Publications

xHfO(2)-(1-x)alpha-Fe2O3 (x = 0.1, 0.3, 0.5 and 0.7) nanoparticles system was obtained using mechanochemical activation by high energy ball milling for time periods ranging from 0 to 12 h. X-ray diffraction patterns revealed the presence of two phases, a hafnium-doped hematite and an iron-doped hafnia, which competed with each other to form a solid solution. The trend observed in the lattice parameters using Rietveld refinement was consistent with differences in ionic radii between Hf and Fe. Crystallite sizes for both hematite and hafnia were analyzed as function of milling time using the Scherrer method and found to decrease down to similar to 15 nm for all molar concentrations used. Mossbauer spectroscopy revealed the presence of 1-5 sextets corresponding to different numbers of Hf nearest neighbors of Fe in the hematite structure. The different hyperfine magnetic fields could be resolved in the model of local atomic environment. Substitutions of Fe in hafnia gave rise to a nonmagnetic phase represented by a quadrupole split doublet, whose abundance was found to increase with ball milling time. Hysteresis loops recorded at 5 K showed that the Hf-doped system does not saturate in an applied magnetic field of 5 T. The Morin transition was observed during zero-field-cooling-field cooling (ZFC-FC) in an external magnetic field of 200 Oe. Differential scanning calorimetry with thermal gravimetric analysis (DSC-TGA) evidenced an exothermic peak for the starting oxides and an endothermic peak for the solid solution.

In this work, the ferroelectric and fatigue characteristics of Au/0.5Ba(Zr0.2Ti0.8)O-3-0.5(Ba0.7Ca0.3)TiO3(BCZT)/Si metal-ferroelectric-semiconductor (MFS) structures are investigated. Moreover, the effect of introducing a thin dielectric HfO2-Al2O3 (HAO) layer with different thicknesses between the BCZT layer and the Si substrate on the ferroelectric characteristics in the metal-ferroelectric-insulator-semiconductor (MFIS) configuration is evaluated. It is evidenced that the insertion of the HAO layer with a thickness of 8 nm improves the memory window of the capacitance-voltage (C-V) curves by 106% compared to the value obtained in the MFS structure and reduces the leakage currents. Furthermore, the Au/BCZT/HAO (8 nm)/Si structure shows a remarkable remnant polarization (P-r) of 7.8 mu C/cm(2), with a coercive voltage of 1.9 V. The obtained value for P-r corresponds to a six times enhancement when compared to the value obtained in the Au/BCZT/Si structure. In addition, the fatigue studies reveal that the P-r obtained in the Au/BCZT/HAO/Si structure slightly decreases (3%) with continuous cycling, up to 10(9) cycles. The present work evidences that Au/BCZT/HAO/Si structures are promising for nonvolatile memory applications.

The development of robust, safe, cost-effective and efficient photocatalytic systems for water splitting should take into account the presence of a proper and powerful photon absorber and an efficient, low-cost and earth-abundant electrocatalyst to perform the reaction at high conversions. In this study, Ni-Zn/TiO(2)ternary composites with high photocatalytic activity for water splitting under UV irradiation were successfully prepared via a simple and low-cost deposition-precipitation route. Thus, different Ni : Zn molar ratios (1 : 0, 1 : 1, 3 : 1, 6 : 1, 9 : 1, and 0 : 1) were deposited on TiO(2)in order to reach a total metal loading of 50 wt. %. The obtained composites were characterized using several techniques, such as: X-ray diffraction, UV-Vis spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The most active synthesized composite, namely Ni-Zn/TiO2(9 : 1), exhibits H(2)generation rate above 17 mmols g(-1) h(-1), which is nearly one thousand times higher than that obtained with TiO(2)Evonik P25. Our study demonstrates that TiO(2)becomes a degenerated semiconductor in the presence of Ni and ZnO, with remarkable photocatalytic properties. Thus, the obtained results can open new opportunities in the preparation of very active materials for hydrogen production based on the optimization of three-component structures.

Y-modified LDHs with atomic Mg2+/(Al3+ + Y3+) of 3 and Al3+/Y3+ ratios of 0.5, 1 and 1.5 were prepared following two preparation methods, i.e. the co-precipitation and mechano-chemical one. The substitution of Al by Y in the brucite-type layer was less effective for the samples prepared by co-precipitation compared to those prepared via mechano-chemical route. In spite the fact yttrium has a larger ionic radius (0.9 angstrom) the structural characterizations of these solids confirmed that the layered structure incorporates part of it in the octahedral positions. Further, the reconstruction of the layered structure after an exposure to water for 1 h was more effective for the solid prepared by co-precipitation. The yttrium modified LDHs showed better catalytic activities for cyclohexene oxidation to the corresponding epoxide than the un-modified LDH sample. Then, mixed oxides derived from yttrium-LDH showed very high conversions and selectivities for the synthesis of chalcone.

Hydroxyapatite (HAp) and samarium doped hydroxyapatite, Ca10-xSmx(PO4)(6)(OH)(2),x(Sm)= 0.05, (5SmHAp), coatings were prepared by sol-gel process using the dip coating method. The stability of 5SmHAp suspension was evaluated by ultrasound measurements. Fourier transform infrared spectroscopy (FTIR) was used to examine the optical characteristics of HAp and 5SmHAp nanoparticles in suspension and coatings. The FTIR analysis revealed the presence of the functional groups specific to the structure of hydroxyapatite in the 5SmHAp suspensions and coatings. The morphology of 5SmHAp nanoparticles in suspension was evaluated by transmission electron microscopy (TEM). Moreover, scanning electron microscope (SEM) was used to evaluate the morphology of nanoparticle in suspension and the morphology of the surface on the coating. The SEM and TEM studies on 5SmHAp nanoparticles in suspension showed that our samples consist of nanometric particles with elongated morphology. The SEM micrographs of HAp and 5SmHAp coatings pointed out that the coatings are continuous and homogeneous. The surface morphology of the 5SmHAp coatings was also assessed by Atomic Force Microscopy (AFM) studies. The AFM results emphasized that the coatings presented the morphology of a uniformly deposited layer with no cracks and fissures. The crystal structure of 5SmHAp coating was characterized by X-ray diffraction (XRD). The surface composition of 5SmHAp coating was analyzed by X-ray photoelectron spectroscopy (XPS). The XRD and XPS analysis shown that the Sm(3+)ions have been incorporated into the 5SmHAp synthesized material. The antifungal properties of the 5SmHAp suspensions and coatings were studied usingCandida albicansATCC 10231 (C. albicans) fungal strains. The quantitative results of the antifungal assay showed that colony forming unity development was inhibited from the early phase of adherence in the case of both suspensions and coatings. Furthermore, the adhesion, cell proliferation and biofilm formation of theC. albicanswere also investigated by AFM, SEM and Confocal Laser Scanning Microscopy (CLSM) techniques. The results highlighted that theC. albicansadhesion and cell development was inhibited by the 5SmHAp coatings. Moreover, the data also revealed that the 5SmHAp coatings were effective in stopping the biofilm formation on their surface. The toxicity of the 5SmHap was also investigated in vitro using HeLa cell line.

This study develops, for the first time, composite coatings based on silver and zinc doped hydroxyapatite in chitosan matrix (AgZnHApCs). The AgZnHApCs composite coatings were prepared by dip coating method. The hydroxyapatite (HAp), biocompatible material for regenerating and strengthening damaged bones were doped with silver and zinc ions and coated with chitosan in order to produce a uniform and homogenous coating with biocompatibility and antimicrobial properties. The stability of AgZnHApCs suspensions was evaluated by ultrasound measurements. The value of stability parameters of AgZnHApCs suspension is in good agreement with the value of bidistilled water used as reference fluid. Homogeneously dispersed solutions of AgZnHApCs were synthesized to endeavor to optimize the physico-chemical and biological characteristics of the coatings obtained at room temperature. The AgZnHApCs composite suspension and coatings were analyzed using various investigation techniques, such as X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR), MTT (3-[4,5-dimethylthiazol-2-yl]-2,5-diphenylte-2H-tetrazolium bromide) assay and antimicrobial studies. The optical spectroscopy, atomic force microscopy (AFM), metallographic examination and X-ray photoelectron spectroscopy (XPS) on AgZnHApCs composite coatings were also conducted. Cell culture and MTT assays demonstrate that AgZnHApCs composite suspension and coatings have no negative effect on the cell viability and proliferation. The cell morphology was not affected in presence of AgZnHApCs composite suspension and coatings. The antimicrobial assays conducted againstStaphylococcus aureusATCC 25923,Escherichia coliATCC 25922, andCandida albicansATCC 90029 microbial strains revealed that both the AgZnHApCs composite suspension and coatings exhibited great antimicrobial properties.

In this work, a complementary ultraviolet-visible (UV-VIS) spectroscopy and photoluminescence (PL) study on melatonin (MEL) hydrolysis in the presence of alkaline aqueous solutions and the photodegradation of MEL is reported. The UV-VIS spectrum of MEL is characterized by an absorption band with a peak at 278 nm. This peak shifts to 272 nm simultaneously with an increase in the band absorbance at 329 nm in the presence of an NaOH solution. The isosbestic point localized at 308 nm indicates the generation of some chemical compounds in addition to MEL and NaOH. The MEL PL spectrum is characterized by a band at 365 nm. There is a gradual decrease in the MEL PL intensity as the alkaline solution concentration added at the drug solution is increased. In the case of the MEL samples interacting with an alkaline solution, a new photoluminescence excitation (PLE) band at 335 nm appears when the exposure time to UV light reaches 310 min. A down-shift in the MEL PLE band, from 321 to 311 nm, as a consequence of the presence of excipients, is also shown. These changes are explained in reference to the MEL hydrolytic products.

This work investigates the structural, magnetic and magneto-optical properties of a new zinc phosphate-tellurite glass belonging to the 45ZnO-10Al(2)O(3)-40P(2)O(5)-5TeO(2)system. The glass was prepared by a wet method of processing the starting reagents followed by suitable melting-stirring-quenching-annealing steps. Specific parameters such as density, average molecular mass, molar volume, oxygen packaging density, refractive index, molar refractivity, electronic polarizability, reflection loss, optical transmission, band gap and optical basicity have been reported together with thermal, magnetic and magneto-optical characteristics. Absorption bands appear in the blue and red visible region, while over 600 nm the glass becomes more transparent. FTIR and Raman spectra evidenced phosphate-tellurite vibration modes proving the P(2)O(5)and TeO(2)network forming role. Magnetic measurements reveal the diamagnetic character of the Te-doped glass with an additional weak ferromagnetic signal, specific to diluted ferromagnetic oxides. Positive Faraday rotation angle with monotonous decreasing value at increasing wavelength was evidenced from magneto-optical measurements. The final product is a composite material comprising of a non-crystalline vitreous phase and Te-based nanoclusters accompanied by oxygen vacancies. The metallic-like Te colloids are responsible for the dark reddish color of the glass whereas the accompanying oxygen vacancies might be responsible for the weak ferromagnetic signal persisting up to room temperature.

In this paper, we investigate the origin of point defects revealed by electron spin resonance (ESR) and photoluminescence (PL) emission in correlation with the photocatalytic activity of ZnO nanocrystals subjected to thermal annealing at various temperatures. Two ESR signals at g similar to 1.96 and similar to 2.003 were consistently observed in all annealed ZnO samples. However, their relative intensities have changed, indicating that the point defect densities were influenced by the annealing temperature. Interestingly, when doping nanoZnO with Cr3+, the Q-band ESR measurements at T = 100 K did show that the g similar to 1.96 signal was completely passivated, suggesting that the origin of the signal lies in the electrons located near the conduction band, i.e. at a shallow-donor level. The intensity of the g similar to 2.003 signal decreased by rising the annealing temperature, and this is attributed to the depopulation of zinc interstitials through the thermally induced migration process and/or recombination with the zinc vacancies. The green PL emission line at similar to 520 nm, which is dominant in the 700 degrees C annealed ZnO sample, shows a correlation with the ESR signal at g similar to 1.96, whose origin is attributed to the radiative transition of the electron from the shallow donor level to the singly ionized zinc vacancy. Furthermore, the high density of the shallow donor electron states was found to be primarily responsible for the high photocatalytic activity in the degradation of methylene blue.