremendous efforts were made in the past to identify inexpensive materials to be used as cocatalysts, for which metal oxides (MOs) are one of the traditional choices. Among alternative categories of materials investigated, the recently discovered MXenes display enormous potential owing to their unique 2D layered structure, tuneable composition, abundant surface functionalities and superior electronic conductivity. Specifically, MOs and MXenes encompass a variety of distinct as well as analogous characteristics that allows them to be tailored to different extents. Unfortunately, a comprehensive overview covering the synthetic, structural and photocatalytic aspects of MOs and MXenes is not available as of now. Herein, we intend to summarize the progress achieved so far in these two families of materials to be used as cocatalysts for the photoconversion of H2O, CO2 and N-2. Followed by a general introduction, we briefly outline the fundamental principles and the role of cocatalysts in photocatalytic reactions. A discussion regarding the use of MOs and MXenes as cocatalysts for the conversion of H2O, CO2 and N-2 is then provided in separate sections. Critical assessment regarding structure and morphology control, surface properties and stability concerns can not only help to recognize the challenges that limit further advancement, but can also highlight the future research directions of these materials for the effective transformation of H2O, CO2 and N-2.

The paper presents a study concerning the role of ferroelectric filler size and clustering in the dielectric properties of 20%BaTiO3-80%PVDF and of 20% (2%Ag-98%BaTiO3)-PVDF hybrid nanocomposites. By finite element calculations, it was shown that using fillers with epsilon > 103 does not provide a permittivity rise in the composites and the effective dielectric constant tends to saturate to specific values determined by the filler size and agglomeration degree. Irrespective of the ferroelectric filler sizes, the addition of metallic ultrafine nanoparticles (Ag) results in permittivity intensification and the effect is even stronger if the metallic nanoparticles are connected to a higher degree with the ferroelectric particles' surfaces. When using coarse ferroelectric fillers, the probability of clustering is higher, thus favoring the permittivity increase by field concentration in small regions close to the interfaces separating dissimilar materials. The modeling results were validated by an experimental dielectric analysis performed in a series of PVDF-based thick films with the same amount of BaTiO3 fillers or with Ag-BaTiO3 hybrid fillers. Similar trends as predicted by simulations were found experimentally but with slightly higher permittivity values which were assigned to the modifications of the polymer phase composition due to the presence of nanofillers and the local sample inhomogeneity (the presence of clustering, in particular for coarse BaTiO3 grains), which create regions with enhanced local fields.

Photocatalytic conversion of H2O, CO2 and N-2 represents one promising approach to harvest and store solar energy, for which efficient visible light responsive semiconductors are inevitable. Often, the presence of a small amount of an additional component called a "cocatalyst", is required to synergistically enhance the performance of the photocatalyst. Tremendous efforts were made in the past to identify inexpensive materials to be used as cocatalysts, for which metal oxides (MOs) are one of the traditional choices. Among alternative categories of materials investigated, the recently discovered MXenes display enormous potential owing to their unique 2D layered structure, tuneable composition, abundant surface functionalities and superior electronic conductivity. Specifically, MOs and MXenes encompass a variety of distinct as well as analogous characteristics that allows them to be tailored to different extents. Unfortunately, a comprehensive overview covering the synthetic, structural and photocatalytic aspects of MOs and MXenes is not available as of now. Herein, we intend to summarize the progress achieved so far in these two families of materials to be used as cocatalysts for the photoconversion of H2O, CO2 and N-2. Followed by a general introduction, we briefly outline the fundamental principles and the role of cocatalysts in photocatalytic reactions. A discussion regarding the use of MOs and MXenes as cocatalysts for the conversion of H2O, CO2 and N-2 is then provided in separate sections. Critical assessment regarding structure and morphology control, surface properties and stability concerns can not only help to recognize the challenges that limit further advancement, but can also highlight the future research directions of these materials for the effective transformation of H2O, CO2 and N-2.

The purpose of the work is the synthesis and characterization of TiO2 nanoparticles. These were obtained by two different methods, precipitation and sol-gel, starting from titanium(IV) isopropoxide and calcining at 500 degrees C for 2 h. The compositional, structural, morphological and optical properties of the resulting powders were investigated by energy dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy, X-ray diffraction, Raman spectroscopy, scanning electron microscopy, reflectance spectroscopy and photoluminescence spectroscopy. The thermally treated samples contain TiO2 as single phase with tetragonal structure, known as anatase. SEM analysis showed quasi-spherical particles with a diameter of few nanometres for the calcined samples, while the optical studies revealed band gap values of 3.04 and 3.17 eV, as a function of the preparation route.

In the present work, stannite Cu2CoSnS4 (CCTS) films were elaborated using spray pyrolysis method on soda-lime glass, at different deposition temperatures (T-d = 250, 300, and 350 degrees C), followed by different chosen sulfurization temperatures (T-s = 450, 500, and 550 degrees C). X-ray diffraction (XRD) revealed the nearly single-phase formation of CCTS films at 300 degrees C deposition temperature. After sulfurization in argon flow, the XRD lines become narrower, the average crystallite size expanding above 70 nm. The Raman spectroscopy analysis confirmed the stannite structure formation, as well as the presence CoS2 secondary phases, which reduces at higher sulfurization temperature (550 degrees C). The energy dispersive spectroscopy results indicated atomic ratios of Cu/Co/Sn/S close to the ideal stoichiometric ratio 2:1:1:4. The room temperature photoluminescence emission is recorded with maximum in the 1.35-1.40 eV range. Thermoelectric properties are measured up to 130 degrees C, the films show poor power factor as a result of small positive Seebeck coefficients 10-45 Of K -1 and low electrical conductivity despite of having relatively high carrier concentration (similar to 10(20) cm(-3)).

In this work, new information concerning the optical properties of black phosphorus (BP) sheets chemically/electrochemically functionalized with diphenyl amine (DPA) and its macromolecular compound (poly(diphenylamine) (PDPA)) in the absence/presence of phosphotungstic acid (PTA) is reported. Raman scattering and FTIR spectroscopy studies indicate that the interaction of BP with PTA leads to the elimination of the PxOy layer onto the surface of the BP sheets. In the case of the chemical interaction of BP with DPA, the reaction product corresponds to DPA chemically functionalized BP sheets having an imino-phosphorane (IP) structure. The electrochemical oxidation of BP sheets chemically functionalized with DPA in the presence of PTA leads to an increase in the weight of P-N bonds as a consequence of the generation of PDPA doped with the PTA heteropolyanions, as shown by FTIR spectroscopy and Raman scattering. This process is evidenced by a shift of the Raman line from 362 cm(-1) to 378 cm(-1), assigned to the A(1g) mode. This change was explained by taking into account the compression of the layers containing P atoms, which is induced by PDPA macromolecular chains. The decrease in the intensity of the PL spectra of DPA as well as PDPA, in the presence of BP, indicates that BP acts as a PL quenching agent for these compounds. A preferential orientation of the PDPA doped with the PTA heteropolyanions on the surface of BP sheets is highlighted by the variation of the binding angle of the PDPA on the surface of BP sheets from 44.7 degrees to 39.9 degrees.

In this paper, new results on the degradation of losartan potassium (LP, (1)), in the absence and presence of excipients, which was induced by UV light, the acid character of phosphate buffer solution (PBS) and alkaline medium, respectively, are reported through correlated studies of FTIR spectroscopy, photoluminescence and dielectric spectroscopy. The photoluminescence (PL) spectra of LP and the drug marked under the name Lorista (LO) are characterized by intense emission bands, peaking at 378 nm and 380 nm, respectively, accompanied by low intensity bands with a maximum at similar to 450-460 nm. Photodegradation of LO in a solid state is evidenced by a decrease in the intensity of the PL band at 380 nm, a variation that originates both in the adsorption of water vapors from the air and in the interaction of LP with excipients such as cornstarch, silicon dioxide and cellulose. The LP-water interaction is described, taking into account the main electrical parameters, i.e., complex dielectric permittivity and electrical conductivity. Photodegradation of LP and LO also induces an increase in the intensity of the emission band, at similar to 450-460 nm. The influence of acid and alkaline medium on the LO degradation is analyzed using phosphate buffer (PBS) and NaOH solutions, respectively. In both cases, a decrease in the intensity of the PL band, at 380 nm, is reported. The intensity diminution of the PL spectra of NaOH-reacted LP and LO is the result of the formation of the photodegradation product N-methanolamide-{[2\'-(1H-tetrazol-5-yl)(1,1\'-biphenyl)-4-yl]methyl} (2). This compound was proven by the studies of FTIR spectroscopy achieved on LP and NaOH-reacted LP. The appearance of the IR band at 1740 cm(-1) and the increase in the absorbance in the IR band at 1423 cm(-1) indicate that the photodegradation product (2) contains the C=O and C-OH functional groups.

Understanding the phonon anharmonicity and temperature-dependent behavior of phonons that affect the thermal transport properties in 2D materials is crucial for developing efficient thermoelectric and memristor devices. SnSe has attracted significant interest because of its potential applications for developing such novel devices. Here, orthorhombic SnSe nanoflakes with a thickness of less than 100 nm and oriented along the [100] crystal axis were obtained using physical vapor transport at atmospheric pressure. Polarization-resolved Raman spectroscopy of SnSe nanoflakes was performed at a temperature of 5 K. Temperature-dependent frequencies and linewidths of Raman modes in tin selenide were fitted according to the anharmonic phonon coupling theory. The results indicate that both two and three order processes are responsible for the phonon decay in tin selenide. The memristive property was confirmed by electrical measurements of SnSe devices. SnSe memristors have an operating current of 10-4 A, similar to other transition-metal dichalcogenide memristors, but are more energy efficient than memristors based on defect migration, with a threshold voltage of 3 V.

A CuCrFeTiV high entropy alloy was prepared and irradiated with swift heavy ions in order to check its adequacy for use as a thermal barrier in future nuclear fusion reactors. The alloy was prepared from the elemental powders by ball milling, followed by consolidation by spark plasma sintering at 1178 K and 65 MPa. The samples were then irradiated at room temperature with 300 keV Ar+ ions with fluences in the 3 x 1015 to 3 x 1018 Ar+/cm2 range to mimic neutron-induced damage accumulation during a duty cycle of a fusion reactor. Structural changes were investigated by X-ray diffraction, and scanning electron microscopy and scanning transmission electron microscopy, both coupled with X-ray energy dispersive spectroscopy. Surface irradiation damage was detected for high fluences (3 x 1018 Ar+/cm2) with formation of blisters of up to 1 mu m in diameter. Cross-sectional scanning transmission electron microscopy showed the presence of intergranular cavities only in the sample irradiated with 3 x 1018 Ar+/cm2, while all irradiation experiments produced intragranular nanometric-sized bubbles with increased density for higher Ar+ fluence. The Williamson-Hall method revealed a decrease in the average crystallite size and an increase in residual strain with increasing fluence, consistent with the formation of Ar+ bubbles at the irradiated surface.